Method for moisturizing and anti-warping of paraffin milk of plant fiberboard

A plant fiber board and paraffin emulsion technology, which is applied in the field of plant fiber production technology, can solve the problems of short pressure holding time, residual molecular stress, and product warping easily, so as to eliminate internal stress, solve warping deformation, and effectively good effect

Inactive Publication Date: 2017-08-22
XIAMEN HUSKS NEW MATERIAL TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main base material of the plant fiber products made by the above two patents is plant fiber, and the product contains a certain amount of starch components. And the molecular weight of starch fails to fully release the molecular chain conformational energy, a large amount of molecular stress remains, and the product is prone to warping

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] S1. Put 40g of gum arabic powder in a dry mortar and grind it evenly; then add 120g of liquid paraffin and continue grinding to make it evenly mixed; then add 80g of distilled water, and grind in the same direction quickly until you hear crackling sound and thick milky white colostrum Add 70g of distilled water for the second time, and continue to grind evenly to obtain paraffin milk.

[0019] S2. Put 310g of paraffin milk and 15.5Kg of rice husk fiber synthetic resin powder in a high-speed ball mill and mix evenly to obtain a mixed material.

[0020] S3. Start the high-temperature molding machine, heat the mold temperature to 170° C., adjust the pressure to 22 MPa, and then inject the mixed material into the mold for compression molding to obtain a cutting board.

[0021] S4. Quickly put the demolded cutting board into an oven preheated to 170°C and press it with a marble plate preheated to 170°C to shape the shape, continue heating until the oven temperature reaches 1...

Embodiment 2

[0023] S1. Put 30g of gum arabic powder in a dry mortar and grind it evenly; then add 120g of liquid paraffin and continue grinding to make it evenly mixed; then add 80g of distilled water, and quickly grind in the same direction until you hear crackling sound and thick milky white colostrum Add 70g of distilled water for the second time, and continue to grind evenly to obtain paraffin milk.

[0024] S2. Put 300g of paraffin milk and 10Kg of plant fiber synthetic resin powder in a high-speed ball mill and mix evenly to obtain a mixed material.

[0025] S3. Start the high-temperature molding machine, heat the mold temperature to 200° C., adjust the pressure to 21 MPa, and then inject the mixed material into the mold for compression molding to obtain chopsticks.

[0026] S4. Put the chopsticks out of the mold into an oven preheated to 200°C quickly and press them with a marble plate preheated to 200°C to shape the shape. Continue heating until the oven temperature reaches 200°C,...

Embodiment 3

[0028] S1. Put 50g of gum arabic powder in a dry mortar and grind it evenly; then add 110g of liquid paraffin and continue grinding to make it evenly mixed; then add 80g of distilled water and grind in the same direction quickly until you hear crackling sound and thick milky white colostrum until; add 70g of distilled water again, and continue to grind evenly to obtain paraffin milk.

[0029] S2. Put 310g of paraffin emulsion and 6.2Kg of rice husk fiber synthetic resin powder in a high-speed ball mill and mix evenly to obtain a mixed material.

[0030] S3. Start the high-temperature molding machine, heat the mold temperature to 180° C., adjust the pressure to 26 MPa, and then inject the mixed material into the mold for compression molding to obtain a cutting board.

[0031] S4. After demolding, the chopping board is quickly put into an oven preheated to 180°C and pressed to shape with a marble plate preheated to 180°C. Continue heating until the oven temperature reaches 180°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for moisturizing and anti-warping of paraffin milk of a plant fiberboard. The method comprises the following steps: placing gum acacia powder in a dry container, uniformly grinding, then adding liquid paraffin, grinding to be mixed uniformly, then adding distilled water, and grinding uniformly to obtain the paraffin milk; placing the paraffin milk and a plant fiber material in a high-speed ball mill, mixing uniformly, obtaining a mixed material; placing the mixed material in a high-temperature mould pressing machine, pressing and molding, and finally demolding and cooling to room temperature to obtain the plant fiberboard, wherein the plant fiber material is rice husk fiber synthetic resin powder or plant fiber synthetic resin powder. According to the invention, the gum acacia powder and the liquid paraffin are mixed uniformly and dissolved in the distilled water to prepare a humectant, and are mixed with the plant fiber material uniformly to obtain a product by pressing and molding. The humectant can lock the easy-to-lose water and prevent a molecular chain from being deformed, the steps are simple, the design is reasonable, implementation is convenient, and the effect is good.

Description

technical field [0001] The invention relates to a production process of plant fibers, in particular to a method for moisturizing and preventing warping of plant fiber boards with paraffin emulsion. Background technique [0002] The plant fiber products made of rice husk fiber or plant fiber, whose raw materials are all derived from nature, have the characteristics of green and environmental protection. They can be degraded into organic fertilizers in nature and return to nature, so they have broad market prospects. . [0003] The applicant has consistently devoted himself to the development and research of plant fibers, made great progress, and applied for two patents on the research and development results. Patent 1: The patent authorization announcement number is CN102690524B, and the authorization announcement date is 2014.09.10. The patent name is a production process of rice husk fiber synthetic resin powder and rice husk fiber products. Patent 2: The authorized annou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L5/00C08L91/06
CPCC08L97/02C08L2205/03C08L5/00C08L91/06
Inventor 王少会庄展鹏柯婵
Owner XIAMEN HUSKS NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com