Sun-proof and anti-corrosion cable sheath material and preparation method thereof

A cable sheath material and anti-corrosion technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve problems such as aging and cracking of cable sheaths, affecting life and work, and deterioration of transmission performance, reaching a broad market and application Foreground, small bulk density, excellent acid and alkali resistance and the effect of chemical agent corrosion

Inactive Publication Date: 2017-11-03
HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the service life of the cable, the sheath must protect the cable core from moisture and other pollution. The degree of protection should keep the circuit performance in the cable core normal. Once too much moisture or other pollutants enter the cable core, the transmission performance will be affected. will seriously deteriorate
This requires the cable sheath to have high mechanical strength and internal toughness to prevent cracking or damage in harsh environments, resulting in abnormal cable transmission or potential safety hazards
[0003] Cables used in outdoor, underwater or other environments are often in contact with corrosive substances, especially in poor outdoor environments, often encountering rainwater with a certain pH value, coupled with sunlight, high temperature, etc. Environmental conditions, long-term use of the cable sheath often appear aging cracks and other phenomena, resulting in varying degrees of circuit failures, affecting people's normal life and work

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sun-proof and anti-corrosion cable sheath material and preparation method thereof
  • Sun-proof and anti-corrosion cable sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A sun-resistant and anti-corrosion cable sheath material, the following raw materials are weighed for use: chlorinated polyethylene 60kg, thermoplastic polyurethane elastomer 25kg, polyphenylene sulfone resin 20kg, modified sodium zeolite powder 15kg, sodium-based bentonite 5kg, Microcrystalline wax 4kg, glass fiber 6kg, boron nitride 3kg, dioctyl phthalate 5kg, diphenyl phosphate 4kg, adhesive 1kg, antistatic agent 1kg, antioxidant 1kg and anti-radiation agent 1kg;

[0026] The above-mentioned modified sodium zeolite powder is prepared by the following steps: take 15 kg of sodium zeolite and crush it through a 100-mesh sieve to obtain sodium zeolite powder, then place the sodium zeolite powder in a calcination furnace at 360 ° C for 1 hour, and then roast the calcined Sodium zeolite powder is conveyed in the high-speed kneader, add the aluminate coupling agent that is equivalent to 3% of fly ash weight, 2% sodium lignosulfonate, 2% triethyl citrate and 1% liquid paraffi...

Embodiment 2

[0033] A sun-resistant and anti-corrosion cable sheathing material, the following raw materials are weighed for use: 70kg of chlorinated polyethylene, 30kg of thermoplastic polyurethane elastomer, 25kg of polyphenylene sulfone resin, 20kg of modified sodium zeolite powder, 10kg of sodium bentonite, Microcrystalline wax 6kg, glass fiber 8kg, boron nitride 5kg, dioctyl phthalate 6kg, diphenyl phosphate 5kg, adhesive 3kg, antistatic agent 3kg, antioxidant 3kg and anti-radiation agent 3kg;

[0034] The above-mentioned modified sodium zeolite powder is prepared by the following steps: take 20 kg of sodium zeolite and crush it through a 150-mesh sieve to obtain sodium zeolite powder, then place the sodium zeolite powder in a calcination furnace at 370 ° C for 1.5 h, and then roast the The sodium zeolite powder is transported to the high-speed kneader, and the aluminate coupling agent equivalent to 4% of the weight of fly ash, 3% sodium lignosulfonate, 3% triethyl citrate and 2% liqui...

Embodiment 3

[0041] A sun-resistant and anti-corrosion cable sheath material, the following raw materials are weighed for use: 80kg of chlorinated polyethylene, 35kg of thermoplastic polyurethane elastomer, 30kg of polyphenylene sulfone resin, 25kg of modified sodium zeolite powder, 15kg of sodium bentonite, Microcrystalline wax 8kg, glass fiber 10kg, boron nitride 7kg, dioctyl phthalate 7kg, diphenyl phosphate 6kg, adhesive 5kg, antistatic agent 5kg, antioxidant 5kg and anti-radiation agent 5kg;

[0042] The above-mentioned modified sodium zeolite powder is prepared by the following steps: take 25 kg of sodium zeolite and crush it through a 200-mesh sieve to obtain sodium zeolite powder, then place the sodium zeolite powder in a calcination furnace at 380 ° C for 2 hours, and then roast the roasted Sodium zeolite powder is conveyed in the high-speed kneader, adds the aluminate coupling agent that is equivalent to 5% of fly ash weight, 4% sodium lignosulfonate, 4% triethyl citrate and 3% li...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sun-proof and anti-corrosion cable sheath material and a preparation method thereof, and relates to the technical field of an electric wire and a cable. The sheath material is prepared from the following raw materials including chlorinated polyethylene, thermoplastic polyurethane elastomers, polyphenylene sulfone resin, modified natrolite powder, sodium bentonite, microcrystalline wax, glass fiber, boron nitride, dioctyl phthalate, diphenyl phosphate, bonding agents, antistatic agents, antioxidants and anti-radiation agents. According to the preparation method, the sun-proof and anti-corrosion cable sheath material is obtained through performing mixing, banburying and granulation on the raw materials. The cable sheath material provided by the invention has the advantages that the preparation is simple and convenient; the production cost is low; excellent acid, alkali and chemical corrosion performance, sun-proof insulation performance, anti-aging performance and tensile strength are realized; the application field is wide; the service life is long; wide market and application prospects are realized.

Description

technical field [0001] The invention relates to the technical field of electric wires and cables, in particular to a sun-resistant and anti-corrosion cable sheathing material and a preparation method thereof. Background technique [0002] Wire and cable are the carriers of power transmission and information transmission, and are widely used in industrial and civil electrical facilities. Wires and cables are used in different environments or occasions and have different requirements, which puts forward higher requirements for the cable sheath covering the outside of the cable. The main function of the cable sheath is to mechanically and electrically protect the transmission cable from various conditions that will cause it to lose its transmission function. The cable jacket must fulfill this protective function during installation, splicing and throughout the service life of the cable. During the service life of the cable, the sheath must protect the cable core from moisture...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L75/04C08L81/06C08L91/06C08K13/06C08K7/14C08K9/04C08K7/26C08K3/34C08K5/12H01B3/44
CPCC08L23/286C08L2201/08C08L2203/202C08L2205/035H01B3/441C08L75/04C08L81/06C08L91/06C08K13/06C08K7/14C08K9/04C08K9/08C08K7/26C08K3/346C08K5/12
Inventor 齐慧
Owner HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com