Conductive material for high-power motor and production method thereof

A conductive material and high-power technology, which is applied in the field of conductive copper alloy materials for high-power motors and its production, can solve the problems that cannot fully meet the requirements of high-power traction motors, affect the service life of the motor, and be brittle at medium temperature tempering, and achieve cost reduction. Effects of low, high softening temperature and high softening temperature

Active Publication Date: 2017-06-30
浙江力博实业股份有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under high temperature conditions, copper chromium zirconium materials are prone to temper brittleness at medium temperature, which affects the service life of the motor
However, the strength of H90Cr material under high temperature and low temperature conditions is insufficient, and cannot fully meet the requirements of high-power traction motors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be further described below in conjunction with specific examples, but the protection scope of the present invention is not limited thereto.

[0017] A conductive material for a high-power motor provided by the present invention is composed of the following components by weight percentage: copper, cadmium, zirconium, silver, zinc, titanium, phosphorus;

[0018] The cadmium 0.30%, zirconium 0.10%, silver 0.10%, zinc 0.20%, titanium 0.10%, phosphorus 0.02%;

[0019] The impurity content is not more than 0.005%, the oxygen content is not more than 3ppm, and the sum of zirconium, silver, zinc, titanium and phosphorus is less than 1%;

[0020] The production method of the conductive material for high-power motors includes the following steps: batching, vacuum smelting, hot extrusion, solid solution, cold working and graded aging. The softening temperature of the prepared conductive materials for high-power motors is greater than 580 ° C. At ℃, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a conductive material for high-power motor and a production method thereof. The material contains such chemical components as 0.10-0.9% of cadmium, 0.02-0.30% of zirconium, 0.10-0.30% of silver, 0.10-0.50% of zinc, 0.10-0.20% of titanium, and 0.02-0.05% of phosphorus, and not greater than 0.005% of impurities, and not greater than 3 ppm of oxygen, wherein the sum of the zirconium, silver, zinc, titanium, and phosphorus is not greater than 1%. The material in the present invention has the characteristics of high strength, high electrical conductivity, and the like.The softening temperature of the material is higher than 550 DEG C. At 360 DEG C, the material has the tensile strength of greater than 400 MPa and the elongation of greater than 15%, thus meeting the requirements of use for a high-power motor.

Description

technical field [0001] The invention relates to a conductive material and a production method thereof, in particular to a conductive copper alloy material for a high-power motor and a production method thereof. Background technique [0002] High-performance copper alloy is a new type of structural functional material widely used in the fields of electronic information technology, electrical power technology, communication technology, transportation, aerospace, and major national defense equipment. Conductivity is the most important characteristic of copper and copper alloys, which determines the high cost performance of copper and copper alloy materials. Therefore, it has become the most widely used type of metal materials for conductive purposes, among which conductive copper alloy profile products for high-power motors occupy an important position in this type of material, and are widely used in various motors in the transportation industry. In recent years, my country's ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/04C22C9/00C22C1/02C22F1/08
CPCC22C1/02C22C9/00C22C9/04C22F1/08
Inventor 徐高磊
Owner 浙江力博实业股份有限公司