Alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry and preparation method thereof

An anti-sedimentation and nanotechnology, applied in the direction of coating, etc., can solve the problems of high sedimentation rate, short storage time, limited use, etc., achieve fast dispersion effect and save dispersion time

Active Publication Date: 2017-03-22
GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the preparation process of ATO nano thermal insulation slurry, it is easy to form aggregates due to the surface force of ATO particles and the existence of bridge bonds. During the storage process of ATO nano thermal insulation slurry, a high sedimentation rate will occur, thus causing the current The storage time of ATO nano thermal insulation slurry in the market is short, which leads to the limited use of this product in the process of use and promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry and preparation method thereof
  • Alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry and preparation method thereof
  • Alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment 1 provides an alcoholic nano-transparent infrared heat-insulating anti-sedimentation slurry, which comprises the following components in parts by mass: 8 parts of ATO nano antimony-doped tin dioxide, 3 parts of absolute ethanol, D 5 parts of type dispersant, 6 parts of P type dispersant, and 1 part of sodium hydroxide.

[0034] Among them, the D-type dispersant in Example 1 is alkanol ammonium salt DISPERBYK180, and the P-type dispersant is polyethyleneimine PEI.

[0035] The preparation method of the alcoholic nano-transparent infrared heat-insulating and anti-sedimentation slurry of the present embodiment 1, the specific operation steps are as follows: put the ATO nano-antimony-doped tin dioxide and dehydrated alcohol of the said portion into the container, and use a magnetic stirring bar Mix evenly, put the mixture of ATO nano antimony-doped tin dioxide and absolute ethanol into the powder disperser, and put the D-type dispersant of the said amount in...

Embodiment 2

[0037] This embodiment 2 provides an alcoholic nano-transparent infrared heat-insulating anti-sedimentation slurry, which comprises the following components according to mass dispersion: 9 parts of ATO nano antimony-doped tin dioxide, 4 parts of isopropanol, D type 6 parts of dispersant, 7 parts of P-type dispersant, and 1 part of potassium hydroxide.

[0038] Among them, the D-type dispersant in Example 2 is alkanol ammonium salt DISPERBYK194, and the P-type dispersant is polyethyleneimine PEI.

[0039] The preparation method of the alcoholic nano-transparent infrared heat-insulating and anti-sedimentation slurry of the present embodiment 2, the specific operation steps are as follows: put the ATO nanometer antimony-doped tin dioxide and isopropyl alcohol into the container, and use a magnetic stirring bar Mix evenly, put the mixture of ATO nanometer antimony-doped tin dioxide and isopropanol into the powder disperser, and put the D-type dispersant of the said amount into the...

Embodiment 3

[0041]This embodiment 3 provides an alcoholic nano-transparent infrared thermal insulation and anti-sedimentation slurry, which comprises the following components according to mass dispersion: 10 parts of ATO nano antimony-doped tin dioxide, 5 parts of isobutanol, D type 7 parts of dispersant, 8 parts of P-type dispersant, 1 part of sodium hydroxide and 1 part of potassium hydroxide.

[0042] Among them, the D-type dispersant in Example 3 is alkanol ammonium salt DISPERBYK194, and the P-type dispersant is polyethyleneimine PEI.

[0043] The preparation method of the alcoholic nano-transparent infrared heat-insulating and anti-sedimentation slurry of the present embodiment 3, the specific operation steps are as follows: put the ATO nanometer antimony-doped tin dioxide and isobutanol into the container, and use a magnetic stirring bar Mix evenly, put the mixture of ATO nanometer antimony-doped tin dioxide and isobutanol into the powder disperser, and put the D-type dispersant of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry and a preparation method thereof. The alcoholic nano transparent infrared thermal insulation anti-sedimentation slurry comprises the following components in parts by mass: 8-12 parts of ATO nano stibium-doped tin dioxide, 3-6 pats of an alcohol solvent, 5-10 parts of a D type dispersant, 6-12 parts of P type dispersant and a pH adjustor; the D type dispersant is macromolecular multivalent carboxylate, the P type dispersant is methyl silicate, and the dosage of the pH adjustor is based on adjustment of the pH value of the slurry to 8-10. According to the slurry and the preparation method, the sedimentation rate of the ATO nano thermal insulation slurry in an alcohol solvent is effectively reduced, the dispersing effect and stability of the slurry are enhanced, and the storage time of the slurry is prolonged.

Description

technical field [0001] The invention relates to the field of building energy-saving glass heat-insulating slurry, in particular to an alcohol-based nano-transparent infrared heat-insulating and anti-settling slurry and a preparation method thereof. Background technique [0002] In the building envelope, the thermal performance of glass has always been the biggest factor affecting building energy consumption and human comfort. Ordinary single-layer glass usually produces a large energy loss in the building envelope, especially when the indoor and outdoor temperature difference is large, the air-conditioning load will be lost by 20-30% through the glass, resulting in energy consumption. In order to improve the heat insulation performance of glass and reduce building energy consumption, various forms of energy-saving glass such as filmed glass and coated glass have appeared on the market in recent years, which have achieved the purpose of building energy conservation to a large...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12C09D7/00
CPCC09D7/20C09D7/61C09D7/63C09D7/65
Inventor 张楠李宁孟庆林杨建坤江向阳
Owner GUANGZHOU INSTITUTE OF BUILDING SCIENCE CO LTD