A kind of orange-red glaze material with orange peel texture and preparation method thereof

A technology of orange-red and orange-peel, which is applied in the field of orange-red glazed materials with orange-peel texture and its preparation, can solve the problems of demanding raw materials, reduce glaze production costs, enrich glaze varieties, and promote the utilization of mine resources horizontal effect

Active Publication Date: 2020-07-17
NORTHEASTERN UNIV LIAONING
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the theory based on the traditional glaze method has relatively strict requirements on raw materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The natural minerals containing potassium feldspar, manganese carbonate, manganese oxide, calcite, quartz, dolomite, serpentine, muscovite, chlorite and talc are crushed one by one until the particle size is below 200 mesh, and weighed 24g potassium feldspar, 8g manganese carbonate, 8g manganese oxide, 24g calcite, 24g dolomite, 32g quartz, 16g serpentine, 24g muscovite, 40g chlorite and 40g talc powder, mix evenly, add appropriate amount of water and stir to form a slurry Finally, filter to obtain the glaze slurry. After dedusting and moisturizing the surface of the ceramic test piece, spray the glaze slurry evenly on the surface of the ceramic test piece and let it stand for 10 minutes. Place the treated ceramic test piece in an electric kiln, and uniformly raise the temperature from room temperature to 800°C after 300 minutes, and the firing temperature ranges from 800 to 1400°C. After 10 hours, it is naturally cooled to room temperature, and an orange-red colored G...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a glazed material, in particular to an orange-red glazed material with orange peel texture and a preparation method thereof. The technical solution of the present invention is as follows: an orange-red glazed material with orange peel texture, using common mineral materials as raw materials, including: potassium feldspar, manganese carbonate, manganese oxide, calcite, quartz, dolomite, serpentine Stone, muscovite, chlorite and talc, the proportions by weight are: 2-4 parts potassium feldspar, 0.5-2 parts manganese carbonate, 0.5-2 parts manganese oxide, 2-4 parts calcite, 2-4 parts Dolomite, 3‑5 parts quartz, 1‑3 parts serpentine, 2‑4 parts muscovite, 4‑6 parts chlorite and 4‑6 parts talc. The orange-red glazed material with orange peel texture and its preparation method provided by the invention use natural mineral raw materials, promote the utilization level of mine resources, reduce glaze production costs, and enrich glaze varieties.

Description

technical field [0001] The invention relates to a glaze material, in particular to an orange-red glaze material with orange peel texture and a preparation method thereof. Background technique [0002] my country's ceramic industry has a long history and brilliant porcelain culture. The development history of ceramics is an important part of the history of Chinese civilization. As one of the four ancient civilizations, China has made outstanding contributions to the progress and development of human society. Among them, the invention and development of ceramics has unique significance. Different dynasties and dynasties in Chinese history have different artistic styles and different technical characteristics. "china" in English means both China and ceramics, which clearly shows that China is the "hometown of ceramics". As early as more than a thousand years before the Europeans mastered the porcelain manufacturing technology, the Han people had already produced very exquisit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C03C1/06C04B41/86
CPCC03C1/06C03C8/14C04B41/5022C04B41/86C04B41/4543
Inventor 黄菲安佰高王道恒闫莹灿张志彬任亚群孟林
Owner NORTHEASTERN UNIV LIAONING