Method for preparing copper titanate calcium-based ceramic with core-shell structure

A technology of calcium copper titanate and shell structure is applied in the field of preparation of calcium copper titanate-based ceramics, which can solve the problems of low-frequency dielectric constant reduction of CCTO ceramics, and achieve the advantages of reducing dielectric loss, increasing insulation and improving oxidation degree. Effect

Inactive Publication Date: 2017-09-29
TAIYUAN UNIV OF TECH
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problem that the low-frequency dielectric constant of CCTO ceramics is greatly reduced when reducing the low-frequency dielectric loss of CCTO ceramics, the present invention provides a method for preparing copper calcium titanate-based ceramics with a core-shell structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing copper titanate calcium-based ceramic with core-shell structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] To analyze pure calcium nitrate (Ca(NO 3 ) 2 • 4H 2 O, 99%), copper nitrate (Cu(NO 3 ) 2 •3H 2 O, 99%) and tetrabutyl titanate ([CH 3 (CH 2 ) 3 O] 4 Ti, 99%) as the initial raw material, adding citric acid (C 6 h 8 o 7 , 99%), the CCTO precursor powder was prepared by the sol-gel method, first according to the CaCu 3 Ti 4 o 12 The stoichiometric ratio of various raw materials is accurately weighed, then dissolved in ethanol and mixed evenly, and the pH of the solution is only adjusted to 2~3 with nitric acid. After the solution was stirred by magnetic force, it was placed in a constant temperature of 80°C and incubated for 6 hours to make the solution form a colloid, and then kept in a constant temperature of 100°C for 2 hours to become a xerogel. The xerogel was calcined in the atmosphere at 750°C for 2 hours to obtain CCTO powder. Next follow CCTO / xMgTiO 3 (x=0, 0.5, 1 and 2) stoichiometric ratio Accurately weigh CCTO powder, magnesium nitrate (Mg(NO ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing dielectric ceramic materials and in particular relates to a method for preparing a copper titanate calcium-based ceramic with a core-shell structure. The method for preparing the copper titanate calcium-based ceramic with the core-shell structure comprises the following steps: (1) taking calcium nitrate, copper nitrate and tetrabutyl titanate as initial raw materials, adding citric acid, and preparing CCTO powder by utilizing a sol-gel method; (2) accurately weighing the CCTO powder, magnesium nitrate and tetrabutyl titanate according to a stoichiometric ratio of CCTO / xMgTiO3, weighing the citric acid, fully stirring the materials in ethanol, forming suspension, and finally obtaining CCTO / MgTiO3 mixed powder; and (3) fully grinding the powder, pressing into sheets under the pressure of 150 MPa, sintering at the temperature of 1080 DEG C for 10 hours, thereby obtaining the CCTO / xMgTiO3 ceramic.

Description

technical field [0001] The invention relates to a preparation method of dielectric ceramics, in particular to a preparation method of copper calcium titanate-based ceramics with a core-shell structure. Background technique [0002] High dielectric constant materials provide the possibility to realize the miniaturization and high performance of important electronic devices such as filters, resonators, memories and capacitors, and have received extensive attention. Calcium copper titanate (CaCu 3 Ti 4 o 12 , CCTO) is a more typical and representative high-dielectric material discovered in the past few years, whether it is a single crystal or a ceramic, it has a high dielectric strength of up to 10 4 The dielectric constant, the dielectric constant basically remains unchanged in a wide frequency range (10 Hz ~ 100 kHz) and a wide temperature range (100 ~ 350 K). However, while CCTO ceramics have a high low-frequency dielectric constant, their low-frequency dielectric loss i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/465C04B35/628
CPCC04B35/465C04B35/62805C04B35/62886C04B2235/443C04B2235/48
Inventor 郝文涛孙礼杨帅王明文吴辉曹恩思张雍家
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com