Modified magnesium cement
A magnesium cement and modification technology, applied in the field of magnesium cement materials, can solve the problems of easy deformation and cracking, strong thermal expansion, low mechanical strength, etc., and achieve good compressive performance, strong rigidity, and high gel strength.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0009] Example 1: A modified magnesium cement, which is made by mixing 100 parts of magnesium oxide, 100 parts of 30% magnesium sulfate aqueous solution, 0.1 part of citric acid or sodium citrate, and 100 parts of fly ash as fillers. , Its compressive performance is 75MPa.
Example Embodiment
[0010] Example two, a modified magnesium cement composed of 100 parts of magnesium oxide, 85 parts of magnesium sulfate aqueous solution with a concentration of 35%, 1 part of modifier mixed with citric acid or sodium citrate and aluminum sulfate, and 110 parts of silicon Ash is made by mixing and stirring fillers, and its compressive performance is 90MPa.
Example Embodiment
[0011] Example three, a modified magnesium cement, consisting of 100 parts of magnesium oxide, 90 parts of a 40% magnesium sulfate aqueous solution, 2 parts of modifiers mixed with citric acid or sodium citrate and potassium aluminum sulfate, 150 parts The slag is mixed and stirred with fillers, and its compressive performance is 105MPa.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap