Hole sealing agent, hole sealing process and aluminum alloy product

A sealing agent and hole sealing technology, which is applied in the field of aluminum alloy products and sealing agents, can solve the problem that the sealing agent cannot perform secondary sealing, and achieve anti-pollution effects, good anti-fingerprints, anti-pollution self-purification Effect

Inactive Publication Date: 2017-09-05
SHENZHEN MENGZHIFANG COMM PROD
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main purpose of the present invention is to provide a high temperature resistant sealing agent,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hole sealing agent, hole sealing process and aluminum alloy product

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0043] Example 1: The preparation of the sealing agent is as follows: an emulsion is formed by dispersing calcium acetate, barium acetate, lithium silicate, ammonium acetate, titanium acetate, sodium fluorotitanate and sodium dodecylbenzene sulfonate in deionized water. The content of each component in the emulsion is calculated by weight percentage, including: 30% calcium acetate, 8% barium acetate, 5% lithium silicate, 6% ammonium acetate, 9% titanium acetate, 4% sodium fluorotitanate, 1.2% twelve Sodium alkylbenzene sulfonate, the balance is water. The sealing storage time of the above-mentioned sealing agent can reach more than one year.

[0044] Dilute the above plugging agent into a plugging liquid with a concentration of 12g / L for use; adjust the PH value of the plugging liquid to 6.0; heat the plugging liquid to 94°C; immerse the pre-treated aluminum alloy product for 15 minutes . It can make aluminum alloy products get a smooth surface, no powder frost sealing film, in...

Example Embodiment

[0045] Example 2: The composition of the above-mentioned sealing agent is calculated by weight percentage, including: 20% calcium acetate, 15% barium acetate, 8% lithium silicate, 5% ammonium acetate, 12% titanium acetate, 7% sodium fluorotitanate , 1.4% sodium dodecylbenzene sulfonate, other operations are the same as in Example 1. The sealed storage time of the above-mentioned sealing agent can be up to 2 years. In the sealing process, the concentration of the sealing material liquid is 10g / L, the PH value is 5.5; the sealing temperature is 90℃, and the sealing time is 18min, which can make the aluminum alloy product get a smooth surface and no powder frost sealing film.

Example Embodiment

[0046] Example 3: The composition of the above-mentioned sealing agent is calculated by weight percentage, including: 20% calcium acetate, 25% barium acetate, 10% lithium silicate, 8% ammonium acetate, 12% titanium acetate, 9% sodium fluorotitanate , 4% sodium dodecylbenzene sulfonate, other operations are the same as in Example 1. The sealing storage time of the above-mentioned sealing agent can reach more than one year. In the sealing process, the concentration of the sealing material liquid is 14g / L, the PH value is 6.0; the sealing temperature is 97℃, and the sealing time is 10min, which can make the aluminum alloy product obtain a smooth surface and no powder frost sealing film.

[0047] The embodiment of the present invention also provides an aluminum alloy product, and the above-mentioned aluminum alloy product is subjected to the above-mentioned sealing process with the above-mentioned sealing agent. The above-mentioned aluminum alloy products have a smooth surface, no p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hole sealing agent, a hole sealing process and an aluminum alloy product. The hole sealing agent is emulsion formed by dispersing non nickel-containing inorganic salt in water serving as a solvent, and is prepared from 35 to 45 percent of a main alkaline earth metal acetate hole sealing agent, 5 to 10 percent of an alkaline earth metal acetate stabilizer and 15 to 20 percent of a metal acetate promoter. According to the hole sealing agent, by the adoption of the high-content main alkaline earth metal acetate hole sealing agent, high-temperature hole sealing can be supported, high-temperature and quick hole sealing can be realized, the hole sealing time is shortened, the hole sealing reinforcing effect is also enhanced, and the requirement for closing an oxidized film on the surface of a product. Meanwhile, after the high-temperature hole sealing is carried out, the hole sealing effect is better; and moreover, on the basis of a primary hole sealing process, hole sealing operation is carried out for the second time or multiple times, so that other industrial design requirements can be met after the primary hole sealing is completed.

Description

technical field [0001] The invention relates to the field of surface treatment technology, in particular to a sealing agent, a sealing process and an aluminum alloy product. Background technique [0002] The application range of aluminum alloy products is very wide. The daily contact includes door and window profiles, curtain wall profiles, general profiles, industrial profiles, etc., but aluminum alloy products are easily corroded. In order to avoid corrosion of aluminum alloy products, aluminum alloy products are generally treated by anodic oxidation process. Anodizing technology is to form a dense oxide film on the surface of aluminum alloy to isolate the corrosive medium to protect the aluminum base and other surface decorations. The aluminum alloy after anodic oxidation treatment has the advantages of high hardness, insulation, heat insulation and corrosion resistance. However, anodic oxidation will make the surface of the aluminum alloy present a porous layered struc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D11/18
CPCC25D11/18
Inventor 肖佰元李晓杰
Owner SHENZHEN MENGZHIFANG COMM PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap