Chai Porcelain Bean Green Glaze

A bean green glaze and green ash technology, applied in the field of ceramics, can solve the problems of no high transparency and high gloss, and achieve the effects of uniform glaze layer, good gloss and low cost

Active Publication Date: 2020-08-21
马聚魁
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chai porcelain is a kiln mouth named after Shizong Chai Rong's surname during the Five Dynasties. It is a famous porcelain kiln in history and is revered as the crown of all kilns. Mirror, thin as paper, and sound like a chime", it is infinitely yearning. The existing light-colored glazes are mainly high-temperature colored glazes produced in Jingdezhen, while there are almost no high-transparency, high-moisture, and high-gloss glazes in medium-temperature colored glazes. visual effect; therefore, it is very necessary to provide a chai porcelain bean green glaze that is fired at medium temperature quickly, with low cost, uniform glaze layer and good gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Chai Porcelain Bean Green Glaze is made of the following components by weight: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone powder, 3.48 parts of agate stone, and 2.56 parts of water bone stone. part, 2.83 parts of Wujin soil.

[0017] The quartz is quartz sand.

[0018] The feldspar is albite.

[0019] The content of iron oxide in the black gold soil is 30%-32%, and the content of manganese oxide is 8%-9%.

[0020] The preparation method of Chai Porcelain Bean Green Glaze, which includes the following steps:

[0021] a. Make ingredients according to the mass ratio of each component and each component;

[0022] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 16-18 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slurry on the incense ash body, then heat it...

Embodiment 2

[0027] Chai Porcelain Bean Green Glaze is made of the following components by weight: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone powder, 3.48 parts of agate stone, and 2.56 parts of water bone stone. part, 2.83 parts of Wujin soil.

[0028] The quartz is quartz sand.

[0029] The feldspar is potassium feldspar.

[0030] The content of iron oxide in the black gold soil is 30%-35%, and the content of manganese oxide is 8%-10%.

[0031] The preparation method of Chai Porcelain Bean Green Glaze, which includes the following steps:

[0032] a. Make ingredients according to the mass ratio of each component and each component;

[0033] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 18-20 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slurry on the incense ash body,...

Embodiment 3

[0038] Chai Porcelain Bean Green Glaze is made of the following components by weight: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of blue ash, 5.58 parts of phosphorus bone powder, 3.48 parts of agate stone, and 2.56 parts of water bone stone. part, 2.83 parts of Wujin soil.

[0039] The quartz is quartz sand.

[0040] The feldspar is a combination of albite and potassium feldspar.

[0041] The content of iron oxide in the black gold soil is 32%-35%, and the content of manganese oxide is 9%-10%.

[0042] The preparation method of Chai Porcelain Bean Green Glaze, which includes the following steps:

[0043] a. Make ingredients according to the mass ratio of each component and each component;

[0044] b. Mix the components evenly, add 20-22 parts of water, wet ball milling for 18-20 hours, the glaze after ball milling passes through a 250-mesh sieve, and then adjust to a glaze slurry of 60-65 Baume degree , and then spray the glaze slu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to Chai kiln porcelain yellowish pea green glaze which is prepared from the following ingredients in parts by weight: 20.18 parts of quartz, 35.28 parts of feldspar, 11.26 parts of calcite, 18.83 parts of slate gray, 5.58 parts of phosphorous bone powder, 3.48 parts of agate, 2.56 parts of hydrotalcite and 2.83 parts of white metal soil, wherein quartz sand serves as the quartz, the feldspar is a combination of one or two of sodaclase and potassium feldspar, the content of ferric oxide in the white metal soil is 30-35%, the content of manganese oxide is 8-10%, the used preparation method of Chai kiln porcelain green glaze comprises the following steps: a. carrying out burdening according to various ingredients and the proportion by weight of the various ingredients; and b. mixing the various ingredients uniformly, adding 20-22 parts of water, ball-milling for 16-20 hours by using a wet method, enabling ball-milled glaze to pass through a 250-mesh screen, then turning the glaze into glaze slip with 60-65 baume degrees, then spraying the glaze slip on a incense ash tire, afterwards, heating the glaze slip at normal temperature to 1,180-1,250 DEG C, then cooling, and drawing for 15 hours or so. The Chai kiln porcelain yellowish pea green glaze has the advantages of fast firing at medium temperature, lower cost, even and clean enamel layer, good glossiness and strong decorative perception.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a chai porcelain bean green glaze. Background technique [0002] Chai Porcelain is a kiln named after the surname of Sejong Chai Rong during the Five Dynasties. It is a famous porcelain kiln in history and is respected as the crown of all kilns. "Mirror, thin as paper, sound like a chime", people yearn for infinitely. The existing light-colored glazes are mainly high-temperature color glazes produced in Jingdezhen. Among the medium-temperature color materials, there are almost no high-transparency, high-moisture, and high-gloss glazes. Therefore, it is very necessary to provide a chai porcelain bean green glaze with fast firing at medium temperature, low cost, uniform glaze layer and good gloss. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, and to provide a kind of firewood celadon glaze wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86C04B41/4539C04B41/0072
Inventor 马聚魁马铭马得原
Owner 马聚魁
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap