Rotary furnace cooling agent made of metallurgical waste material product and using method thereof

Abstract

The invention provides a rotary furnace cooling agent and a manufacturing method thereof. The cooling agent is a carbonic and ferreous conglomeration which mainly takes iron scale, carbonic waste material and ferreous waste material as raw materials, and prepared by additionally adding caking agent into the raw materials. The weight percentage of the main chemical compositions of the cooling agent meets the following condition: the carbon content is 5-25%, the content of TFe is more than or equal to 50%, the content of S is less than or equal to 0.50% and the content of P is less than or equal to 0.50%. The manufacturing method comprises: the wet materials in the carbonic waste material and the ferreous waste material are firstly dried and crushed by a crusher, and then enters a blending machine to be mixed together with the dry materials such as the iron scale and the like; the mixture is added with the caking agent to be evenly mixed, and the mixed material is sent into a mixing mill and then into a twin-roller ball press machine to be pressed into conglomeration; the pressed conglomeration is screened by a sieving machine, and the qualified screened conglomeration can be sent into a dry furnace to be dried, so that the finished product conglomeration can be obtained. The rotary furnace cooling agent completely uses the waste materials generated in the steel production, and can be used for replacing the common waste steel to be applied in smelting of a rotary furnace, so that no special reduction plant is needed for use, the process flow is short, the cost is low, the using method is flexible, the adding quantity is large, the recovery rate is high, the field operation is seldom affected, the economic benefit and the environmental protection benefit are remarkable, and the promotion and application values are excellent.

Description

technical field [0001] The invention belongs to the field of metallurgical waste recycling, in particular to a converter coolant using metallurgical waste as a raw material and a manufacturing method thereof. Background technique [0002] In the process of converter steelmaking, in order to make good slag, early melt slag and control the appropriate temperature of molten steel, it is necessary to add cooling and flux. [0003] Traditional cooling and fluxing agents, including lump iron ore, steel scrap, fluorspar, lime, etc. When lumpy iron ore is used as cooling flux, due to the low iron content of lumpy iron ore, the main component is iron oxide which is difficult to reduce, and most of them are acidic ores, not only the metal yield is low, but also the amount of slag will increase , the life of the furnace lining is reduced, and it cannot play a good role as a flux; when scrap steel, lime and fluorite are used as cooling and fluxing agents, on the one hand, the supply of...

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a converter coolant and its manufacturing method using metallurgical waste as raw material, which can replace ordinary steel scrap, has low cost and good effect, and can overcome the existing deficiencies in cooling and flux, and solve the problem of iron and steel plant containing Carbon-containing iron-containing scrap cannot be efficiently utilized, and the cost of steelmaking plants rises rapidly due to the purchase of scrap steel.

This solves the problem that the converter coolant made of other iron-containing wastes has a high content of FeO, which is easy to cause splashing, slag running, and slag overflow during converter smelting, which affects the smelting operation, thereby improving the quality of the coolant. Added amount

Images