Method for preparing high-length-diameter-ratio calcium sulfate nanowires under low-temperature conditions

A technology with high aspect ratio and low temperature conditions, applied in the direction of nanotechnology, calcium/strontium/barium sulfate, etc., can solve the problems of complex preparation process, high reaction temperature, and high equipment requirements, and achieve simple preparation process and low reaction temperature , good solubilizing effect
CN106745154AInactive Publication Date: 2017-05-31SHANGHAI UNIV
2 Cites 5 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
SHANGHAI UNIV
Publication Date
2017-05-31
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a method for preparing high-length-diameter-ratio calcium sulfate nanowires under low-temperature conditions. The method comprises the following steps: (1) preparing a sodium sulfate inverse microemulsion composed of n-pentanol, cyclohexane, sodium sulfate and cetyl trimethylammonium bromide; (2) preparing a calcium chloride inverse microemulsion composed of n-pentanol, cyclohexane, sodium sulfate and cetyl trimethylammonium bromide; (3) mixing the sodium sulfate inverse microemulsion prepared in the step (1) and the calcium chloride inverse microemulsion prepared in the step (2) to obtain a transparent uniform mixed microemulsion; (4) adding 4-12 vol% acetone or ethanol into the mixed microemulsion, and carrying out demulsification reaction; and (5) carrying out centrifugal separation on the demulsified mixed microemulsion, sequentially carrying out ultrasonic cleaning with acetone and ethanol, and drying to obtain the calcium sulfate nanowire product. The method has the advantages of simple technique, high efficiency and low cost, and implements continuous production. The prepared calcium sulfate nanowires have favorable solubilizing power, the length-diameter ratio is 20-400, and thus, the calcium sulfate nanowires can satisfy the market demands.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a method for preparing calcium sulfate nanowires with high aspect ratio under low temperature conditions, and belongs to the technical field of preparation and modification of calcium sulfate nanowires. Background technique

[0002] Calcium sulfate whiskers, also known as gypsum whiskers, are fibrous single crystals with complete shape, uniform cross-section, and perfect internal structure. The calcium sulfate whiskers prepared at present are usually micron-sized, with a diameter of 1-10 μm and a length of several Ten microns to hundreds of microns, can be used in environmental engineering, asphalt modification, coatings, fillers, etc., with a wide range of applications.

[0003] According to the dimensions, nano calcium sulfate can be divided into: calcium sulfate nanoparticles, calcium sulfate nanosheets, calcium sulfate nanorods, calcium sulfate nanotubes, calcium sulfate nanowires, calcium sulfate nanobeams, etc. Calcium s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More