Lightweight polycarbonate material

A technology of polycarbonate and carbonate, applied in the field of materials, can solve the problems of heavy weight, poor compatibility, and reduce the mechanical properties of finished materials, and achieve the effect of improving dispersion, improving compatibility, and enhancing mechanical properties

Active Publication Date: 2017-09-15
苏州远略知识产权运营有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a lightweight polycarbonate for the problems that the fillers such as magnesium hydroxide and graphene added in the prior art are heavy in weight, have poor compatibility with the polymer matrix, and easily reduce the mechanical properties of the finished material. Material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In parts by weight, each raw material was weighed: 160 parts of trimethylene carbonate monomer, 3 parts of pyromellitic dianhydride, 2 parts of ammonium molybdate, 8 parts of oxidized polyethylene wax, 12 parts of polyether glycol 1 part of vinyl distearic acid amide, 2 parts of calcium acetylacetonate, 13 parts of light filler, 2 parts of trimethylolpropane, 0.4 part of 2-mercaptobenzimidazole, 5 parts of N-methylpyrrolidone , 1 part of sorbitan monooleate, 0.2 part of stannous sulfide, and 20 parts of anhydrous toluene.

[0024] Wherein, the light filler is composed of light calcium carbonate and diatomaceous earth with a weight ratio of 6:1.

[0025] Each raw material that weighs is carried out preparation lightweight polycarbonate material, and specific preparation steps are:

[0026] (1) Take 2-mercaptobenzimidazole, add it to 15 times its weight in absolute ethanol, stir evenly, raise the temperature to 70°C, add trimethylolpropane, keep stirring for 10 minutes, ...

Embodiment 2

[0033] In parts by weight, each raw material was weighed: 140 parts of trimethylene carbonate monomer carbonate, 2 parts of pyromellitic dianhydride, 1 part of ammonium molybdate, 6 parts of oxidized polyethylene wax, 10 parts of polyether glycol 0.8 parts of vinyl distearic acid amide, 1 part of calcium acetylacetonate, 10 parts of light filler, 1 part of trimethylolpropane, 0.4 parts of 2-mercaptobenzimidazole, 3 parts of N-methylpyrrolidone , 0.8 parts of sorbitan monooleate, 0.1 parts of stannous sulfide, and 16 parts of anhydrous toluene.

[0034] The light filler is composed of light calcium carbonate and diatomaceous earth with a weight ratio of 4:1.

[0035] Each raw material that weighs is carried out preparation lightweight polycarbonate material, and specific preparation steps are:

[0036] (1) Take 2-mercaptobenzimidazole, add it to 10 times its weight in absolute ethanol, stir evenly, raise the temperature to 60°C, add trimethylolpropane, keep stirring for 4 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lightweight polycarbonate material, made from, by weight, 140-160 parts of a carbonate monomer, 2-3 parts of pyromellitic dianhydride, 1-2 parts of ammonium molybdate, 6-8 parts of oxidized polyethylene wax, 10-12 parts of polyether glycol, 0.8-1 part of ethylene bis-stearamide, 1-2 parts of calcium acetylacetonate, 10-13 parts of lightweight filler, 1-2 parts of trimethylolpropane, 0.4-1 part of 2-mercaptobenzimidazole, 3-5 parts of N-methylpyrrolidone, 0.8-1 part of sorbitan monooleate, 0.1-0.2 part of stannous sulfide, and 16-20 parts of anhydrous toluene. The lightweight filler is organically modified and is subjected to mixed esterification with acid-doped polyester, the dispersity of the lightweight filler in a polyester matrix is effectively improved, the compatibility of the lightweight filler with other materials is improved, the stability strength of a finished product is improved, and the mechanical properties of the finished product are enhanced.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to a lightweight polycarbonate material. Background technique [0002] The three major application areas of polycarbonate engineering plastics are glass assembly industry, automobile industry and electronics and electrical industry, followed by industrial machinery parts, CDs, packaging, computers and other office equipment, medical and health care, films, leisure and protective equipment, etc. . Polycarbonate can be used as door and window glass, and polycarbonate laminates are widely used in banks, embassies, detention centers and protective windows in public places, for aircraft canopies, lighting equipment, industrial safety baffles and bulletproof glass. Polycarbonate sheets can be used for various signs, such as gasoline pump dials, car dashboards, warehouse and open-air commercial signs, dot-type sliding indicators, polycarbonate resins are used in automotive lighting sy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L23/30C08L71/00C08K13/06C08K9/04C08K3/26C08K7/26C08K5/20C08G64/30
CPCC08G64/30C08K2003/265C08L69/00C08L2205/03C08L23/30C08L71/00C08K13/06C08K9/04C08K9/08C08K3/26C08K7/26C08K5/20
Inventor 胡敏刚张宇
Owner 苏州远略知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com