Sweat-absorbing-and-deodorizing slippers and preparing technology thereof

A deodorant and slipper technology, which is applied to footwear, insoles, uppers, etc., can solve the problems of not being able to effectively guarantee the personal safety of users, lack of automated assembly lines, and affect the quality of wearing, and improve the duration of action and the efficiency of adsorption and deodorization , Excellent sweat absorption, antibacterial effect

Inactive Publication Date: 2017-08-18
安徽爱舍家居制品有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the disposable slippers used are mainly based on cost considerations, so the material selection is relatively cheap. From a structural point of view, it basically includes the bottom layer (foam bottom) of the slipper shoe and the upper non-woven fabric layer and non-woven upper. The way of hand-locked cloth strips is stitched together. At present, there is no automatic assembly line production.
Moreover, the above-mentioned disposable slippers have poor anti-slip effect when used in the bathroom, are easy to slip and fall, and cannot effectively protect the personal safety of users, so there is a demand for disposable slippers to increase the functional layer of the bottom surface
In addition, people are prone to foot sweat in the process of wearing, especially in summer, the peculiar smell is relatively strong, and bacteria are easy to breed, which seriously affects the quality of wearing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The plastic shoe body includes the following mass fraction components: 85 parts of polyurethane resin, 15 parts of nano-diatomaceous earth, 4 parts of nano-titanium dioxide, 0.5 part of hydrazine, 4 parts of microcrystalline cellulose, 3 parts of silane coupling agent, emulsifier 1.2 parts, 4 parts of methyl vinyl silicone oil, 20 parts of pigment.

[0022] The steps for preparing the plastic shoe body are as follows:

[0023] 1) Blend nano-titanium dioxide and nano-diatomaceous earth, then add distilled water twice the total mass of the two, then add hydrazine and microcrystalline cellulose, shake at 50°C for 60 minutes, freeze-dry, and grind to a granular If the diameter is less than 30nm, get the powder for later use;

[0024] 2) Add polyurethane resin and powder into the mixer, stir and mix for 20 minutes, then add silane coupling agent and methyl vinyl silicone oil, raise the temperature to 80°C, and stir and mix in a nitrogen atmosphere of 0.2L / min 10min, get th...

Embodiment 2

[0029] The plastic shoe body includes the following mass fraction components: 80 parts of polyurethane resin, 25 parts of nano-diatomaceous earth, 5 parts of nano-titanium dioxide, 1.5 parts of hydrazine, 3 parts of microcrystalline cellulose, 2 parts of silane coupling agent, emulsifier 1.5 parts, 3 parts of methyl vinyl silicone oil, 25 parts of pigment.

[0030] The steps for preparing the plastic shoe body are as follows:

[0031] 1) Blend nano-titanium dioxide and nano-diatomaceous earth, then add distilled water 3 times the total mass of the two, then add hydrazine and microcrystalline cellulose, shake at 50°C for 70 minutes, freeze-dry, and grind to granules If the diameter is less than 30nm, get the powder for later use;

[0032] 2) Add polyurethane resin and powder into the mixer, stir and mix for 25 minutes, then add silane coupling agent and methyl vinyl silicone oil, raise the temperature to 80°C, and stir and mix in a nitrogen atmosphere of 0.3L / min 15min, get t...

Embodiment 3

[0037] The plastic shoe body includes the following mass fraction components: 86 parts of polyurethane resin, 30 parts of nano-diatomaceous earth, 1 part of nano-titanium dioxide, 1.5 parts of hydrazine, 2 parts of microcrystalline cellulose, 1 part of silane coupling agent, emulsifier 1 part, 2 parts of methyl vinyl silicone oil, 35 parts of pigment.

[0038] The steps for preparing the plastic shoe body are as follows:

[0039] 1) Blend nano-titanium dioxide and nano-diatomaceous earth, then add distilled water twice the total mass of the two to it, then add hydrazine and microcrystalline cellulose, shake at 50°C for 80 minutes, freeze-dry, and grind to granules If the diameter is less than 30nm, get the powder for later use;

[0040] 2) Add polyurethane resin and powder into the mixer, stir and mix for 25 minutes, then add silane coupling agent and methyl vinyl silicone oil, raise the temperature to 80°C, and stir and mix in a nitrogen atmosphere of 0.25L / min 15min, get t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention proposes a sweat-absorbing and deodorant slippers and a preparation process thereof, comprising a plastic shoe body and a fiber lining, the plastic shoe body including a sole and a vamp, the upper surface of the sole and the lower surface of the vamp are fitted by Velcro. There is the fiber lining, the plastic shoe body is made of modified polyurethane material, and the fiber lining is modified blended fiber cloth. The slipper of the present invention adopts a two-layer structure, and the plastic shoe body and the fiber lining can be connected by Velcro. Tear and fit, easy to clean and replace. Compared with disposable slippers, it is safe and environmentally friendly, and can effectively reduce costs. In addition, the plastic shoe body made through a reasonable formula combination is comfortable, soft, strong and tough, antibacterial and wear-resistant, and with fiber The lining absorbs sweat, deodorizes, sterilizes, and has good air permeability, which improves the overall quality.

Description

technical field [0001] The invention relates to the technical field of slippers preparation, in particular to sweat-absorbing and deodorant slippers and a preparation process thereof. Background technique [0002] At present, the disposable slippers used are mainly based on cost considerations, so the material selection is relatively cheap. From a structural point of view, it basically includes the bottom layer (foam bottom) of the slipper shoe and the upper non-woven fabric layer and non-woven upper. The way of hand-locking cloth strips and stitching together, as far as it is concerned, there is no automatic assembly line production. Moreover, the above-mentioned disposable slippers have poor anti-slip effect when used in the bathroom, are prone to slipping, and cannot effectively protect the personal safety of users. Therefore, there is a demand for disposable slippers to increase the functional layer of the bottom surface. In addition, people tend to produce foot sweat i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A43B3/10A43B1/10A43B17/00A43B17/18A43B23/07B29D35/12C08L75/04C08L1/04C08L83/07C08K13/06C08K9/00C08K3/22C08K3/36
CPCA43B3/101A43B1/10A43B3/107A43B17/003A43B17/18A43B23/07B29D35/122B29D35/126C08K2003/2241C08K2201/011C08L75/04C08L2205/03C08L1/04C08L83/04C08K13/06C08K9/00C08K3/22C08K3/36
Inventor 刘大涛张明海佘芳芳
Owner 安徽爱舍家居制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com