Acrylate tile back glue emulsion and preparation method thereof

An acrylate-based and acrylic-alkyl technology, which is applied in the field of acrylate-based tile adhesive backing emulsions, can solve the problems of high cost, further improvement of peel strength and cohesiveness, cumbersome processes, etc., and achieves improved stability and improved The effect of monomer conversion

Inactive Publication Date: 2017-04-26
佛山市顺德区巴德富实业有限公司
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the process of two-component brush-and-stick tile adhesive emulsion is c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]An emulsion for acrylic tile back adhesive, which is composed of the following raw materials in parts by weight: 100 parts of alkyl acrylate monomers; 20 parts of alkyl methacrylate monomers; 0.1 part of alkyl carboxylic acid; 1 part of monomer; 0.1 part of vinyltrioxysilane; 1 part of emulsifier; 0.1 part of initiator, 0.1 part of buffer, 100 parts of deionized water.

[0035] The alkyl acrylate monomer is methyl acrylate.

[0036] The alkyl methacrylate monomer is methyl methacrylate.

[0037] The alkyl carboxylic acid is acrylic acid.

[0038] The functional monomer is tert-butylaminoethyl methacrylate.

[0039] The emulsifier is a combined emulsifier, which is formed by mixing an anionic emulsifier and a nonionic emulsifier at a mass ratio of 1:1.

[0040] The anionic emulsifier is C 10 -C 20 Sodium Alkyl Sulfate.

[0041] The nonionic emulsifier is polyoxyethylene sorbitan monooleate.

[0042] The initiator is tert-butyl hydroperoxide.

[0043] Described buf...

Embodiment 2

[0054] An emulsion for acrylic tile back adhesive, which is composed of the following raw materials in parts by weight: 200 parts of alkyl acrylate monomers; 40 parts of alkyl methacrylate monomers; 3 parts of alkyl carboxylic acids; 3 parts of monomer; 3 parts of vinyltrioxysilane; 10 parts of emulsifier; 2 parts of initiator, 2 parts of buffer, 110 parts of deionized water.

[0055] The alkyl acrylate monomer is a mixture of methyl acrylate and ethyl acrylate.

[0056] The alkyl methacrylate monomer is a mixture of methyl methacrylate and ethyl methacrylate.

[0057] The alkyl carboxylic acid is a mixture of acrylic acid and methacrylic acid.

[0058] The functional monomer is a mixture of tert-butylaminoethyl methacrylate and dimethylaminoethyl methacrylate.

[0059] The emulsifier is a combination emulsifier formed by mixing an anionic emulsifier and a nonionic emulsifier at a mass ratio of 10:20.

[0060] The anionic emulsifier is C 10 -C 20 Sodium Alkyl Sulfate, C ...

Embodiment 3

[0074] An emulsion for acrylic tile back adhesive, which is composed of the following raw materials in parts by weight: 300 parts of alkyl acrylate monomers; 60 parts of alkyl methacrylate monomers; 5 parts of alkyl carboxylic acids; 5 parts of monomer; 5 parts of vinyltrioxysilane; 20 parts of emulsifier; 2.5 parts of initiator, 2.5 parts of buffer, 120 parts of deionized water.

[0075] The alkyl acrylate monomer is a mixture of methyl acrylate, ethyl acrylate and butyl acrylate.

[0076] The alkyl methacrylate monomer is a mixture of methyl methacrylate, ethyl methacrylate and propyl methacrylate.

[0077] The alkyl carboxylic acid is a mixture of acrylic acid, methacrylic acid and itaconic acid.

[0078] The functional monomer is a mixture of tert-butylaminoethyl methacrylate, dimethylaminoethyl methacrylate and N-methylolacrylamide.

[0079] The emulsifier is a combined emulsifier, which is formed by mixing an anionic emulsifier and a nonionic emulsifier at a mass ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an acrylate tile back glue emulsion and a preparation method thereof. The preparation method comprises preparation of a base material liquid A, preparation of a monomer solution B, preparation of an initiator solution C, preparation of a later added initiator solution D, pre-emulsification semi-continuous dropwise addtion, and later treatment processes. The emulsion comprises, by weight, 100 to 500 parts of an alkyl acrylate monomer, 20 to 100 parts of an alkyl methacrylate monomer, 0.1 to 10 parts of alkyl carboxylic acid, 1 to 10 parts of a functional monomer, 0.1 to 10 parts of vinyltrioxysilane, 1 to 30 parts of an emulsifier, 0.1 to 5 parts of an initiator, 0.1 to 5 parts of a buffering agent, and 100 to 150 parts of deionized water. The preparation method has the advantages of simple processes, low cost and safety. The emulsion has characteristics of good gloss, good water resistance, good weather resistance, high peel strength, high adhesion and instant-coating and instant-pasting of a single component.

Description

technical field [0001] The invention belongs to the field of macromolecular materials, and relates to an emulsion for acrylic tile back glue and a preparation method thereof. Background technique [0002] Tile back glue can effectively improve the bonding strength between the back of the brick and the bonding material, and solve the common problems of hollowing, peeling, and falling off of the wet tile in the decoration project. It is the most effective interface bonding reinforcement material at present. . Tile adhesives are mainly used to paste decorative materials such as ceramic tiles, facing tiles, and floor tiles, and are widely used in decorative decoration places such as interior and exterior walls, floors, bathrooms, and kitchens. Its main features are high bonding strength, water resistance, freeze-thaw resistance, good aging resistance and convenient construction. It is a very ideal bonding material. [0003] However, although the tile adhesives currently on the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J133/12C08F220/14C08F220/18C08F220/06C08F230/08C08F220/34C08F2/26C08F2/30
CPCC09J133/08C09J133/12C08F2/26C08F2/30C08F220/14C08F220/18C08F220/1818C08F220/1812C08F220/1808C08F220/1806C08F220/1804C08F220/1803C08F220/06C08F222/02C08F230/08C08F220/34C08F220/58C08F220/1802
Inventor 熊乐林耀辉杨文涛黄志林张维维何成
Owner 佛山市顺德区巴德富实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap