Cement-based self-leveling mortar

A self-leveling mortar and cement-based technology, applied in the field of self-leveling mortar, can solve the problems of increased segregation and settlement, accelerated surface, and easy cracking of the surface, and achieves the effect of significantly reducing the cost and reducing the cost of raw materials.

Inactive Publication Date: 2017-05-17
北京宝辰联合科技股份有限公司
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this case, when ordinary cement-based self-leveling mortar is used as a leveling layer, there are at least the following problems: (1) When the construction thickness of self-leveling mortar is high, the degree of segregation and settlement will increase, that is, coarse aggregate It sinks and the mortar floats up, resulting in loose surface structure, prone to dusting, sanding and crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement-based self-leveling mortar

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Example 1

[0040] In terms of mass fraction, the component ratios are as follows: 160 parts of PII52.5 Portland cement, 55 parts of CA50 aluminate cement, 35 parts of anhydrite, 15 parts of bentonite, 125 parts of heavy calcium powder, 20-40 mesh washed river 200 parts of sand, 200 parts of 40-70 mesh washed river sand, 200 parts of 70-140 mesh washed river sand, 5 parts of redispersible polymer powder, 0.5 part of water reducing agent, 0.6 part of retarder, 0.8 part of cellulose ether, 0.8 part of defoamer, 0.3 part of lithium carbonate, 0.3 part of polypropylene fiber, and the mass ratio of water to material was 0.22 to prepare cement-based self-leveling mortar.

Example Embodiment

[0041] Example 2

[0042] In terms of mass fraction, the proportion of raw materials is as follows: 170 parts of PO42.5 Portland cement, 45 parts of CA50 aluminate cement, 35 parts of anhydrite, 20 parts of bentonite, 70 parts of heavy calcium powder, 20-40 mesh washing 150 parts of river sand, 250 parts of 40-70 mesh washed river sand, 250 parts of 70-140 mesh washed river sand, 5 parts of redispersible polymer powder, 0.6 part of water reducing agent, 0.5 part of retarder, 1 part of cellulose ether , 1.2 parts of defoaming agent, 0.5 part of lithium carbonate, 0.4 part of polypropylene fiber, and a water-material mass ratio of 0.21 to prepare cement-based self-leveling mortar.

Example Embodiment

[0043] Example 3

[0044] In terms of mass fraction, the proportion of raw materials is as follows: 165 parts of PO42.5 Portland cement, 45 parts of 52.5 sulfoaluminate cement, 40 parts of anhydrite, 15 parts of bentonite, 120 parts of heavy calcium powder, 20-40 mesh 150 parts of washed river sand, 250 parts of 40-70 mesh washed river sand, 200 parts of 70-140 mesh washed river sand, 10 parts of redispersible polymer powder, 0.4 part of water reducing agent, 0.5 part of retarder, 0.7 part of cellulose ether part, 1 part of defoamer, 0.5 part of lithium carbonate, 0.3 part of polypropylene fiber, and the mass ratio of water to material was 0.21 to prepare cement-based self-leveling mortar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses cement-based self-leveling mortar, which comprises the following components, by mass part, 160-180 parts of Portland cement, 40-55 parts of aluminate cement or sulphoaluminate cement, 30-40 parts of anhydrite, 15-25 parts of bentonite, 60-125 parts of heavy calcium carbonate powder, 600-650 parts of washed fluvial sand, 5-10 parts of redispersible emulsion powder, 0.4-0.6 part of a water reducer, 0.5-0.7 part of a retarder, 0.5-1.0 part of cellulose ether, 0.8-1.2 parts of an antifoaming agent and 0.3-0.5 part of an early strength agent. The cement-based self-leveling mortar is excellent in separation resistance, is low in cost, and is particularly suitable for a self-leveling layer with a relatively large thickness.

Description

technical field [0001] The invention belongs to the field of self-leveling mortar, in particular to a cement-based self-leveling mortar. Background technique [0002] Self-leveling mortar has excellent workability, can save labor, improve construction efficiency, and is widely used in architectural decoration projects. In the construction of floor materials, a leveling layer is usually laid on the base layer first, and then surface materials such as floor tiles, floors, and carpets are laid on top. [0003] When the ground base is relatively rough or there are pipes on it, the thickness of the self-leveling leveling layer must be high enough to pave the ground, and the local construction thickness can sometimes reach 5cm. In this case, when ordinary cement-based self-leveling mortar is used as a leveling layer, there are at least the following problems: (1) When the construction thickness of self-leveling mortar is high, the degree of segregation and settlement will increas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/16C04B111/62
CPCC04B28/16C04B2111/62C04B2201/50C04B7/02C04B7/32C04B14/104C04B14/28C04B14/068C04B24/383C04B22/10C04B16/0633C04B24/2623C04B2103/302C04B2103/22C04B2103/50
Inventor 戴浩
Owner 北京宝辰联合科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap