High-flame retardant high temperature-retardant cable insulation material and preparation method thereof

A technology of cable insulation and high temperature resistance, used in rubber insulators, organic insulators, etc., can solve the problems of uniform dispersion and difficulty in flame retardants, and achieve the effect of improving temperature resistance stability and improving flame retardant effect.

Inactive Publication Date: 2017-11-24
JIANGSU PUCAO TECH CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to propose a high flame-retardant and high-temperature-resistant cable insulation material and a preparation method for the above shortcomings of the prior art, which can not only effectively improve the high-temperature resistance effect, but also improve the flame-retardant effect, and solve the problem of Solve the technical problem that the flame retardant is difficult to uniformly disperse in the polymer resin matrix

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] This embodiment is a high flame-retardant and high-temperature-resistant cable insulation material, which includes the following components by weight: EPDM rubber: 100 parts, vinyl polysiloxane: 10 parts, vinyl phenyl polysiloxane Alkane: 5 parts, Di-(2,3-dichloropropyl) hexamethylenetetramine phosphate: 20 parts, Cyclodextrin: 10 parts, Nano Mica: 5 parts, Nano Kaolin: 5 parts, Monoglycerol Stearate: 0.5 parts, dicumyl peroxide: 1 part.

[0013] The preparation method of the high flame-retardant and high-temperature-resistant cable insulation material of this embodiment comprises the following steps:

[0014] (1) Grind phosphoric acid-bis-(2,3-dichloropropyl)hexamethylenetetramine and cyclodextrin in a mortar for 30 minutes or knead them in a kneader for 20 minutes to obtain a mixture of the two compound;

[0015] (2) Mix the clathrate obtained in step (1) with other materials in the formula according to the proportion, stir the prepared raw materials evenly in the k...

Embodiment 2

[0018] This embodiment is a high flame-retardant and high-temperature-resistant cable insulation material, which includes the following components by weight: EPDM rubber: 100 parts, vinyl polysiloxane: 15 parts, vinyl phenyl polysiloxane Alkane: 10 parts, Di-(2,3-dichloropropyl) hexamethylenetetramine phosphate: 30 parts, Cyclodextrin: 15 parts, Nano mica: 7 parts, Nano kaolin: 8 parts, Glycerol mono Stearate: 1 part, Dicumyl Peroxide: 2 parts.

[0019] The preparation method of the high flame-retardant and high-temperature-resistant cable insulation material of this embodiment comprises the following steps:

[0020] (1) Grind phosphoric acid-bis-(2,3-dichloropropyl)hexamethylenetetramine and cyclodextrin in a mortar for 50 minutes or knead them in a kneader for 30 minutes to obtain a mixture of the two compound;

[0021] (2) Mix the clathrate obtained in step (1) with other materials in the formula according to the proportion, stir the prepared raw materials evenly in the k...

Embodiment 3

[0024] This embodiment is a high flame-retardant and high-temperature-resistant cable insulation material, which includes the following components by weight: EPDM rubber: 100 parts, vinyl polysiloxane: 20 parts, vinyl phenyl polysiloxane Alkane: 15 parts, Di-(2,3-dichloropropyl) hexamethylenetetramine phosphate: 40 parts, Cyclodextrin: 20 parts, Nano Mica: 10 parts, Nano Kaolin: 10 parts, Glycerol Mono Stearate: 1 part, Dicumyl Peroxide: 3 parts.

[0025] The preparation method of the high flame-retardant and high-temperature-resistant cable insulation material of this embodiment comprises the following steps:

[0026] (1) Grind phosphoric acid-bis-(2,3-dichloropropyl)hexamethylenetetramine and cyclodextrin in a mortar for 60 minutes or knead them in a kneader for 40 minutes to obtain a mixture of the two compound;

[0027] (2) Mix the clathrate obtained in step (1) with other materials in the formula according to the proportion, stir the prepared raw materials evenly in the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-flame retardant high-temperature retardant cable insulation material. The cable insulation material comprises, by weight, 100 parts of an ethylene propylene diene monomer, 10 to 20 parts of vinyl polysiloxane, 5 to 15 parts of vinyl phenyl polysiloxane, 20 to 40 parts of bis(2, 3-dichloropropyl)hexamethylenetetramine phosphate (single-component intumescent flame retardant), 10 to 20 parts of cyclodextrin, 5 to 10 parts of nano-mica, 5 to 10 parts of nano-kaolin, 0.5 to 1 part of glyceryl monostearate and 1 to 3 parts of dicumyl peroxide. The bis(2, 3-dichloropropyl)hexamethylenetetramine phosphate and cyclodextrin can form an inclusion compound in the cable insulation material. Through use of excellent transportation and dispersion ability of the cyclodextrin, the flame retardant can be uniformly dispersed at the molecular level in the resin matrix so that the flame retardant effects are greatly improved.

Description

technical field [0001] The invention relates to a cable insulating material and a preparation method thereof, in particular to a high flame-retardant and high temperature-resistant cable insulating material and a preparation method thereof. Background technique [0002] Existing cable insulation materials have unsatisfactory flame retardant and high temperature resistance effects. In order to achieve high temperature resistance, polymer resins are often added to their components; in order to achieve flame retardant effects, flame retardants are often added to their components; However, the flame retardant effect is largely affected by the dispersion uniformity of the flame retardant in the entire material; the polymer resin and the flame retardant have huge differences in molecular weight and physical and chemical properties, and the compatibility is poor. The flame retardant is often difficult to disperse evenly in the polymer resin matrix, which leads to unsatisfactory fla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/16C08L83/07C08L5/16C08K13/06C08K9/12C08K3/34C08K5/103C08K5/14C08K5/521H01B3/28
CPCC08L23/16C08K2201/011C08L2201/02C08L2201/08C08L2203/202C08L2205/025C08L2205/035C08L2312/00H01B3/28C08L83/04C08L5/16C08K13/06C08K9/12C08K3/34C08K3/346C08K5/103C08K5/14C08K5/521
Inventor 芮黎春胡杰
Owner JIANGSU PUCAO TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com