Preparation method of automobile pipe rubber material

A technology for rubber materials and automobile pipelines, applied in the direction of hoses, pipes, mechanical equipment, etc., can solve the problems of unqualified hardness change performance, unqualified tensile stress performance, unqualified tensile strength performance, etc. Diesel performance, effect of improving heat resistance

Active Publication Date: 2017-06-23
宁波市天普橡胶科技股份有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Conclusion: 1.1, 1.4 hardness, 100% modulus stress performance in the first initial state item is unqualified, 2.1 hardness change performance in the 2nd hot air aging resistance item is unqualified, 3.2 tensile strength performance in the 3rd diesel resistance item Unqualified; therefore, there are problems and deficiencies in the prior art that are difficult to meet the TL52361 automobile water pipe standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of automobile pipe rubber material
  • Preparation method of automobile pipe rubber material
  • Preparation method of automobile pipe rubber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0028] Product name: Rubber material for automobile pipes used to make automobile water pipe rubber products that meet the TL52361 standard

[0029] Formula: formula unit is percentage by weight;

[0030] Rubber raw materials: EPDM rubber, 20.78%; oil-extended EPDM rubber, 24.24%;

[0031] Reinforcing agent: quick press furnace black, 16.28%; lamp smoke carbon black, 23.55%;

[0032] Plasticizer: paraffin oil, 7.62%;

[0033] Active agent: highly active magnesium oxide, 1.73%; polyethylene glycol, 0.69%;

[0034] Vulcanizing agent: sulfur, 0.08%; bis-tert-butylperoxycumene, 2.43%;

[0035] N, N'-m-phenylene bismaleimide, 0.87%; trifunctional acrylate, 1.04%;

[0036] Antiaging agent: 4,4'-bis(a,a dimethylbenzyl) diphenylamine, 0.69%;

[0037] preparation:

[0038] Preparation conditions, equipment

[0039] Ambient air pressure: one atmosphere;

[0040] Ambient temperature: room temperature;

[0041] Preparation equipment: open rubber mixer, pressurized internal mixer;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an automobile pipe rubber material. The invention adopts a following formula and a following preparation process. In the formula, ethylene-propylene-diene monomer rubber and oil-filled ethylene-propylene-diene monomer rubber are combined as a main raw material to improve the diesel resistance; bis(tert-butyldioxyisopropyl)benzene, N, N'-m-phenylenedimaleimide and trifunctional acrylate are combined as a vulcanizing agent to improve the heat resistance; 4, 4'-bis(a, a dimethyl benzyl)diphenylamine is used as an anti-aging agent to improve the heat resistance; high-flash point paraffin oil is used as a plasticizer to improve the heat resistance. According to the technical solution, through matching with the corresponding preparation process, automobile rubber water pipe products produced from the prepared rubber material meet requirements of TL52361 automobile water pipe standards.

Description

technical field [0001] The invention relates to a method for preparing a rubber material, in particular to a method for preparing an automobile pipeline rubber material used to manufacture automobile water pipe rubber products conforming to the TL52361 standard. Background technique [0002] With the development of the automobile industry, the standard requirements for auto parts are also constantly improving. The automobile water pipe standard TL52361-2016-11 is the latest standard, referred to as the TL 52361 standard; the rubber products of the automobile water pipe are required to have high temperature resistance, low temperature resistance, and oil resistance. Performance, and meet the requirements of the TL 52361 standard and the ELV directive; the existing technology uses EPDM materials to make rubber products for automotive water pipes, which is difficult to meet the requirements of the TL52361 standard, as follows: [0003] Standard specification for test data of ru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L91/06C08L71/02C08K13/02C08K3/04C08K3/22C08K3/06C08K5/14C08K5/18C08K5/3415F16L11/04
CPCC08L23/16C08L2201/08C08L2203/18C08L2205/025C08L2205/035F16L11/04C08L91/06C08L71/02C08K13/02C08K3/04C08K2003/222C08K3/06C08K5/14C08K5/18C08K5/3415
Inventor 尤建义
Owner 宁波市天普橡胶科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com