Chai kiln porcelain yellowish pea green glaze

The technology of bean green glaze and glaze paste is applied in the field of ceramics, which can solve the problems of no high transparency and high gloss, and achieve the effect of uniform glaze layer, good gloss and strong decorative sense.

Active Publication Date: 2017-10-24
马聚魁
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chai porcelain is a kiln mouth named after Shizong Chai Rong's surname during the Five Dynasties. It is a famous porcelain kiln in history and is revered as the crown of all kilns. Mirror, thin as paper, and sound like a chime", it is infinitely yearning. The existing light-colored glazes are mainly high-temperature colored glazes produced in Jingdezhen, while there are almost no high-transparency, high-moisture, and high-gloss glazes in medium-temperature colored glazes. visual effect; therefore, it is very necessary to provide a chai porcelain bean green glaze that is fired at medium temperature quickly, with low cost, uniform glaze layer and good gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Chai porcelain bean green glaze, which is made of various components according to the following weight ratio: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone meal, 3.48 parts of agate stone, 2.56 parts of hydrocele 2.83 parts of black gold soil.

[0017] The quartz is quartz sand.

[0018] The feldspar is albite.

[0019] The content of iron oxide in the black gold soil is 30%-32%, and the content of manganese oxide is 8%-9%.

[0020] The preparation method of chai porcelain bean green glaze comprises the following steps:

[0021] a. Dosing according to the mass ratio of each component and each component;

[0022] b. Mix all components evenly, add 20-22 parts of water, wet ball mill for 16-18 hours, pass the ball-milled glaze through a 250-mesh sieve, and then adjust it to a glaze slurry of 60-65 degrees Baume , and then spray the glaze slurry on the incense ash tire, then raise the tempe...

Embodiment 2

[0027] Chai porcelain bean green glaze, which is made of various components according to the following weight ratio: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone meal, 3.48 parts of agate stone, 2.56 parts of hydrocele 2.83 parts of black gold soil.

[0028] The quartz is quartz sand.

[0029] The feldspar is potassium feldspar.

[0030] The content of iron oxide in the black gold soil is 30%-35%, and the content of manganese oxide is 8%-10%.

[0031] The preparation method of chai porcelain bean green glaze comprises the following steps:

[0032] a. Dosing according to the mass ratio of each component and each component;

[0033] b. Mix all components evenly, add 20-22 parts of water, wet ball mill for 18-20 hours, pass the ball-milled glaze through a 250-mesh sieve, and then adjust it to a glaze slurry of 60-65 degrees Baume , and then spray the glaze slurry on the incense ash tire, then ra...

Embodiment 3

[0038] Chai porcelain bean green glaze, which is made of various components according to the following weight ratio: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone meal, 3.48 parts of agate stone, 2.56 parts of hydrocele 2.83 parts of black gold soil.

[0039] The quartz is quartz sand.

[0040] The feldspar is a combination of albite and potassium feldspar.

[0041] The content of iron oxide in the black gold soil is 32%-35%, and the content of manganese oxide is 9%-10%.

[0042] The preparation method of chai porcelain bean green glaze comprises the following steps:

[0043] a. Dosing according to the mass ratio of each component and each component;

[0044] b. Mix all components evenly, add 20-22 parts of water, wet ball mill for 18-20 hours, pass the ball-milled glaze through a 250-mesh sieve, and then adjust it to a glaze slurry of 60-65 degrees Baume , and then spray the glaze slurry on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to Chai kiln porcelain yellowish pea green glaze which is prepared from the following ingredients in parts by weight: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of slate gray, 5.58 parts of phosphorous bone powder, 3.48 parts of agate, 2.56 parts of hydrotalcite and 2.83 parts of white metal soil, wherein quartz sand serves as the quartz, the feldspar is a combination of one or two of sodaclase and potassium feldspar, the content of ferric oxide in the white metal soil is 30-35%, the content of manganese oxide is 8-10%, the used preparation method of Chai kiln porcelain green glaze comprises the following steps: a. carrying out burdening according to various ingredients and the proportion by weight of the various ingredients; and b. mixing the various ingredients uniformly, adding 20-22 parts of water, ball-milling for 16-20 hours by using a wet method, enabling ball-milled glaze to pass through a 250-mesh screen, then turning the glaze into glaze slip with 60-65 baume degrees, then spraying the glaze slip on a incense ash tire, afterwards, heating the glaze slip at normal temperature to 1,180-1,250 DEG C, then cooling, and drawing for 15 hours or so. The Chai kiln porcelain yellowish pea green glaze has the advantages of fast firing at medium temperature, lower cost, even and clean enamel layer, good glossiness and strong decorative perception.

Description

technical field [0001] The invention belongs to the technical field of ceramics, in particular to bean green glaze of chai porcelain. Background technique [0002] Chai porcelain is a kiln mouth named after Shizong Chai Rong's surname during the Five Dynasties. It is a famous porcelain kiln in history and is revered as the crown of all kilns. Mirror, thin as paper, and sound like a chime", it is infinitely yearning. The existing light-colored glazes are mainly high-temperature colored glazes produced in Jingdezhen, while there are almost no high-transparency, high-moisture, and high-gloss glazes in medium-temperature colored glazes. Therefore, it is very necessary to provide a chai porcelain bean green glaze that is fired quickly at medium temperature, has low cost, has a uniform glaze layer, and has good gloss. Contents of the invention [0003] The object of the present invention is to overcome the deficiencies of the prior art, and provide a kind of chai porcelain bean...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 马聚魁马铭马得原
Owner 马聚魁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com