Continuous fiber reinforced PVC pre-dip material and preparation method thereof

A continuous fiber and prepreg technology, which is applied in the field of continuous fiber reinforced PVC prepreg and its preparation, can solve the problems of increased resin viscosity, prepreg dry yarn, and reduced fluidity, achieving simple equipment, low energy consumption, The effect of equal mechanical properties

Inactive Publication Date: 2017-03-01
红石极威实业集团有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since thermoplastic composite materials are mostly used outdoors, certain flame retardant requirements are required. Therefore, flame retardants, anti-ultraviolet agents, antioxidants, etc. will be added when processing the above resins, which will increase the viscosity of the resin and reduce its flow. Sex, affecting its wettability, resulting in dry yarn of prepreg, affecting its performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous fiber reinforced PVC pre-dip material and preparation method thereof
  • Continuous fiber reinforced PVC pre-dip material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1: A kind of continuous glass fiber reinforced PVC prepreg is made by the following method:

[0025] (1) Take by weight 22 parts of PVC resin; 15 parts of plasticizer (8 parts of DOP, 7 parts of DBP); 3 parts of heat stabilizer (1 part of dibasic lead phosphite, 2 parts of tribasic lead phosphate ); 1.5 parts of lubricant (0.6 part of barium stearate, 0.3 part of lead stearate, 0.6 part of stearic acid); 1 part of light stabilizer uv944; 3 parts of grafting agent maleic anhydride grafted polyethylene.

[0026] (2) After accurately weighing various raw materials and additives, pour the PVC resin and plasticizer into the high-speed mixer, and then start the high-speed mixer at a low speed. After mixing at a low speed for 3 minutes, pour the heat stabilizer, lubricant, light stabilizer, and grafting agent into the high-speed mixer in sequence, and start the high-speed mixer at a low speed. After mixing for a period of time, when the temperature in the high-spee...

Embodiment 2

[0028] Embodiment 2: A kind of continuous basalt fiber reinforced PVC prepreg is made by the following method:

[0029] (1) Take by weight 25 parts of PVC resin; 18 parts of plasticizer (10 parts of DOP, 8 parts of DBP); 2 parts of heat stabilizer (0.6 part of dibasic lead phosphite, 1.4 parts of tribasic lead phosphate ); 1.5 parts of lubricant (0.6 part of barium stearate, 0.3 part of lead stearate, 0.6 part of stearic acid); 0.6 part of light stabilizer uv944; 2 parts of grafting agent maleic anhydride grafted polyethylene.

[0030] (2) After accurately weighing various raw materials and additives, pour the PVC resin and plasticizer into the high-speed mixer, and then start the high-speed mixer at a low speed. After mixing at a low speed for 3 minutes, pour the heat stabilizer, lubricant, light stabilizer, and grafting agent into the high-speed mixer in sequence, and start the high-speed mixer at a low speed. After mixing for a period of time, when the temperature in the h...

Embodiment 3

[0034]Embodiment 3: A kind of continuous carbon fiber reinforced PVC prepreg is made by the following method:

[0035] (1) Take by weight 30 parts of PVC resin; 20 parts of plasticizer (12 parts of DOP, 8 parts of DBP); 2 parts of heat stabilizer (0.6 parts of dibasic lead phosphite, 1.4 parts of tribasic lead phosphate ); 1.5 parts of lubricant (0.6 part of barium stearate, 0.3 part of lead stearate, 0.6 part of stearic acid); 0.6 part of light stabilizer uv944; 2 parts of grafting agent maleic anhydride grafted polyethylene.

[0036] (2) After accurately weighing various raw materials and additives, pour the PVC resin and plasticizer into the high-speed mixer, and then start the high-speed mixer at a low speed. After mixing at a low speed for 3 minutes, pour the heat stabilizer, lubricant, light stabilizer, and grafting agent into the high-speed mixer in sequence, and start the high-speed mixer at a low speed. After mixing for a period of time, when the temperature in the h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a continuous fiber reinforced PVC pre-dip material and a preparation method thereof. The continuous fiber reinforced PVC pre-dip material comprises the following components: 50-60 parts of continuous fiber, 20-30 parts of thermoplastic resin, 15-20 parts of a plasticizer, 1-3 parts of a heat stabilizer, 0.5-1.5 parts of a lubricant, 0.5-1 part of a light stabilizer, and 1-3 parts of a grafting agent. The pre-dip material and the preparation method can solve the disadvantages of poor heat stability and poor liquidity of the original product, and the invention provides the moulding method with continuous production and stable performance, can keep the raw material characteristic with maximum degree, improves the processing moulding problem, can reach continuous production, and increases the comprehensive energy efficiency.

Description

technical field [0001] The invention belongs to the field of polymer materials, in particular to a continuous fiber reinforced PVC prepreg and a preparation method thereof. Background technique [0002] At present, with the development of composite materials, composite materials are widely used due to their specific strength, high specific stiffness and light density. One of the current development trends of composite materials is to replace traditional thermosetting epoxy composite materials with thermoplastic composite materials. . One of the reasons is that thermoplastic composite materials can be formed by simple heating, melting and cooling, and can be welded like metal. Therefore, the development of thermoplastic composite materials will bring about great changes in the future market. According to the "Thermoplastic Composite Materials Market" report released by MarketsandMarkets of the United States, by 2020, the market for thermoplastic composite materials will expa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/06C08K13/04C08K7/14C08K7/10C08K7/06C08K5/12C08K3/32C08K5/098C08K5/09C08K5/3492C08J5/24
CPCC08L27/06C08J5/24C08J2327/06C08J2451/06C08L2201/02C08L51/06C08K13/04C08K7/14C08K5/12C08K3/32C08K5/098C08K5/09C08K5/3492C08K7/10C08K7/06
Inventor 周海燕张雷鸣
Owner 红石极威实业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional