Anti-corrosive primer for automobile chassis

A technology for anti-corrosion primers and automobile chassis, which is applied in anti-corrosion coatings, biocide-containing paints, anti-fouling/underwater coatings, etc., and can solve problems such as health hazards for operators, reduced service life of equipment, and poor high temperature resistance , to achieve the effect of improving physical and mechanical properties, reducing rust and improving gloss

Inactive Publication Date: 2017-05-24
SUZHOU NIUDONG PRECISION MFG TECH CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many types of primers on the market, but they generally have the defects of slow drying, poor corrosion resistance, and poor high temperature resistance, which not only reduces the service life of the equipment, increases costs, but also leads to low work efficiency due to long drying time, and It is easy to emit chemical odor during processing, which will bring harm to the health of operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of anticorrosion primer for automobile chassis provided by the present embodiment is characterized in that: the primer is composed of bisphenol F type liquid epoxy resin, cellulose ether, aluminum powder, butyl acetate, multifunctional additive AMP-95, Composed of nano-silica, polysulfone and polyethylene glycol, its weight percent composition is: bisphenol F type liquid epoxy resin: 23%, cellulose ether: 5%, aluminum powder: 12%, butyl acetate: 10% %, multifunctional auxiliary agent AMP-95: 15%, nano-silica: 12%, polysulfone: 3%, and the balance is Polyethylene Glycol; The preparation method of this anti-corrosion primer for automobile chassis is carried out as follows:

[0033] Step (1): First, put the bisphenol F liquid epoxy resin and polyethylene glycol into the stirring tank for mixing, control the temperature in the stirring tank at 60°C, set the stirring speed at 900r / min, and stir for 2 hours , and then put in cellulose ether to continue stirring, the st...

Embodiment 2

[0038] A kind of anticorrosion primer for automobile chassis provided by the present embodiment is characterized in that: the primer is composed of bisphenol F type liquid epoxy resin, cellulose ether, aluminum powder, butyl acetate, multifunctional additive AMP-95, Composed of nano-silica, polysulfone and polyethylene glycol, its weight percent composition is: bisphenol F type liquid epoxy resin: 25%, cellulose ether: 8%, aluminum powder: 15%, butyl acetate: 12% %, multifunctional auxiliary agent AMP-95: 18%, nano-silica: 15%, polysulfone: 8%, and the balance is Polyethylene Glycol; The preparation method of this anti-corrosion primer for automobile chassis is carried out as follows:

[0039] Step (1): First, put the bisphenol F liquid epoxy resin and polyethylene glycol into the stirring tank for mixing, control the temperature in the stirring tank at 62°C, set the stirring speed at 920r / min, and stir for 3 hours , and then put in cellulose ether to continue stirring, the st...

Embodiment 3

[0044] A kind of anticorrosion primer for automobile chassis provided by the present embodiment is characterized in that: the primer is composed of bisphenol F type liquid epoxy resin, cellulose ether, aluminum powder, butyl acetate, multifunctional additive AMP-95, Composed of nano-silica, polysulfone and polyethylene glycol, its weight percentage composition is: bisphenol F type liquid epoxy resin: 24%, cellulose ether: 7%, aluminum powder: 13%, butyl acetate: 11% %, multifunctional auxiliary agent AMP-95: 17%, nano silicon dioxide: 13%, polysulfone: 5%, and the balance is Polyethylene Glycol; The preparation method of this anticorrosion primer for automobile chassis is carried out as follows:

[0045] Step (1): First put the bisphenol F type liquid epoxy resin and polyethylene glycol into the stirring tank for mixing, control the temperature in the stirring tank at 61°C, set the stirring speed at 910r / min, and stir for 2.5 h, then put into cellulose ether and continue to st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-corrosive primer for an automobile chassis. The primer is prepared from, by weight, 23-25% of bisphenol F-type liquid epoxy resin, 5-8% of cellulose ether, 12-15% of aluminum powder, 10-12% of butyl acetate, 15-18% of multifunctional additive AMP-95, 12-15% of nano silica, 3-8% of polysulfone and the balance polyethylene glycol. The invention further provides a preparation method of the anti-corrosive primer for the automobile chassis. The primer is quick to dry, free of peculiar smell, stable to alkali and most solvents and long in service life and has anti-corrosive and gas and water blocking properties and good friction and high temperature resisting performance.

Description

technical field [0001] The invention relates to an automobile chassis, in particular to an anti-corrosion primer for the automobile chassis. Background technique [0002] At present, many automobile chassis need to be painted with primer after surface treatment, and its main function is to protect the automobile chassis from being corroded by the atmosphere and sewage. There are many types of primers on the market, but they generally have the defects of slow drying, poor corrosion resistance, and poor high temperature resistance, which not only reduces the service life of the equipment, increases costs, but also leads to low work efficiency due to long drying time, and During the processing, it is easy to emit chemical odor, which is harmful to the health of operators. Contents of the invention [0003] The technical problem to be solved by this invention is to propose a kind of anticorrosion primer for automobile chassis, which has fast drying, no peculiar smell, stable ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/10C09D5/16C09D7/12
CPCC09D163/00C08K2201/011C08L2205/035C09D5/103C09D5/1662C09D5/1687C08L1/28C08L81/06C08L71/02C08K2003/0812C08K3/36C08K5/101C08K5/17
Inventor 汪海涛
Owner SUZHOU NIUDONG PRECISION MFG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More