Advertising cloth with photocorrosion resistance, and processing method thereof

A technology of anti-light corrosion and processing method, which is applied in the direction of coating, artificial filament of inorganic raw materials, textiles and papermaking, etc. It can solve the problems of fading advertisement content, difficulty in replacing advertisement cloth, and damage to advertisement cloth, etc., and achieves a simple production method Fast, good anti-corrosion performance, less difficult industrial transformation effect

Active Publication Date: 2016-12-21
ZHEJIANG HUIFENG NEW MATERIALS
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the large billboards made of advertising cloth are located in the open outdoors, such as around the highway. Due to the long-term exposure to wind and sun, especially in summer, the large outdoor billboards are easily damaged, especially The advertising cloth on the billboard is easy to be corroded under the sunlight, especially the ultraviolet radiation, which may cause the advertisement content to fade, or cause damage to the advertising cloth. Since the large billboard is located in the suburbs and has a large It is very difficult and costly to replace, so there is a huge market demand for advertising cloth that is more resistant to sunlight, especially ultraviolet rays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An advertising cloth with anti-light corrosion performance, which is composed of mesh cloth, PVC bonding layer and anti-light corrosion layer;

[0031] Among them, the PVC bonding layer is made of the following raw materials in parts by weight: 100 parts of PVC paste resin, 50 parts of epoxy butyl stearate, 2 parts of calcium stearate; ZnO fiber composition of μm;

[0032] Zinc oxide fibers are prepared by the following steps: uniformly mix zinc acetate and molten salt, then heat up to 500°C for 0.5 hours, then heat up to 800°C for 4 hours, cool to room temperature, wash with water and dry; The mass ratio of the salt is 1:7, the molten salt is a mixed inorganic salt of potassium carbonate and lithium carbonate, and the molar percentage of lithium carbonate is 35%.

[0033] A method for processing advertising cloth with anti-light corrosion performance, comprising the following steps:

[0034] a) Mix the raw materials for making the PVC bonding layer and stir at 50°C f...

Embodiment 2

[0038] An advertising cloth with anti-light corrosion performance, which is composed of mesh cloth, PVC bonding layer and anti-light corrosion layer;

[0039] Among them, the PVC bonding layer is made of the following raw materials in parts by weight: 100 parts of PVC paste resin, 65 parts of epoxy octyl stearate, 4 parts of zinc stearate, 30 parts of filler, 10 parts of flame retardant, pentachlorophenol 3 parts, 2 parts of dibutyl hydroxytoluene, 5 parts of adhesive; the anti-corrosion layer is composed of zinc oxide fibers with a length of 0.5 mm and a diameter of 0.5 μm;

[0040] Zinc oxide fibers are prepared by the following steps: uniformly mix zinc citrate and molten salt, then heat up to 550°C for 0.7 hours, then heat up to 825°C for 7 hours, cool to room temperature, wash with water and dry; Zinc citrate The mass ratio to the molten salt is 1:8. The molten salt is a mixed inorganic salt of potassium carbonate and lithium carbonate, and the molar percentage of lithium...

Embodiment 3

[0046] An advertising cloth with anti-light corrosion performance, which is composed of mesh cloth, PVC bonding layer and anti-light corrosion layer;

[0047] Among them, the PVC bonding layer is made from the following raw materials in parts by weight: 100 parts of PVC paste resin, 80 parts of epoxy dioctyl tetrahydrophthalate, 5 parts of zinc ricinoleate, 60 parts of filler, 20 parts of flame retardant 5 parts, 5 parts of tributyltin, 5 parts of propyl gallate, 10 parts of adhesive; the anti-corrosion layer is composed of zinc oxide fibers with a length of 1 mm and a diameter of 1 μm;

[0048] Zinc oxide fibers are prepared by the following steps: uniformly mix zinc oxide and molten salt, then heat up to 600°C for 1 hour, then heat up to 850°C for 10 hours, cool to room temperature, wash with water and dry; The mass ratio of the salt is 1:9, the molten salt is a mixed inorganic salt of potassium carbonate and lithium carbonate, and the molar percentage of lithium carbonate i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an advertising cloth with photocorrosion resistance. The advertising cloth is composed of a grid cloth, a PVC laminating layer and a photocorrosion resisting layer, wherein the PVC laminating layer is produced from PVC paste resin, an environmentally-friendly plasticizer, a stabilizer, a filler, a flame retardant, a mildew inhibitor, an antioxidant and an adhesive; and the photocorrosion resisting layer is composed of micro-nano zinc oxide fibers. The invention also discloses a processing method of the advertising cloth with photocorrosion resistance. The advertising cloth has good photocorrosion resistance, can reflect a large amount of visible lights, and also can shield ultraviolet rays; and the above production method of the advertising cloth has the advantages of simplicity, fastness, good effect, realization of production by using present devices, and small difficulty in industry reconstruction.

Description

technical field [0001] The invention relates to the technical field of light box advertising cloth, in particular to an advertising cloth with anti-light corrosion performance and a processing method thereof. Background technique [0002] With the continuous development of the commodity economy, the advertising decoration industry is also booming, and the use of advertising cloth is also increasing. The traditional advertising department is mainly made of two layers of polyethylene and one layer of high-strength grid cloth and three layers of thermal lamination. Most of the large billboards made of advertising cloth are located in open outdoor places, such as around the expressway. Due to long-term exposure to wind and sun, especially in summer, the large outdoor billboards are easily damaged, especially The advertising cloth on the billboard is easy to be corroded under the sunlight, especially the ultraviolet radiation, which may cause the advertisement content to fade,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N7/00D06N3/06D06N3/00D01F9/08
CPCD01F9/08D06N3/0059D06N3/06D06N7/0097D06N2201/08
Inventor 苏跃锋张伟忠沈金凌建丰陆慧斌
Owner ZHEJIANG HUIFENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com