Epoxy colored pavement finish paint and preparation and construction process thereof

A construction technology and topcoat technology, applied in epoxy resin coatings, roads, roads, etc., can solve the problems of difficult preparation and construction, toxicity, high cost, and achieve long construction time, good weather resistance, and long-term adhesion. Effect

Inactive Publication Date: 2017-08-22
深圳市威尔地坪材料有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is that traditional pavement coatings have the problems of high cost, toxicity, low yield, and difficulty in preparation and construction. , Epoxy color pavement paint with excellent performance and its preparation and construction technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy colored pavement finish paint and preparation and construction process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The present embodiment provides a kind of epoxy color pavement finish paint, can be used in environments such as the bus rapid transit lane of city, the leisure greenway around the city, the landscape road in the park, the buffer junction road on the expressway, described color epoxy The topcoat is a two-component paint, consisting of component A and component B, the component A is a curing agent, and the curing agent is an isophorone diamine (IPDA) curing agent, described in this embodiment The isophorone diamine curing agent adopts the IPDA epoxy curing agent produced by BASF Co., Ltd., and the mass ratio of the component A to the component B is 4:1.

[0032] The component B consists of the following components in mass percent:

[0033] Epoxy resin 30%, described epoxy resin is the GELR-128 type epoxy resin that Hongchang Electronic Materials Co., Ltd. produces;

[0034] Reactive diluent 10%, described reactive diluent is C12-14 fatty alcohol glycidyl ether produced ...

Embodiment 2

[0049] The present embodiment provides a kind of epoxy color pavement finish paint, can be used in environments such as the bus rapid transit lane of city, the leisure greenway around the city, the landscape road in the park, the buffer junction road on the expressway, described color epoxy The topcoat is a two-component paint, consisting of component A and component B, the component A is a curing agent, and the curing agent is an isophorone diamine (IPDA) curing agent, described in this embodiment The isophorone diamine curing agent adopts the IPDA epoxy curing agent produced by BASF Co., Ltd., and the mass ratio of the component A to the component B is 2:1.

[0050]The component B consists of the following components in mass percent:

[0051] Epoxy resin 50%, described epoxy resin is the NPEL-128 type epoxy resin that South Asia Epoxy Resin Co., Ltd. produces;

[0052] 5% reactive diluent, which is C12-14 fatty alcohol glycidyl ether produced by Hubei Yuancheng Saichuang Te...

Embodiment 3

[0067] The present embodiment provides a kind of epoxy color pavement finish paint, can be used in environments such as the bus rapid transit lane of city, the leisure greenway around the city, the landscape road in the park, the buffer junction road on the expressway, described color epoxy The topcoat is a two-component paint, consisting of component A and component B, the component A is a curing agent, and the curing agent is an isophorone diamine (IPDA) curing agent, described in this embodiment The isophorone diamine curing agent adopts the IPDA epoxy curing agent produced by BASF Co., Ltd., and the mass ratio of the component A to the component B is 6:1.

[0068] The component B consists of the following components in mass percent:

[0069] Epoxy resin 31%, described epoxy resin is the NPEL-128 type epoxy resin that South Asia Epoxy Resin Co., Ltd. produces;

[0070] 6% reactive diluent, which is C12-14 fatty alcohol glycidyl ether produced by Hubei Yuancheng Saichuang T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an epoxy colored pavement finish paint and a preparation and construction process thereof. The epoxy colored pavement finish paint contains components A and B, wherein the component A is a curing agent, and the component B is prepared from, by mass, 30-50% of epoxy resin, 5-10% of reactive diluent, 0.5-2% of anti-settling agent, 1-5% of pigment, 20-40% of quartz powder and 20-40% of coarse whiting. The epoxy colored pavement finish paint is green and environmentally friendly, is free of irritant smell, has reliable and permanent adhesion power with different basal planes, also has good weather resistance and chemical corrosion resistance, is not saponified on alkaline concrete, and has excellent waterproof and dampproof properties, good flexibility, impact resisting property and excellent anti-slip protection property. In addition, the preparation process of the finish paint is simple, the conditions are mild, the construction time is longer than conventional time, construction operation is easy, the requirements for the environment is not strict during construction, and the finish paint is low in cost, economical, practical and suitable for large-area popularization.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to an epoxy colored road surface paint and its preparation and construction process. Background technique [0002] With the continuous development of the national economy and the level of science and technology, people's living standards and consumption levels continue to improve. For the ground of public transportation areas such as urban express bus lanes, leisure greenways on urban roadsides, landscape roads in parks, and highways The requirements for buffer hub roads and so on are getting higher and higher. Not only the ground of these roads needs to meet the comprehensive requirements, but also the construction cost needs to be considered, and the aesthetics after construction should also be considered to improve the overall image of the city. [0003] At present, colored asphalt, acrylic acid, polyurethane and other materials are usually used for constru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/29C09D5/08C09D7/12C09D7/02C08G59/50C08G59/20E01C7/35
CPCC09D163/00C08G59/20C08G59/5026C08K3/346C08K3/36C08K9/04C08K13/06C08K2003/265C09D5/08C09D5/29C09D7/45C09D7/61E01C7/35
Inventor 洪海诗李百科王刚伟刘塊青
Owner 深圳市威尔地坪材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap