High-glowing filament scratch-resistant PC material suitable for tablet computer shell and preparation method thereof

A high glow wire, tablet computer technology, applied in the field of polymer functional composite materials, can solve the problems of scratch resistance and glow wire performance of non-PC composite materials, and meet the requirements of ensuring electrical safety and long-term use, excellent flame retardant performance and weather resistance, and the effect of large specific surface area

Active Publication Date: 2017-02-01
GUANGZHOU SUPER DRAGON ENG PLASTICS
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent does not conduct research on the scratch resistance and glow wire performance of PC composite materials, but th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-glowing filament scratch-resistant PC material suitable for tablet computer shell and preparation method thereof
  • High-glowing filament scratch-resistant PC material suitable for tablet computer shell and preparation method thereof
  • High-glowing filament scratch-resistant PC material suitable for tablet computer shell and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Weigh the raw materials according to the weight ratio in Table 1 and put them into a high-speed mixer, and mix at high and low speeds for 4 minutes at room temperature. The mixed material is put into the hopper of a twin-screw extruder, melted and blended, extruded and granulated to obtain a composite material. The processing technology is as follows: twin-screw extruder, the temperature of the first zone is 210°C, the temperature of the second zone is 245°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 240°C, the temperature of the sixth zone is 240°C, and the temperature of the seventh zone is 230°C , the eight-zone temperature is 230°C, and the head temperature is 250°C. Screw speed: 400r / min, vacuum: 600mmHg, cooling water temperature: 50°C, drying time: 2h, drying temperature: 100°C.

Embodiment 2

[0045] Weigh the raw materials according to the weight ratio in Table 1 and put them into a high-speed mixer, and mix at high and low speeds for 4 minutes at room temperature. The mixed material is put into the hopper of a twin-screw extruder, melted and blended, extruded and granulated to obtain a composite material. The processing technology is as follows: twin-screw extruder, the temperature of the first zone is 210°C, the temperature of the second zone is 245°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 240°C, the temperature of the sixth zone is 240°C, and the temperature of the seventh zone is 230°C , the eight-zone temperature is 230°C, and the head temperature is 250°C. Screw speed: 400r / min, vacuum: 600mmHg, cooling water temperature: 50°C, drying time: 2h, drying temperature: 100°C.

Embodiment 3

[0047] Weigh the raw materials according to the weight ratio in Table 1 and put them into a high-speed mixer, and mix at high and low speeds for 4 minutes at room temperature. The mixed material is put into the hopper of a twin-screw extruder, melted and blended, extruded and granulated to obtain a composite material. The processing technology is as follows: twin-screw extruder, the temperature of the first zone is 210°C, the temperature of the second zone is 245°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 250°C, the temperature of the fifth zone is 240°C, the temperature of the sixth zone is 240°C, and the temperature of the seventh zone is 230°C , the eight-zone temperature is 230°C, and the head temperature is 250°C. Screw speed: 400r / min, vacuum: 600mmHg, cooling water temperature: 50°C, drying time: 2h, drying temperature: 100°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-glowing filament scratch-resistant PC material suitable for a tablet computer shell and a preparation method thereof. The material is prepared from, by weight, 65-70% of PC, 10-14% of flame retardant, 10-18% of scratch-resistant agent, 4-6% of toughening agent, 0.4-0.6% of anti-dripping agent, 0.1-0.2% of primary antioxidant, 0.3-0.4% of auxiliary antioxidant, 0.5-0.6% of lubricating agent and 0.3-0.5% of weather-proof agent. Engineering plastic PC is used as a main material, the halogen-free flame retardant, the toughening agent, the scratch-resistant agent, anti-dripping agent, the antioxidants, the weather-proof agent and the lubricating agent are added, all the materials are subjected to melt blending through a double-screw extruder, and the high-glowing filament scratch-resistant PC material suitable for the tablet computer shell is prepared. The material has the advantages of low price, low weight, scratch resistance, good weather fastness, halogen-free flame retardation, high-glowing filaments, excellent mechanical properties, high practicability and the like. Meanwhile, the preparation method of the material is simple and easy to implement and can be widely applied to industrial production.

Description

technical field [0001] The invention belongs to the field of polymer functional composite materials, and in particular relates to a high glow wire scratch-resistant PC material suitable for a tablet computer casing and a preparation method thereof. Background technique [0002] With the rapid development of network information technology, the use of tablet computers as smart terminals has increased year by year, and at the same time, higher requirements have been put forward for their performance and appearance. The lightness, thinness, miniaturization, low cost, and high security of tablet computers are the future development trends, and this is closely related to the shell materials used. [0003] Because PC / ABS has the characteristics of good processing performance and low cost, PC / ABS alloys are mostly used in the existing commercial tablet computer shells, but from the patent literature checked, the research on scratch resistance and glow wire performance is less Less ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L51/06C08L27/18C08L85/02C08K13/04C08K7/00C08K3/34C08K5/523
CPCC08K2201/003C08K2201/014C08L69/00C08L2201/02C08L2201/08C08L2201/22C08L2203/20C08L2205/035C08L51/06C08L27/18C08L85/02C08K13/04C08K7/00C08K3/34C08K5/523
Inventor 郝源增曾德明黄泽彬郝建鑫谯盛元袁海兵任萍陈维维
Owner GUANGZHOU SUPER DRAGON ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap