Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Environment-friendly low-temperature-resistant fire-retardant complex plasticizer

A flame retardant compounding and plasticizer technology, applied in the field of plasticizers, can solve problems such as low mechanical properties of plasticizer products, and achieve improved flame retardant performance, low temperature resistance, low volatility, and high plasticizing efficiency. Effect

Inactive Publication Date: 2017-04-26
JIANGSU SENHE CHEM TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (2) How to improve the technical problem of the low mechanical properties of the plasticizer product of the present invention due to the addition of the low temperature flame retardant system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] This embodiment is an environment-friendly, low-temperature resistant and flame-retardant composite plasticizer, including a plasticizer matrix, which is made of sebacic acid, decyl alcohol, catalyst, sodium carbonate and auxiliary materials through esterification, refining, pressure filtration refining, Prepared by distillation; the weight ratio of sebacic acid and decanol is: sebacic acid: 1 part, decanol: 1.57 parts; the addition amount of catalyst is 0.2% of the total weight of sebacic acid and decanol, the The addition amount is 0.1% of the total weight of sebacic acid and decanol, and the addition amount of auxiliary materials is 0.3% of the total weight of sebacic acid and decanol; 1.7% of the weight of the plastic matrix; the components by weight of the flame retardant system are: nano-silica: 8.7 parts, fumed silica: 3.5 parts, methyl hydrogen silicone oil: 71 parts, hydroxyl polydimethyl Base siloxane: 9.7 parts, vinyl trimethoxysilane: 3 parts, ammonium polyp...

Embodiment 2

[0027]This embodiment is an environment-friendly, low-temperature resistant and flame-retardant composite plasticizer, including a plasticizer matrix, which is made of sebacic acid, decyl alcohol, catalyst, sodium carbonate and auxiliary materials through esterification, refining, pressure filtration refining, Prepared by distillation; the weight ratio of sebacic acid and decanol is: sebacic acid: 1 part, decanol: 3 parts; the addition amount of the catalyst is 0.6% of the total weight of sebacic acid and decanol, and the amount of sodium carbonate The addition amount is 0.5% of the total weight of sebacic acid and decanol, and the addition amount of auxiliary materials is 0.6% of the total weight of sebacic acid and decanol; 1.8% of the weight of the plastic matrix; the components by weight of the low-temperature flame-retardant system are: nano-silica: 8.8 parts, fumed silica: 3.6 parts, methyl hydrogen-containing silicone oil: 72 parts, hydroxyl poly Dimethyl siloxane: 9.8 ...

Embodiment 3

[0035] This embodiment is an environment-friendly, low-temperature resistant and flame-retardant composite plasticizer, including a plasticizer matrix, which is made of sebacic acid, decyl alcohol, catalyst, sodium carbonate and auxiliary materials through esterification, refining, pressure filtration refining, Prepared by distillation; the weight ratio of sebacic acid and decyl alcohol is: sebacic acid: 1 part, decyl alcohol: 5 parts; the addition of catalyst is 1% of the total weight of sebacic acid and decyl alcohol, sodium carbonate The addition amount is 0.7% of the total weight of sebacic acid and decanol, and the addition amount of auxiliary materials is 1% of the total weight of sebacic acid and decanol; 1.9% of the weight of the plastic matrix; the components by weight of the low-temperature flame-retardant system are: nano-silica: 8.9 parts, fumed silica: 3.7 parts, methyl hydrogen-containing silicone oil: 73 parts, hydroxyl poly Dimethicone: 9.9 parts, vinyltrimetho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention discloses an environment-friendly low-temperature-resistant fire-retardant complex plasticizer, comprising a matrix of the plasticizer, the matrix is prepared from sebacic acid, decyl alcohol, a catalyst, sodium carbonate and an auxiliary by exetrification, refining, filter-press refining and distilling. The weight ratio of sebacic acid to decyl alcohol is 1 to 1.57-5. The adding amount of the catalyst is 0.2-1% of the total weight of sebacic acid and decyl alcohol, the adding amount of sodium carbonate is 0.1-0.7% of the total weight of sebacic acid and decyl alcohol and the adding amount of the auxiliary is 0.3-1% of the total weight of sebacic acid and decyl alcohol. The plasticizer also comprises a low-temperature-resistant fire-retardant system. The plasticizer disclosed by the invention has the advantages of great environmental friendliness, high plasticizing efficiency, low-temperature resistance, low volatility, extremely low volatility and great stability.

Description

technical field [0001] The invention relates to a plasticizer, in particular to an environment-friendly low temperature resistant flame retardant composite plasticizer. Background technique [0002] Plasticizer is a kind of polymer material additives. There are many kinds. The most common variety is DEHP (commercial name DOP). DEHP chemical name is bis(2-ethylhexyl) phthalate, which is a colorless , Odorless liquid, widely used in industry. Plasticizer is a polymer material additive widely used in industry. Adding this substance in plastic processing can make it more flexible, easy to process, and can be legally used for industrial purposes. The existing ordinary low-temperature resistant plasticizers are easy to volatilize because of their small molecular weight and low boiling point. After long-term use, the plasticizers will precipitate from the product, which directly affects the low temperature resistance of the product and the life of the product. It is easy to harden...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K13/02C08K5/11C08K3/36C08K5/5425C08K3/32C08K3/16C07C67/08C07C67/48C07C69/50
CPCC08K13/02C07C67/08C07C67/48C08K3/16C08K3/32C08K3/36C08K5/11C08K5/5425C08K2003/323C08K2201/003C08K2201/011C08K2201/014C08L2201/02C08L2201/04
Inventor 吴胜刚丁磊
Owner JIANGSU SENHE CHEM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com