Decorative material for electric power tower

A decorative material and technology for power poles and towers, applied in the field of decorative materials, can solve problems such as shedding, exposed poles, and vulnerability to northern weather, etc., and achieve the effects of prolonging service life and cold resistance, reasonable compatibility, and structural stability

Inactive Publication Date: 2017-05-17
STATE GRID SHANDONG TANCHENG POWER SUPPLY +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the stability of the structure is relatively vulnerable to weather, especially to northern weather
Wind, frost, rain and snow, as well as severe summer and cold winter climate change greatly, the decorative materials such as marble or ceramic tiles can easily fall off from the power tower, causing the pole body to be exposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: Decorative materials for power poles and towers, including the following raw materials in parts by mass: 50-55 parts of cement, 180-190 parts of ceramic particles, 10-12 parts of hydroxyethyl cellulose ether, zirconium silicate powder or yttrium 6-8 parts of stabilized zirconia powder, 20-22 parts of styrene-acrylic latex powder, 5-6 parts of aluminum silicate, 4-5 parts of silicone water repellent, 4-5 parts of powder defoamer, 30-30 parts of polymer matrix 32 parts, phenolic fiber 25-27 parts, water glass 12-14 parts.

Embodiment 2

[0011] Embodiment 2: Decorative materials for power towers, including the following raw materials in parts by mass: 85 parts of cement, 50 parts of metakaolin, 8 parts of calcium hydrogen phosphate, 13 parts of zirconium silicate powder or yttrium-stabilized zirconia powder, butyric acid 5.5 parts of sodium, 6.3 parts of sodium humate, 3 parts of aluminum silicate, 3 parts of sodium tartrate, 16 parts of nano calcium carbonate, 15 parts of nano zeolite, and 3 parts of powder defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a decorative material for an electric power tower, belonging to the technical field of the decorative material. The decorative material mainly comprises the following raw materials in parts by weight: 80-85 parts of cement, 45-50 parts of metakaolin, 7-8 parts of calcium hydrophosphate, 12-13 parts of zirconium silicate powder or yttria-stabilized zirconia powder, 5.5 parts of sodium butyrate, 6.3 parts of sodium humate, 2-3 parts of aluminum silicate, 2-3 parts of sodium tartrate, 15-16 parts of nanometer calcium carbonate, 14-15 parts of nanometer zeolite and 2-3 parts of a powdered de-foaming agent. According to the decorative material, the formula is reasonable, the service life of gate post decorative material is greatly prolonged and the decorative material is mainly used for the electric power tower.

Description

technical field [0001] The invention belongs to the technical field of decorative materials, and in particular relates to a decorative material for power poles and towers. Background technique [0002] Existing power towers are usually as follows: first build the pole body with masonry concrete, then smooth the surface of the pole body with fine sand, and finally install decorative patches such as marble or ceramic tiles. But the stability of the structure is relatively vulnerable to the weather, especially to the northern weather. The wind, frost, rain, snow, and hot summer and winter climate change greatly, and decorative materials such as marble or ceramic tiles are easily detached from the power tower, causing the pole body to be exposed. Contents of the invention [0003] The purpose of the present invention is to overcome the above-mentioned defects and provide a decorative material for power poles and towers, which has reasonable compatibility and greatly prolongs ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/02C04B14/10C04B22/16C04B14/28
Inventor 纪涛
Owner STATE GRID SHANDONG TANCHENG POWER SUPPLY