Dental restoration photocuring ceramic material and application thereof

A technology of oral restorative and ceramic materials, which is applied in the fields of medical science, dentistry, dental preparations, etc., can solve the problems that the strength of ceramic materials cannot meet the needs of users, complex molding, and inconvenient curing molding, etc., to achieve strength enhancement, improve mechanical properties, The effect of improving the service life

Inactive Publication Date: 2017-04-26
东莞市永嘉义齿有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the development and application of ceramic restoration materials in recent years, the properties of oral ceramics have been greatly improved, and they have superior performance in many aspects. However, the molding of ceramics is more complicated, and it is inconvenient to solidify. Unable to meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: A light-cured ceramic material for dental restoration, in parts by weight, includes the following components:

[0026] 166 parts of nano-ceramic powder from Nanjing Xiaoke Nano Ceramic Technology Development Co., Ltd.; 5 parts of dispersant; 2 parts of photoinitiator from BASF Group; 20 parts of main monomer; 30 parts of diluted monomer; 1 part of colorant; filler 35 parts; 0.15 parts of fluoride ion source;

[0027] The filling material is composed of silanized and zirconated calcium phosphate, nano zirconia, and nano diamond, and the parts by weight of each component in the filling material are: 0.07 part of calcium phosphate, 0.09 part of nano zirconia, and 0.07 part of nano diamond.

[0028] The invention provides a light-cured ceramic material for dental restoration. The invention adopts nano-ceramic powder, which can effectively enhance the strength, toughness and superplasticity of the material, and add silanization and zirconium during the curing p...

Embodiment 2

[0033] Embodiment 2: A light-cured ceramic material for dental restoration, in parts by weight, includes the following components:

[0034] 177 parts of nano-ceramic powder from Nanjing Xiaoke Nano Ceramic Technology Development Co., Ltd.; 6 parts of dispersant; 1 part of photoinitiator from BASF Group; 40 parts of main monomer; 37 parts of diluted monomer; 1 part of colorant; filler 46 parts; 0.1 part of fluoride ion source;

[0035] The nano-ceramic powder is prepared by mixing titanium and boron carbide according to the weight ratio of 3:2, and is prepared by high-energy mechanical ball milling. Boron carbide and titanium react completely, which maximizes the formation of the prepared nano-ceramic material. Denture hardness and strength.

[0036] The filling material is composed of silanized and zirconated calcium phosphate, nano zirconia and nano diamond, and the parts by weight of each component in the filling material are: 0.09 part of calcium phosphate, 0.12 part of na...

Embodiment 3

[0037] Embodiment 3: A light-cured ceramic material for dental restoration, in parts by weight, includes the following components:

[0038] 185 parts of nano-ceramic powder from Nanjing Xiaoke Nano Ceramic Technology Development Co., Ltd.; 8 parts of dispersant; 2 parts of photoinitiator from BASF Group; 42 parts of main monomer; 39 parts of diluted monomer; 1 part of colorant; filler 48 parts; 0.2 parts of fluoride ion source;

[0039] The nano-ceramic powder is prepared by high-energy mechanical ball milling after mixing titanium and boron carbide at a weight ratio of 3:1.

[0040] The filling material is composed of silanized and zirconated calcium phosphate, nano zirconia, and nano diamond, and the parts by weight of each component in the filling material are: 0.06 part of calcium phosphate, 0.05-0.15 part of nano zirconia, and 0.1 part of nano diamond.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of dental restoration materials, in particular to a dental restoration photocuring ceramic material and application thereof. The material is used for restoration of dental caries and tooth defects. The dental restoration photocuring ceramic material is prepared from, by weight, 166-187 parts of nanometer ceramic powder, 5-8 parts of a dispersing agent, 1-2 parts of a photoinitiator, 15-45 parts of a main monomer, 15-45 parts of a diluting monomer, 1-2 parts of a coloring agent, 27-55 parts of fillings and 0.5-1 part of a fluorine ion source, wherein the fillings are prepared from silanized and zirconated calcium phosphate, nano-zirconia and nano-diamond. The material has the advantages of being high in strength and curing speed, stable in curing effect and capable of effectively prolonging the service life.

Description

technical field [0001] The invention relates to the field of oral restorative materials, in particular to a light-cured ceramic material for oral restorative and its application. Background technique [0002] Restorative materials used to repair tooth defects caused by dental caries, trauma, etc. are mainly divided into three categories: alloy materials, porcelain materials and composite resins. Because light-curing composite resin is one of the commonly used filling materials and repair materials in the department of stomatology, and it has a beautiful appearance and is easy to operate clinically, it is more and more widely used in the field of stomatology. [0003] However, with the development and application of ceramic restoration materials in recent years, the properties of oral ceramics have been greatly improved, and they have superior performance in many aspects. However, the molding of ceramics is more complicated, and it is inconvenient to solidify. Can not meet t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/02A61K6/033A61K6/027A61K6/00A61K6/838
CPCA61K6/71A61K6/75A61K6/802A61K6/831
Inventor 胡永国何东艳
Owner 东莞市永嘉义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap