Structural steel welding rod and method for preparing same

A technology for structural steel and welding rods, applied in welding equipment, welding media, manufacturing tools, etc., can solve the problems of difficult removal of weld slag, difficulty in secondary arc ignition, small spark spatter, etc., and achieve good secondary arc ignition , The production is simple and convenient, and the effect of small spark splash

Active Publication Date: 2017-06-13
石家庄旭家焊接材料有限公司
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a structural steel welding rod and its preparation method, aiming to solve the problems in the prior art that the smoke is relatively large, the sparks are large, the secondary arc ignition is difficult, the weld slag is difficult to remove, the operation is complicated, and the work is difficult. The problem of low efficiency has the characteristics of less smoke, less spark spatter, beautiful welding seam, high finish, good secondary arc ignition, good connection performance between coating and welding core, and easy slag removal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Structural steel welding rod and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0025] Further, as a specific embodiment of the structural steel welding rod provided by the present invention, the diameter of the welding core is 2-4mm.

[0026] Furthermore, as a specific embodiment of the structural steel electrode provided by the present invention, the ratio of the thickness of the coating to the diameter of the welding core is 0.2-0.25.

[0027] Further, the structural steel is carbon steel. The carbon steel used in this welding core is H08A.

[0028] The present invention also provides the preparation method of above-mentioned structural steel welding rod, and its concrete process method step is:

[0029] Milling steps: mix 5-35 parts of titanium dioxide, 20-27 parts of reduced titanium, 7-8.5 parts of medium manganese, 7-10 parts of white mud, 5 parts of mica, 3 parts of white clay, and 2-2 parts of feldspar according to the weight ratio. 4 parts, 7-8.5 parts of marble, 0-2 parts of wood powder, 1-3 parts of cellulose, 0-30 parts of rutile, 0-5 parts...

Embodiment 1

[0040]The structural steel electrode includes a welding core and a coating wrapped on the welding core. According to the proportion by weight, the components of the coating include: 5-35 parts of titanium dioxide, 20-27 parts of reduced titanium, 7 parts of medium manganese -8.5 parts, white mud 7-10 parts, mica 5 parts, clay 3 parts, feldspar 2-4 parts, marble 7-8.5 parts, wood powder 0-2 parts, cellulose 1-3 parts, rutile 0-30 parts parts, 0-5 parts of illite; made by adding binder wet mixing, pressure coating and drying steps; made by adding binder wet mixing mixing, pressure coating and drying steps. The diameter of the welding core is 2-4mm; the ratio of the thickness of the coating to the diameter of the welding core is 0.2-0.25; the structural steel is carbon steel. The carbon steel used in this welding core is H08A.

[0041] The preparation method of structural steel welding rod, its specific process method steps are:

[0042] Milling steps: mix 5-35 parts of titaniu...

Embodiment 2

[0047] The structural steel electrode includes a welding core and a coating wrapped on the welding core. The components of the coating are: 35 parts of titanium dioxide, 25 parts of reduced titanium, 7 parts of medium manganese, 10 parts of white clay, and 5 parts of mica , 3 parts of clay, 4 parts of feldspar, 8 parts of marble, 2 parts of wood flour, and 1 part of cellulose; made by wet mixing, pressure coating, and drying by adding adhesive; wet mixing by adding adhesive , pressure coating and drying steps. The diameter of the welding core is 2-4mm; the ratio of the thickness of the coating to the diameter of the welding core is 0.2-0.25; the structural steel is carbon steel. The carbon steel used in this welding core is H08A.

[0048] The preparation method of structural steel welding rod, its specific process method steps are:

[0049] Milling steps: mix 35 parts of titanium dioxide, 25 parts of reduced titanium, 7 parts of medium manganese, 10 parts of white clay, 5 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Granularityaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a structural steel welding rod and a method for preparing the same. The structural steel welding rod comprises welding cores and coating. The coating wraps the welding cores. The coating comprises, by weight, 5-35 parts of titanium dioxide powder, 20-27 parts of reduction titanium, 7-8.5 parts of medium manganese, 7-10 parts of lime mud, 5 parts of mica, 3 parts of argil, 2-4 parts of feldspar, 7-8.5 parts of marble, 0-2 parts of wood meal, 1-3 parts of celluloses, 0-30 parts of rutile and 0-5 parts of illite. The method includes steps of adhesive adding and wet mixing, press coating and drying. The diameters of the welding cores are 2-4 mm. The structural steel welding rod and the method have the advantages that processes for manufacturing the structural steel welding rod are simple, the coating and the welding cores are good in connection performance, the structural steel welding rod generates little smoke and is low in spark splashing during use, and welded joints are attractive and are high in smooth finish; the structural steel welding rod is good in secondary arc strike property and is environmentally friendly and safe during use, slag is easy to remove, and the work efficiency can be greatly improved.

Description

technical field [0001] The invention belongs to the technical field of welding materials, and more specifically relates to a structural steel welding rod and a preparation method for making the welding rod. Background technique [0002] The welding rod is a metal strip that is melted and filled at the joint of the welding workpiece during gas welding or electric welding. It consists of two parts, the coating and the welding core. Relying on the melting of the coating and adding it to the weld as a filler metal, it becomes the main component of the weld metal. Now some welding rods have a lot of smoke and sparks during use, and they emit more pollutants, causing environmental pollution. It is difficult to strike the arc twice at the weld seam, and it is difficult to remove the weld slag. It needs to be removed by knocking. The operation is complicated, which is a waste of time and results in low work efficiency. Contents of the invention [0003] The purpose of the presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/32B23K35/365B23K35/40B23K35/12
CPCB23K35/0266B23K35/325B23K35/3601B23K35/365B23K35/404
Inventor 许晓强许嘉强许宪斌
Owner 石家庄旭家焊接材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap