Method of preparing anti-wearing and anti-corrosion coating on surface of ejection roller table of continuous casting machine

A technology of continuous casting machine and roller table, which is applied in the direction of coating, metal material coating process, etc., can solve the lack of research on the laser cladding process of the billet roller table of the continuous casting machine, and achieve small deformation, compact structure, The effect of low dilution

Active Publication Date: 2017-06-16
SHENYANG DALU LASER TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, there is still a lack of research on the laser cladding process for the billet roller table of the continuous casting machine

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The billet roller table of the continuous casting machine is made of No. 45 steel.

[0027] The method for preparing a wear-resistant and corrosion-resistant coating on the surface of a billet discharge roller table of a continuous casting machine includes the following process.

[0028] 1) Surface pretreatment of billet roller table of continuous casting machine.

[0029] Derust and degrease the surface of the continuous casting machine at room temperature, and use alcohol to clean the surface of the roller table to prevent the presence of pollutants at the interface and affect the quality of the interface between the laser cladding layer and the substrate. It is also inspected by coloring flaw detection method, and the surface is required to be free of pores, inclusions, cracks and other defects.

[0030] 2) Design and preparation of alloy powder.

[0031] The nickel-based alloy powder with good corrosion resistance and wear resistance is selected, and the material ...

Embodiment 2

[0042] The billet roller table of the continuous casting machine is made of No. 45 steel.

[0043] The method for preparing a wear-resistant and corrosion-resistant coating on the surface of a billet discharge roller table of a continuous casting machine includes the following process.

[0044] 1) Surface pretreatment of billet roller table of continuous casting machine.

[0045] Derust and degrease the surface of the continuous casting machine at room temperature, and use alcohol to clean the surface of the roller table to prevent the presence of pollutants at the interface and affect the quality of the interface between the laser cladding layer and the substrate. It is also inspected by coloring flaw detection method, and the surface is required to be free of pores, inclusions, cracks and other defects.

[0046] 2) Design and preparation of alloy powder.

[0047] The nickel-based alloy powder with good corrosion resistance and wear resistance is selected, and the material ...

Embodiment 3

[0058] The billet roller table of the continuous casting machine is made of No. 45 steel.

[0059] The method for preparing a wear-resistant and corrosion-resistant coating on the surface of a billet discharge roller table of a continuous casting machine includes the following process.

[0060] 1) Surface pretreatment of billet roller table of continuous casting machine.

[0061] Derust and degrease the surface of the continuous casting machine at room temperature, and use alcohol to clean the surface of the roller table to prevent the presence of pollutants at the interface and affect the quality of the interface between the laser cladding layer and the substrate. It is also inspected by coloring flaw detection method, and the surface is required to be free of pores, inclusions, cracks and other defects.

[0062] 2) Design and preparation of alloy powder.

[0063] The nickel-based alloy powder with good corrosion resistance and wear resistance is selected, and the material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method of preparing an anti-wearing and anti-corrosion coating on the surface of an ejection roller table of a continuous casting machine. The method comprises the steps of: (1) pretreatment on the surface of the ejection roller table of the continuous casting machine: at room temperature, derusting and deoiling the surface of the ejection roller table of the continuous casting machine and cleaning the surface of the ejection roller table with alcohol; (2) design and preparation of alloy powder: selecting nickel-based alloy powder having good anti-wearing and anti-corrosion performance; and (3) preparation of a laser cladding layer: directly feeding alloy powder into a weld pool in a gravitational synchronic delivery manner with a DL-HL-T5000 type CO2 gas laser device to perform laser cladding to the surface of the ejection roller table of the continuous casting machine, powder thickness after cladding being 1.0-1.5 mm. The ejection roller table of the continuous casting machine is improved in anti-wearing and anti-corrosion performances by more than six times than a new product in the same type, while the cost is only about 50% of the new product.

Description

technical field [0001] The invention relates to a method for preparing a wear-resistant and corrosion-resistant coating on the surface of a metallurgical component, in particular to a method for preparing a wear-resistant and corrosion-resistant coating on the surface of a billet discharge roller table of a continuous casting machine by using laser cladding technology. Background technique [0002] During the service process of some large-scale key equipment parts in my country's metallurgy, petrochemical and national defense industries, most of them are only due to surface damage caused by mechanical wear or corrosion, which seriously affects the safe, stable and efficient operation of production and equipment, and even directly leads to The scrapping of parts and even the whole equipment not only causes serious economic losses, but also causes a huge waste of materials. Surface repair technology can not only improve economic benefits, but also save a lot of raw materials an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C24/10C22C19/05C22C30/00B22D11/128
CPCB22D11/1287C22C19/056C22C19/057C22C30/00C23C24/103
Inventor 陈海涛张冬雪朴新欣
Owner SHENYANG DALU LASER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com