A long afterglow, paint film technology, applied in coatings, luminescent coatings, polyurea/polyurethane coatings, etc., can solve the problems of blackening of products, structural changes of luminous powder, influence of luminous effect, etc., to achieve good ductility, excellent long-term Afterglow luminous performance, the effect of improving overall performance and application range

Active Publication Date: 2017-10-03
广州雷诺丽特塑料有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing luminous PVC film is generally prepared by directly adding rare earth luminous pigments to the PVC formula, and is prepared by calendering or casting. Since the luminous powder has a high hardness, strong friction with the metal cannot be avoided through the calendering process. Affect the saturation state of the luminous powder, and easily lead to blackening of the product. At the same time, strong friction will also cause changes in the structure of the lumi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PVC paint film with long afterglow and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] A long afterglow PVC paint film, its preparation method includes the following steps: (1) First, stir the hydroxyacrylic resin with a blender for three minutes to make it evenly distributed, then weigh 100 parts, and then weigh 10 parts 6 Methylene diisocyanate, and add 33.3 parts of methyl ethyl ketone to fully mix it with hexamethylene diisocyanate, slowly add it to the weighed hydroxyacrylic acid resin paint while stirring; then, add 0.5 part of rare earth luminous Pigment whose composition can be expressed as Al 2 O 3 ·(Sr, Mg, Ca) O: (Eu, La, Dy) B, and stir evenly; use a viscosity cup to measure the viscosity of the mixed material, and use methyl ethyl ketone to adjust the viscosity of the material to 12 seconds, and finally The adjusted material is added to the circulating pump and waits to be turned on;

[0022] (2) Unwinding: Install the prepared PVC film on the unwinder, and pull it through the coating roller, then through the oven, and finally ...

Example Embodiment

[0026] Example 2

[0027] A long afterglow PVC paint film, its preparation method includes the following steps: (1) First, stir the propylene hydroxy acrylic resin with a mixer for three minutes to make it evenly distributed, then weigh 100 parts, and then weigh 22 parts Isocyanate, and add 22 parts of cyclohexanone to fully mix it with isocyanate, slowly add it to the weighed hydroxyacrylic resin paint while stirring; then, add 3 parts of rare earth luminous pigment, its composition can be expressed as Al 2 O 3 ·(Sr, Mg, Ca) O: (Eu, La, Dy) B, and stir evenly; use a viscosity cup to measure the viscosity of the mixed material, and use cyclohexanone to adjust the viscosity of the material to 15.5 seconds, and finally, Add the adjusted material to the circulating pump and wait for it to start;

[0028] (2) Unwinding: Install the prepared PVC film on the unwinder, and pull it through the coating roller, then through the oven, and finally fixed on the winder;

[0029] (3) Startup: adju...

Example Embodiment

[0032] Example 3

[0033] A long afterglow PVC paint film, its preparation method includes the following steps: (1) First, stir the propylene polyether resin with a mixer for three minutes to make it evenly distributed, then weigh 100 parts, and then weigh 33.3 parts Liuya Methyl diisocyanate, and add 10 parts of ethyl acetate to fully mix it with hexamethylene diisocyanate, and slowly add it to the weighed polyether resin paint while stirring; then, add 5 parts of rare earth luminous pigments, Its composition can be expressed as Al 2 O 3 ·(Sr, Mg, Ca) O: (Eu, La, Dy) B, and stir evenly; use a viscosity cup to measure the viscosity of the mixed material, and use ethyl acetate to adjust the viscosity of the material to 18 seconds, finally, Add the adjusted material to the circulating pump and wait for it to start;

[0034] (2) Unwinding: Install the prepared PVC film on the unwinder, and pull it through the coating roller, then through the oven, and finally fixed on the winder;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVC paint film with long afterglow. The PVC paint film comprises a PVC film and a noctilucent coating on the PVC film. The noctilucent coating is prepared from the following raw materials by weight: 100 parts of acrylate or polyurethane, 10 to 33.3 parts of a curing agent, 10 to 33.3 parts of a solvent and 0.5 to 5 parts of a rare earth noctilucent pigment. Meanwhile, the invention also discloses a preparation method for the PVC paint film with long afterglow. The PVC paint film with long afterglow prepared by using the method has good ductility, weatherability and scratch resistance and excellent long-afterglow noctilucence performance; and the luminescence duration of the film can reach 6 to 8 h, far longer than the luminescence duration (2 to 3 h) of common PVC films.

Description

technical field [0001] The invention relates to the field of outdoor advertising and warning technology, in particular to a long afterglow PVC paint film and a preparation method thereof. Background technique [0002] The existing luminous PVC film is generally prepared by directly adding rare earth luminous pigments to the PVC formula, and is prepared by calendering or casting. Since the luminous powder has a high hardness, strong friction with the metal cannot be avoided through the calendering process. Affect the saturation state of the luminous powder, and easily lead to blackening of the product. At the same time, strong friction will also cause changes in the structure of the luminous powder, affecting the luminous effect; moreover, the temperature of the calendering process will exceed 180 degrees Celsius at least, while the processing temperature of the luminous powder It must be lower than 170 degrees Celsius. At such a high temperature, the initial structural orien...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J7/04C08J5/18C09D5/22C09D175/04C09D175/08C08L27/06
CPCC08J5/18C08J7/0427C08J2327/06C09D5/22C09D175/04C09D175/08
Inventor 江溪曾勇军
Owner 广州雷诺丽特塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap