Fireproof material for firefighting engineering and preparation method thereof

A fireproof material and engineering technology, applied in the field of fireproof materials, can solve the problems of general thermal insulation performance, general fireproof performance, complex production process, etc., to improve thermal insulation and tensile performance, high tensile and flexural strength, Good leveling effect

Inactive Publication Date: 2017-09-01
合肥博之泰电子科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems that the existing fireproof materials have general fireproof performance, general thermal insulation performance, low tensile strength, high cost and complicated manufacturing process, the purpose of the present invention is to provide a fireproof material and its The preparation method, the prepared fireproof material for fire protection engineering has the advantages of good fireproof performance, good thermal insulation, high tensile strength, low cost and simple manufacturing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A fireproof material for fire engineering, including the following raw materials: 95kg of phenolic resin, 7kg of fly ash, 2kg of silica fume, 1.5kg of magnesium hydroxide, 9kg of glass fiber, 9kg of ceramic fiber, 14kg of polyurethane rubber, attapulgite 15kg of soil, 16kg of expanded vitrified microbeads, 17kg of airgel, 5kg of foaming agent, 4kg of heat stabilizer, 2kg of light stabilizer, 4kg of flame retardant, 3kg of antioxidant and 19kg of curing agent.

[0042] Glass fiber is added to the raw material of the invention, and the glass fiber has the characteristics of high temperature resistance, non-combustibility, corrosion resistance, good sound insulation and high tensile strength, which helps to improve the fireproof and tensile properties of the prepared fireproof material.

[0043] Ceramic fiber is added to the raw material of the present invention, and the ceramic fiber has the characteristics of light weight, high temperature resistance, good thermal stabili...

Embodiment 2

[0061] A fireproof material for fire engineering, including the following raw materials: 80kg of phenolic resin, 5kg of fly ash, 1kg of silica fume, 1kg of magnesium hydroxide, 6kg of glass fiber, 7kg of ceramic fiber, 12kg of polyurethane rubber, attapulgite 13kg, expanded vitrified microbeads 14kg, airgel 15kg, foaming agent 3kg, heat stabilizer 2kg, light stabilizer 1kg, flame retardant 3kg, antioxidant 1kg and curing agent 15kg.

[0062] Glass fiber is added to the raw material of the invention, and the glass fiber has the characteristics of high temperature resistance, non-combustibility, corrosion resistance, good sound insulation and high tensile strength, which helps to improve the fireproof and tensile properties of the prepared fireproof material.

[0063] Ceramic fiber is added to the raw material of the present invention, and the ceramic fiber has the characteristics of light weight, high temperature resistance, good thermal stability, good thermal insulation and hi...

Embodiment 3

[0081] A fireproof material for fire engineering, including the following raw materials: 110kg of phenolic resin, 9kg of fly ash, 3kg of silica fume, 2kg of magnesium hydroxide, 12kg of glass fiber, 11kg of ceramic fiber, 16kg of polyurethane rubber, attapulgite 17kg, expanded vitrified microbeads 18kg, airgel 19kg, foaming agent 7kg, heat stabilizer 6kg, light stabilizer 3kg, flame retardant 5kg, antioxidant 5kg and curing agent 23kg.

[0082] Glass fiber is added to the raw material of the invention, and the glass fiber has the characteristics of high temperature resistance, non-combustibility, corrosion resistance, good sound insulation and high tensile strength, which helps to improve the fireproof and tensile properties of the prepared fireproof material.

[0083] Ceramic fiber is added to the raw material of the present invention, and the ceramic fiber has the characteristics of light weight, high temperature resistance, good thermal stability, good thermal insulation and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a fireproof material for firefighting engineering and a preparation method thereof, and relates to the field of fireproof materials. The fireproof material is prepared from the following raw materials in parts by weight: 80-100 parts of phenolic resin, 5-9 parts of pulverized fuel ash, 1-3 parts of tiny silicone powder, 1-2 parts of magnesium hydroxide, 6-12 parts of glass fibers, 7-11 parts of ceramic fibers, 12-16 parts of polyurethane rubber, 13-17 parts of attapulgite, 14-18 parts of expanded and vitrified small balls, 15-19 parts of aerogel, 3-7 parts of a foaming agent, 2-6 parts of a thermal stabilizing agent, 1-3 parts of a photo-stabilizing agent, 3-5 parts of flame retardant, 1-5 parts of antioxidant and 15-23 parts of a curing agent. The preparation method comprises the following steps: (1) weighing raw materials; (2) preparing a stirring material; (3) preparing a mixture; (4) preparing mixed slurry; and (5) molding in a mold. The fireproof material can be used for solving the problems of common fireproof performance, common temperature insulating and heat isolating performance, low tensile strength, high cost and complicated manufacture cost.

Description

technical field [0001] The invention belongs to the field of fireproof materials, and in particular relates to a fireproof material used in fire engineering and a preparation method thereof. Background technique [0002] With the development of economy and society, people have put forward higher requirements for the functions of buildings, especially the fire protection engineering in buildings. The construction of fire protection engineering is directly related to the life safety of every family resident. In fire protection engineering, nothing plays a key role in fire prevention than fireproof materials, but the existing fireproof materials generally have the general problem of fireproof performance. [0003] When used in buildings with multi-functional and comprehensive performance requirements, the existing fireproof materials should not only have good fireproof performance, but also have the characteristics of good thermal insulation, high tensile strength, low cost and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/06C08L75/04C08K13/04C08K7/14C08K7/04C08K7/28C08K3/34C08K5/098C08K3/04C08K5/17C08J9/08
CPCC08L61/06C08J9/08C08J2203/02C08J2361/06C08J2475/04C08L2201/02C08L2201/08C08L2203/14C08L2205/03C08L75/04C08K13/04C08K7/14C08K7/04C08K7/28C08K3/346C08K5/098C08K3/04C08K5/17
Inventor 王飞
Owner 合肥博之泰电子科技有限公司