Anti-corrosive paint for low-carbon steel valve and preparation method of anti-corrosive paint

A technology for anti-corrosion coatings and low-carbon steel, applied in the direction of anti-corrosion coatings, conductive coatings, polyamide coatings, etc., can solve the research and discussion of conductive copolymer/inorganic composites, which are rarely reported, and achieve the ability to enhance the ability to inhibit anodic reactions , slow down the corrosion reaction, the effect of good electrical conductivity

Inactive Publication Date: 2017-04-26
TONGLING JINGWEI FLUID SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, scholars at home and abroad have done a lot of research on the synthesis, structure and performance of conductive homopolymers and their inorganic composites, but there are few reports on the research and discussion of conductive copolymers / inorganic composites.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A kind of anticorrosion paint for low-carbon steel valve, it is made of the raw material of following parts by weight:

[0019] Sulfosalicylic acid 1, aniline 10, ammonium persulfate 0.1, pyrrole 10, tetrabutyl titanate 37, n-butanol 41, ethylene glycol butyl ether 70, epoxy resin E4080, polyamide resin 5, dimethyl Silicone oil 0.8.

[0020] A preparation method of the anti-corrosion coating for the low carbon steel valve, comprising the following steps:

[0021] (1) Add the above-mentioned ammonium persulfate into deionized water 100 times its weight, and stir evenly to obtain an initiator solution;

[0022] (2) Add the above-mentioned sulfosalicylic acid into deionized water 60 times its weight, stir evenly, add the above-mentioned aniline and pyrrole, put it into a water bath at 3°C, stir and react for 1 hour, add the above-mentioned tetrabutyl titanate Ester, discharge, increase the temperature to 74°C, add dropwise ammonia water with a concentration of 6%, adjust...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-corrosive paint for a low-carbon steel valve. The anti-corrosive paint is prepared from the following raw materials including, by weight, 1-2 parts of sulfosalicylic acid, 10-13 parts of aniline, 0.1-0.4 part of ammonium persulfate, 10-12 parts of pyrrole, 37-40 parts of tetrabutyl titanate, 41-50 parts of n-butyl alcohol, 70-90 parts of butyl cellosolve, 80-90 parts of epoxy resin E40, 5-7 parts of polyamide resin and 0.8-2 parts of dimethicone. The anti-corrosive paint has the advantages that the metal passivation capacity is enhanced, a layer of high-compactness oxidation film is generated on the surface of low alloy steel, the anodic reaction inhibiting capacity is enhanced, a base metal material and a corrosive medium are better isolated from each other, and the corrosion resistance is better.

Description

technical field [0001] The invention relates to the technical field of anti-corrosion coatings, in particular to an anti-corrosion coating for low-carbon steel valves and a preparation method thereof. Background technique [0002] The physical and chemical characteristics of nanoparticles are relatively unique, and there are some special effects such as micro volume, large surface, quantum size, and macro quantum tunnel. The conductivity of the conductive polymer compounded with nanoparticles has been greatly improved, making it applicable in new scientific research fields. According to the special properties of conductive polymers, conductive polymer composite materials are widely used in the fields of transmission and shielding of light, electricity, magnetism, microwaves, sensors, and metal anticorrosion; In-depth and extensive research on polymers, the development and application of conductive polymer corrosion-resistant coatings have become a reality. A large number o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D179/02C09D179/04C09D177/00C09D5/08C09D5/24C09D7/12
CPCC08L2205/02C08L2205/035C09D5/08C09D5/24C09D7/61C09D7/63C09D7/65C09D163/00C08L79/02C08L79/04C08L77/00C08L83/04C08K5/057C08K2003/2241C08K5/42
Inventor 吴寿涛
Owner TONGLING JINGWEI FLUID SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com