Treatment method for aluminum metal surface and aluminum metal shell

A treatment method, aluminum metal technology, applied in the direction of surface reaction electrolytic coating, coating, electrolytic coating, etc., can solve the problems of high surface roughness, complicated process steps, uneven nanopore size, etc., and achieve high quality and process Simple steps, good gloss effect

Inactive Publication Date: 2017-06-09
AAC TECH PTE LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a method for treating the surface of aluminum metal and an aluminum metal shell, which effectively solve the problems of uneven nanopore size, high surface roughness, Technical issues with complex process steps

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method for aluminum metal surface and aluminum metal shell
  • Treatment method for aluminum metal surface and aluminum metal shell
  • Treatment method for aluminum metal surface and aluminum metal shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0033] see figure 1 , figure 1 It is a process flow chart of the treatment method for aluminum metal surface of the present invention. The invention provides a method for treating the surface of aluminum metal. The aluminum metal used in the treatment method includes extruded aluminum and die-cast aluminum, and the extruded aluminum is selected from: aluminum 1050, aluminum 5052, aluminum 6061, aluminum 6063, aluminum 7003 and aluminum 7075 ; The die-casting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a novel aluminum metal surface treatment method and an aluminum metal shell. The treatment method adopts the steps of degreasing, alkali etching, ash removal, anodic oxidation and N treatment to treat the aluminum metal surface. In the step, using N1 agent, N2 agent, N3 agent, N4 agent and N5 agent in order to perform N treatment on the surface of the aluminum metal that has been anodized, the aluminum metal shell includes an aluminum base, and is arranged on the aluminum The barrier layer on the surface of the substrate and the oxide film layer arranged on the surface of the barrier layer, the oxide film layer contains nanopores. Compared with the related art, the aluminum metal surface treated by the aluminum metal surface treatment method provided by the present invention has uniform nanopore size, good gloss, high-quality oxide film, and simple process steps.

Description

[0001] 【Technical field】 [0002] The invention relates to the technical field of metal surface treatment, in particular to an aluminum metal surface treatment method and an aluminum metal shell. [0003] 【Background technique】 [0004] In the fields of automobiles, household electrical appliances, industrial machinery, etc., it is necessary to firmly combine metal and resin. At present, the common technology uses adhesives to function at room temperature or under heating to integrate metal and synthetic resin. . Directly integrating high-strength engineering resins with ferroalloys such as magnesium, aluminum alloys, and stainless steel without adhesives has become a research direction. [0005] Nano Machining Technology (NMT) is the integrated combination technology of metal and plastic. By nano-processing the surface of aluminum metal, plastic can be directly injection-molded on the surface of aluminum metal, so as to obtain metal-plastic integrated molding products. For t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D11/08C25D11/16C25D11/24C23G1/22C23F1/36C23G1/12
CPCC25D11/08C23F1/36C23G1/125C23G1/22C25D11/16C25D11/24
Inventor 郑明峰严绪东陈南南韩启超
Owner AAC TECH PTE LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com