Water permeable brick prepared from alkali residues and construction waste and preparation method thereof
A technology of construction waste and permeable bricks, which is applied in cement production, ceramic products, and other household appliances, etc., can solve the problems of high production cost of ecological ceramic permeable bricks, consumption of construction waste, and intensified greenhouse effect, etc., to achieve low production costs and low The effect of heat of hydration and simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0020] Example 1
[0021] A permeable brick with alkali slag construction waste is composed of the following parts by weight: 100 parts of alkali slag, 500 parts of construction waste, 5 parts of silica fume, 10 parts of cement, 5 parts of alkaline activator, and 25 parts of water. The specific surface area of the alkali slag≥350cm 2 / g. The alkaline activator is made by mixing lime, sodium water glass and sodium sulfate in a mass ratio of 1:1:1. The construction waste is made by mixing waste concrete, waste bricks, waste marble and waste mortar according to a mass ratio of 1:1:1:1. The construction waste includes the following components by weight percentage: 0.15mm-0.60mm construction waste 15%, 0.60mm-4.75mm construction waste 30%, and 4.75mm-8mm construction waste 55%.
[0022] The preparation method of the above-mentioned alkali slag construction waste permeable bricks is carried out according to the following steps:
[0023] (1) The construction waste is crushed to a parti...
Example Embodiment
[0028] Example 2
[0029] A permeable brick with alkali slag construction waste is composed of the following parts by weight: 100 parts of alkali slag, 200 parts of construction waste, 2 parts of silica fume, 5 parts of cement, 2 parts of alkaline activator, and 18 parts of water. The specific surface area of the alkali slag≥350cm 2 / g. The alkaline activator is made by mixing lime, sodium water glass, and sodium sulfate in a mass ratio of 1:1:1. The construction waste is made by mixing waste concrete, waste bricks, waste marble and waste mortar according to a mass ratio of 1:1:1:1. The construction waste includes the following components by weight percentage: 0.15mm-0.60mm construction waste 25%, 0.60mm-4.75mm construction waste 15%, and 4.75mm-8mm construction waste 60%.
[0030] The preparation method of the above-mentioned alkali slag construction waste permeable bricks is carried out according to the following steps:
[0031] (1) The construction waste is crushed to a parti...
Example Embodiment
[0036] Example 3
[0037] A permeable brick for alkali slag construction waste is composed of the following parts by weight: 100 parts of alkali slag, 800 parts of construction waste, 8 parts of silica fume, 15 parts of cement, 7.5 parts of alkaline activator, and 40 parts of water. The specific surface area of the alkali slag≥350cm 2 / g. The alkaline activator is made by mixing lime, sodium water glass and sodium sulfate in a mass ratio of 1:1:1. The construction waste is made by mixing waste concrete, waste bricks, waste marble and waste mortar in a mass ratio of 1:1:1:1. The construction waste includes the following components by weight percentage: 0.15mm-0.60mm construction waste 10%, 0.60mm-4.75mm construction waste 20%, and 4.75mm-8mm construction waste 70%.
[0038] The preparation method of the above-mentioned alkali slag construction waste permeable bricks is carried out according to the following steps:
[0039] (1) Crush the construction waste through a large hammer o...
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap