A kind of non-oil-seepage creep rubber waterproof coating and preparation method thereof

A waterproof coating and creep technology, applied in recycled rubber coatings, asphalt coatings, chloroprene homopolymer coatings, etc., to prevent water channeling, excellent durability, and excellent bonding performance.

Active Publication Date: 2020-07-10
明象新型建材科技(上海)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the above-mentioned defects of existing waterproof materials, and propose a non-oil-seepage creep rubber waterproof coating with extremely low VOC. Technical Problems of Coating Oil Seepage and Waterproof Membrane Construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A non-oil-permeable creep rubber waterproof coating, calculated in mass percentage, its component ratio is as follows:

[0037] Butyl rubber 5%;

[0038] SBR 7%;

[0039] Polymer modifier 8%;

[0040] Asphalt 15%;

[0041] Inorganic modifier 10%;

[0042] Rubber powder 55%;

[0043] The rubber powder is a mixture of reclaimed rubber and nitrile rubber; the asphalt is a mixture of 70# and 90# petroleum asphalt; the polymer modifier is polyethylene, bis(triethoxysilicone propylene) base) tetrasulfide, bis(triethoxysilylpropyl) disulfide, γ-mercaptopropyl trimethoxysilane, oxidized polyethylene wax, ethylene-ethyl acetate copolymerized mixture; the inorganic modification The material is a mixture of vitrified microbeads and light calcium powder.

[0044] In this example, the rubber powder is first modified, and a modifier is added and modified by high pressure or screw extrusion to form modified rubber particles, which are then heated and mixed with other materials t...

Embodiment 2

[0051] A non-oil-permeable creep rubber waterproof coating, calculated in mass percentage, its component ratio is as follows:

[0052] Butyl rubber 15%;

[0053] SBR 5%;

[0054] Polymer modifier 10%;

[0055] Asphalt 20%;

[0056] Inorganic modifier 10%;

[0057] Rubber powder 40%;

[0058] The rubber powder is a mixture of reclaimed rubber and chloroprene rubber; the asphalt is 90# petroleum asphalt; the polymer modifier is polypropylene, bis(triethoxysilylpropyl) disulfide , a mixture of γ-mercaptopropyl trimethoxysilane; the inorganic modified material is a mixture of vitrified microbeads and light calcium powder.

Embodiment 3

[0060] A non-oil-permeable creep rubber waterproof coating, calculated in mass percentage, its component ratio is as follows:

[0061] Butyl rubber 5%;

[0062] SBR 5%;

[0063] Polymer modifier 15%;

[0064] Asphalt 25%;

[0065] Inorganic modifier 15%;

[0066] Rubber powder 35%;

[0067] The rubber powder is a mixture of reclaimed rubber and chloroprene rubber; the asphalt is 90# petroleum asphalt; the polymer modifier is polystyrene, bis(triethoxysilylpropyl) disulfide compound, γ-mercaptopropyl trimethoxysilane, oxidized polyethylene wax, and ethylene-ethyl acetate copolymer wax; the inorganic modifier is a mixture of vitrified microbeads and light calcium powder.

[0068] The non-oil-permeable creep rubber waterproof coating prepared in the above example was smeared on neutral filter paper, put into an incubator at 60 degrees Celsius for 2 hours, and taken out for testing. There was no oil leakage on the back of the filter paper. And the measured VOC content is les...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to non-oil-penetrating type creep rubber waterproof coating. The coating is characterized in that the coating includes, by mass, 3-20% of butyl rubber, 5-10% of styrene-butadiene rubber, 35-60% of rubber powder, 5-20% of a polymer modifying agent, 5-25% of asphalt and 5-15% of an inorganic modifying material; the polymer modifying agent is one of or a mixture of materials selected from a group consisting of polypropylene, polystyrene, bis(triethoxysilylpropyl) tetrasulfide, bis(triethoxysilylpropyl) disulfide, gamma-mercaptopropyl trimethoxysilane, oxidized polyethylene wax and ethylene-vinyl acetate copolymer wax; and the inorganic modifying material is glass microbeads, precipitated calcium carbonate powder, talcum powder, ground calcium carbonate powder or a mixture thereof. The actually measured VOC content of the coating is less than 10, and no oil is penetrated at 60 DEG C.

Description

technical field [0001] The invention relates to a non-oil-permeable creeping rubber waterproof coating and a preparation method thereof, which are applied to the construction waterproofing and leakage plugging and repairing industries. [0002] technical background [0003] At present, architectural waterproof coatings mainly include epoxy coatings, asphalt modified coatings, and polyurethane coatings. [0004] Among them, asphalt modified coatings have appeared non-cured rubber asphalt coatings in recent years. Most of them are high-flash point solvent oil and a small amount of rubber powder added to the modified asphalt coatings in large quantities, and formed by physical heating and mixing. The solid content of these non-cured coatings The test was carried out at 105 degrees by weighing with a thermobalance, but in reality, a large amount of high flash point solvent oil (flash point greater than 105 degrees) was added. Such a product is used in actual engineering, and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D117/00C09D109/02C09D111/00C09D109/06C09D123/22C09D123/06C09D123/30C09D123/08C09D195/00C09D123/12C09D7/61C09D7/63
Inventor 郑建张念明许俊
Owner 明象新型建材科技(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap