Low-silicon titanium-containing acid pickling board with yield strength being in 500MPa grade and preparation method thereof
A technology of yield strength and pickling plate, which is applied in the field of pickling plate and its preparation, can solve problems such as roll pitting, affecting the surface quality of strip steel, and increasing rolling force, so as to achieve good processing performance, improve Ti utilization rate, The effect of grain refinement
Active Publication Date: 2017-06-13
MAGANG (GROUP) HOLDING CO LTD +1
View PDF3 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In the hot rolling process, due to the recrystallization inhibitory effect of Nb, the rolling force of this steel type rises rapidly during the rolling process, and the damage to the roll is more obvious, resulting in pitting of the roll and affecting the strip after pickling. Surface Quality
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0026] The present invention will be described in detail below in conjunction with accompanying drawing and embodiment
[0027] A low-silicon titanium-containing pickling plate with a yield strength of 460MPa, the chemical composition and weight percentage are: C 0.06-0.09%, Mn 0.35-0.80%, Als 0.03-0.06%, Ti 0.07-0.09%, Si≤0.05% , Nb≤0.01%, S≤0.008%, P≤0.015%, N≤0.004%, O≤0.003%, and the rest are iron and unavoidable impurities.
[0028] Prepared by the following steps:
[0029] Converter smelting - ladle blowing argon - LF furnace refining - RH vacuum treatment - continuous casting - hot continuous rolling - laminar cooling - coiling - into the continuous pickling line for pickling.
[0030]Among them, in the hot continuous rolling step, the exit temperature of the heating furnace is 1220-1250°C, and the soaking time is not less than 40 minutes; the finishing temperature of rough rolling is 1082-1095°C; The final rolling temperature is 840-900°C; the rough rolling is rolled...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a low-silicon titanium-containing acid pickling board with yield strength being in a 500MPa grade and a preparation method thereof. The acid pickling board comprises the following chemical ingredients by weight percentage: 0.06-0.09% of C, 0.35-0.80% of Mn, 0.03-0.06% of Als, 0.07-0.09% of Ti, less than or equal to 0.05% of Si, less than or equal to 0.01% of Nb, less than or equal to 0.008% of S, less than or equal to 0.015% of P, less than or equal to 0.004% of N, less than or equal to 0.003% of N and the balance of iron and unavoidable impurities. The acid pickling board is prepared by the following steps: converter melting, ladle argon stirring, LF refining, RH vacuum treatment, continuous casting, hot continuous rolling, laminar cooling, reeling and acid pickling in a continuous acid pickling line. According to the acid pickling board, the form of organization comprises ferrite, a small amount of carbide and a small amount of pearlites, the grain size number is 11-12 grade, the yield strength is 535-550MPa, and the tensile strength is 625-645MPa, the ductility is 22-25%, the band steel face quality is in a grade more than FB (02), and the processability is good.
Description
technical field [0001] The invention relates to a pickling board and a preparation method thereof, in particular to a low-silicon titanium-containing pickling board with a yield strength of 500 MPa and a preparation method thereof. Background technique [0002] High-strength low-alloy automotive structural steels are generally designed with Nb microalloys and appropriate addition of Si components. In the hot rolling process, due to the recrystallization inhibitory effect of Nb, the rolling force of this steel type rises rapidly during the rolling process, and the damage to the roll is more obvious, resulting in pitting of the roll and affecting the strip after pickling. Surface Quality. The addition of Si element increases the viscosity of iron oxide scale on the surface of strip steel, which is difficult to remove, and longitudinal oxygen-compressed stripes appear along the rolling direction. Contents of the invention [0003] In order to solve the above-mentioned techn...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More IPC IPC(8): C22C38/04C22C38/06C22C38/14C22C38/02C22C38/12C21D8/02
CPCC21D8/0226C21D2211/005C21D2211/009C22C38/001C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14