Non-oil-penetrating type creep rubber waterproof coating and a preparing method thereof

A waterproof coating and creep technology, applied in recycled rubber coatings, asphalt coatings, chloroprene homopolymer coatings, etc., to prevent water channeling, excellent durability, and excellent bonding performance.

Active Publication Date: 2017-04-19
明象新材料科技(上海)有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the above-mentioned defects of existing waterproof materials, and propose a non-oil-s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A non-oil-penetrating creep rubber waterproof coating, calculated by mass percentage, its component ratio is as follows:

[0037] Butyl rubber 5%;

[0038] SBR 7%;

[0039] Polymer modifier 8%;

[0040] Bitumen 15%;

[0041] Inorganic modifier 10%;

[0042] Rubber powder 55%;

[0043] The rubber powder is a mixture of reclaimed rubber and nitrile rubber; the asphalt is a mixture of 70# and 90# petroleum asphalt; base) tetrasulfide, bis(triethoxysilylpropyl) disulfide, γ-mercaptopropyltrimethoxysilane, oxidized polyethylene wax, ethylene-ethyl acetate copolymerized mixture; the inorganic modification The material is a mixture of vitrified microspheres and light calcium powder.

[0044] In this example, the rubber powder is firstly modified, a modifier is added, and modified by high pressure or screw extrusion to form modified rubber particles, and then heated and mixed with other materials to form a finished product, so that the rubber powder is in the overall mass...

Embodiment 2

[0051] A non-oil-penetrating creep rubber waterproof coating, calculated by mass percentage, its component ratio is as follows:

[0052] Butyl rubber 15%;

[0053] SBR 5%;

[0054] Polymer modifier 10%;

[0055] Bitumen 20%;

[0056] Inorganic modifier 10%;

[0057] Rubber powder 40%;

[0058] The rubber powder is a mixture of reclaimed rubber and neoprene; the asphalt is 90# petroleum asphalt; the polymer modifier is polypropylene, two (triethoxysilylpropyl) disulfide , γ-mercaptopropyltrimethoxysilane mixture; the inorganic modifier is a mixture of vitrified microspheres and light calcium powder.

Embodiment 3

[0060] A non-oil-penetrating creep rubber waterproof coating, calculated by mass percentage, its component ratio is as follows:

[0061] Butyl rubber 5%;

[0062] SBR 5%;

[0063] Polymer modifier 15%;

[0064] Bitumen 25%;

[0065] Inorganic modifier 15%;

[0066] Rubber powder 35%;

[0067] The rubber powder is a mixture of reclaimed rubber and neoprene; the asphalt is 90# petroleum asphalt; the polymer modifier is polystyrene, two (triethoxysilylpropyl) disulfide compound, γ-mercaptopropyltrimethoxysilane, oxidized polyethylene wax, and ethylene-ethyl acetate copolymerized wax; the inorganic modifier is a mixture of vitrified microspheres and light calcium powder.

[0068] The non-oil-seepage creep rubber waterproof coating prepared in the above examples was applied on a neutral filter paper, put into an incubator at 60°C for 2 hours and taken out for testing. No oil seeped out from the back of the filter paper. And the measured VOC content is less than 10, there is n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to non-oil-penetrating type creep rubber waterproof coating. The coating is characterized in that the coating includes, by mass, 3-20% of butyl rubber, 5-10% of styrene-butadiene rubber, 35-60% of rubber powder, 5-20% of a polymer modifying agent, 5-25% of asphalt and 5-15% of an inorganic modifying material; the polymer modifying agent is one of or a mixture of materials selected from a group consisting of polypropylene, polystyrene, bis(triethoxysilylpropyl) tetrasulfide, bis(triethoxysilylpropyl) disulfide, gamma-mercaptopropyl trimethoxysilane, oxidized polyethylene wax and ethylene-vinyl acetate copolymer wax; and the inorganic modifying material is glass microbeads, precipitated calcium carbonate powder, talcum powder, ground calcium carbonate powder or a mixture thereof. The actually measured VOC content of the coating is less than 10, and no oil is penetrated at 60 DEG C.

Description

technical field [0001] The invention relates to a non-oil-seepage creep rubber waterproof coating and a preparation method thereof, which are applied to building waterproofing and leakage plugging and repairing industries. [0002] technical background [0003] At present, architectural waterproof coatings mainly include epoxy coatings, asphalt modified coatings, and polyurethane coatings. [0004] Among them, non-curing rubber asphalt coatings have appeared in asphalt-modified coatings in recent years. Most of them use high-flash-point solvent oil and a small amount of rubber powder to add a large amount of modified asphalt coatings to the modified asphalt coatings. They are formed by physical heating and mixing. The solid content of these non-curing coatings The test is carried out at 105 degrees with a thermal balance for testing, but in fact a large amount of high-flash point solvent oil (flash point greater than 105 degrees) is added. Such products are used in actual pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D117/00C09D109/02C09D111/00C09D109/06C09D123/22C09D123/06C09D123/30C09D123/08C09D195/00C09D123/12C09D7/12
Inventor 郑建张念明许俊
Owner 明象新材料科技(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap