Polarizing plate, composite polarizing plate and liquid crystal display device
一种偏振板、偏振膜的技术,应用在复合偏振板,液晶显示装置领域,能够解决不能满足液晶显示装置薄型轻量化等问题,达到优异防眩功能、减小厚度的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
manufacture example 1
[0278] (Manufacturing example 1: Production of polarizing film)
[0279] After immersing a polyvinyl alcohol film with a thickness of 75 μm having an average degree of polymerization of about 2400 and a degree of saponification of 99.9 mol% or more in pure water at 30°C, it is immersed in pure water at 30°C with a weight ratio of iodine / potassium iodide / water of 0.02 / 2 / 100 in aqueous solution for iodine staining. Then, it immersed in the aqueous solution whose weight ratio of potassium iodide / boric acid / water was 12 / 5 / 100 at 56.5 degreeC, and performed boric-acid treatment (crosslinking treatment). Next, after washing|cleaning with the pure water of 8 degreeC, it dried at 65 degreeC, and the polarizing film which adsorb|sucked iodine to polyvinyl alcohol and it was oriented was obtained. Stretching is mainly carried out in the process of iodine dyeing and boric acid treatment, and the total stretching ratio is 5.3 times.
manufacture example 2
[0280] (Manufacturing example 2: Preparation of active energy ray-curable resin composition A)
[0281] The active energy ray-curable resin composition A was prepared by mixing the following components.
[0282] 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate (CELLOXIDE 2021P, manufactured by Daicel Chemical Co.): 35 parts
[0283] Bis[(3-ethyl-3-oxetanyl)methyl]ether (ARON OXETANE OXT-221, manufactured by Toagosei Co., Ltd.): 15 parts
[0284] - Diacrylate (A-DOG, manufactured by Shin-Nakamura Chemical Co., Ltd.) of an acetal compound of hydroxytrimethylacetaldehyde and trimethylolpropane: 50 parts
[0285] 2-Hydroxy-2-methyl-1-phenylpropan-1-one (DAROCUR 1173, manufactured by Ciba, photoradical polymerization initiator): 2.5 parts
[0286] 4. 4'-bis(diphenylsulfonium)diphenylthiobishexafluorophosphate-based photocationic polymerization initiator (SP-150, manufactured by ADEKA Corporation): 2.5 parts.
[0287] In addition, the above-mentioned A-DOG (diacrylate es...
manufacture example 3
[0289] (Manufacturing example 3: Preparation of active energy ray-curable resin composition B)
[0290] The active energy ray-curable resin composition B was prepared by mixing the following components.
[0291] 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate (CELLOXIDE 2021P, manufactured by Daicel Chemical Co.): 35 parts
[0292] Bis[(3-ethyl-3-oxetanyl)methyl]ether (ARON OXETANE OXT-221, manufactured by Toagosei Co., Ltd.): 15 parts
[0293] ・1,3,5-tris(2-hydroxyethyl)isocyanurate triacrylate (A-9300, manufactured by Shin-Nakamura Chemical Industry Co., Ltd.): 50 parts
[0294] 2-Hydroxy-2-methyl-1-phenylpropan-1-one (DAROCUR 1173, manufactured by Ciba, photoradical polymerization initiator): 2.5 parts
[0295] 4. 4'-bis(diphenylsulfonium)diphenylthiobishexafluorophosphate-based photocationic polymerization initiator (SP-150, manufactured by ADEKA Corporation): 2.5 parts.
PUM
Property | Measurement | Unit |
---|---|---|
visible light transmittance | aaaaa | aaaaa |
saponification | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction