Water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent and application thereof

An antibacterial finishing agent, antibacterial finishing technology, applied in flame retardant fiber, fiber treatment, biochemical fiber treatment and other directions, can solve the problems of increasing economic cost, environmental burden of waste liquid, and high concentration of hydrophilic finishing agent process prescription, and achieve The effect of improving the degree of crosslinking, enhancing reactivity and softness, and excellent flame retardant effect

Inactive Publication Date: 2017-03-15
FOSHAN XUNTUOAO TECH CO LTD
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, due to the large concentration of the process prescription of the hydrophilic finishing agent, the economic cost is increased, and catalysts and other auxiliary agents need to be added during the use process, resulting in a large amount of industrial waste liquid and a burden on the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent and application thereof
  • Water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent and application thereof
  • Water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A water-soluble heat-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent consists of the following components in parts by weight:

[0040] Water-soluble heat-reactive polyurethane: 15 parts;

[0041] Acetylglutamine: 0.1 parts; Glycerin: 2 parts.

[0042] The water-soluble heat-reactive polyurethane is synthesized with isophorone diisocyanate, N-methyldiethanolamine and polypropylene glycol-2000 as main raw materials and methyl ethyl ketone oxime as a blocking agent.

[0043] The finishing liquid formula of the hydrophilic, flame-retardant and antibacterial finishing of the synthetic fiber fabric is:

Embodiment 2

[0045] A water-soluble heat-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent consists of the following components in parts by weight:

[0046] Water-soluble heat-reactive polyurethane: 20 parts;

[0047] Acetylglutamine: 10 parts; Glycerin: 12 parts.

[0048] The water-soluble heat-reactive polyurethane is synthesized with isophorone diisocyanate, N-methyldiethanolamine and polypropylene glycol-2000 as main raw materials and methyl ethyl ketone oxime as a blocking agent.

Embodiment 3

[0050] A water-soluble heat-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent consists of the following components in parts by weight:

[0051] Water-soluble heat-reactive polyurethane: 15 parts;

[0052] Acetylglutamine: 0.5 parts; Glycerin: 4.0 parts.

[0053] The water-soluble heat-reactive polyurethane is synthesized by reacting polyether and isocyanate to obtain a polyurethane prepolymer, and then using sodium bisulfite as a blocking agent to react with the prepolymer.

[0054] The finishing liquid formula of the hydrophilic, flame-retardant and antibacterial finishing of the synthetic fiber fabric is:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of textile auxiliary agents, and discloses a water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent. The water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent comprises components by following weight part: 15-20 parts of water-soluble thermal-reactive polyurethane, 0.1-10 parts of aceglutamide and 2-12 parts of glycerol. The aceglutamide is added as an additive in the finishing agent, and the water-soluble thermal-reactive polyurethane hydrophilic, flame-retardant and antibacterial finishing agent can catalyze proceeding of reaction and significantly improve crosslinking rate of the polyurethane and synthetic fibers, the lower concentration polyurethane can endow the synthetic fibers and wool fibers with lasting hydrophilicity, and simultaneously significantly enhances reactivity and softness, and is high in durability, and a fabric after being tidied not only has good hydrophilicity, but also has fire resistance and antibacterial performance.

Description

[0001] Technical field: [0002] The invention relates to the technical field of textile auxiliaries, in particular to a water-soluble heat-reactive polyurethane finishing agent. [0003] Background technique: [0004] Heat-responsive water-soluble polyurethane is a series of additives used in the textile finishing process that were successfully developed by Daiichi Kogyo Pharmaceutical Company of Japan and Bayer Company of Germany in the early 1970s after more than 10 years of research and development. Since this series of products does not contain formaldehyde, APEO, or solvent, it has been widely used in Western textile processing in Europe, America, and Japan since it was put into the market in the late 1980s. [0005] The main application of heat-responsive water-soluble polyurethane is anti-wrinkle and anti-shrinkage processing of wool and silk fabrics, anti-wrinkle and anti-shrinkage processing of cotton and linen fabrics, long-lasting water-absorbing and anti-static fin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/568D06M13/148D06M13/402D06M101/06D06M101/12D06M101/10D06M101/32
CPCD06M15/568D06M13/148D06M13/402D06M16/00D06M2101/06D06M2101/10D06M2101/12D06M2101/32D06M2200/20D06M2200/30
Inventor 付淑珍
Owner FOSHAN XUNTUOAO TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com