High-strength antibacterial garbage bag and manufacture method thereof

A high-strength, garbage bag technology, applied in the field of garbage bags, can solve the problems of poor mechanical strength and durability, bacterial growth, etc.

Inactive Publication Date: 2017-11-24
WUHU BLUE SKY ENG PLASTIC CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although paper garbage bags and paper-plastic composite bags are environmentally friendly due to their materials, they are far inferior to plastic garbage bags in terms of mechanical strength and durability.
However, the airtightness of the material that plastic waste is easy to cause will easily lead to the growth of bacteria

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0010] The invention provides a kind of preparation method of high-strength antibacterial garbage bag, comprising:

[0011] First polycarbonate resin, phenolic resin, aluminum stearate, kaolin, calcium silicate, attapulgite, chitin fiber, turpentine, vinyl trimethoxysilane, dioctyl phthalate and brand KH560 The silane coupling agent is mixed and rubberized to obtain a rubber compound; then, the rubber compound is added to an extruder for extrusion molding and processing to obtain a high-strength antibacterial garbage bag;

[0012] Wherein, the extruder includes a feeding section, a middle section and an extruder head connected in sequence, and the working temperature of the extruder is: feeding section 90-100°C, middle section 110-125°C, extruder head 150°C -195°C.

[0013] In the above technical solution, the conditions of the rubber mix can be selected in a wide range, but in order to further improve the tensile strength and tensile properties of the garbage bag made, prefe...

Embodiment 1

[0026] First polycarbonate resin (weight average molecular weight is 20,000), phenolic resin (weight average molecular weight is 30,000), aluminum stearate, kaolin, calcium silicate, attapulgite (average particle size is 20 μm), chitin Fiber (chitin fiber is extracted from the shells of shrimp, crab and locust), turpentine, vinyltrimethoxysilane, dioctyl phthalate and KH560 silane coupling agent according to 100:15:2: 5: 1.5: 3: 1.5: 3: 1.1: 0.5: 0.5 weight ratio, mix at room temperature 25°C, speed 2000rpm for 1h; then, stir and mix at 90°C, speed 2000rpm for 2h; then , at 130°C for 4 hours to get rubber compound;

[0027] Finally, the prepared rubber material is added to the extruder (the temperature control of the extruder is: feeding section 90°C, middle section 110°C, extruder head 165°C) to extrude and granulate, and then go through inflation, traction The high-strength antibacterial garbage bags are obtained through processing procedures such as printing, winding and b...

Embodiment 2

[0030] First polycarbonate resin (weight average molecular weight is 25,000), phenolic resin (weight average molecular weight is 35,000), aluminum stearate, kaolin, calcium silicate, attapulgite (average particle size is 25 μm), chitin Fiber (chitin fiber is extracted from shells of shrimp, crab, locust, silkworm, and snail), turpentine, vinyltrimethoxysilane, dioctyl phthalate and KH560 silane coupling agent according to 100: 18: 3: 6: 1: 2.5: 4: 2.5: 5: 1.5: 1.7: 1.1 weight ratio, at room temperature 28 ° C, the rotation speed is 2500 rpm for 2 hours; then, at 100 ° C, the rotation speed is 3000 rpm Stir and mix for 2 hours; then, mix at 140°C for 3 hours to obtain the rubber compound;

[0031] Finally, the prepared rubber material is added to the extruder (the temperature control of the extruder is: feeding section 95°C, middle section 115°C, extruder head 185°C) to extrude and granulate, and then go through inflation, traction , printing, winding and bag making processes ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength antibacterial garbage bag and a manufacture method thereof. The manufacture method comprises the steps of firstly carrying out mixing and rubber mixing on polycarbonate resin, phenolic resin, aluminum stearate, kaolin, calcium silicate, attapulgite, chitosan fiber, turpentine, vinyl trimethoxy silane, dioctyl phthalate and a silane coupling agent of which the mark is KH560 to prepare a sizing material; adding the sizing material to an extruder for extrusion molding and processing to prepare the high-strength antibacterial garbage bag, wherein the extruder comprises a feeding section, a medium section and an extrusion head which are sequentially connected; and the operating temperatures of the extruder are as follows: the operating temperature of the feeding section is 90-100 DEG C, the operating temperature of the medium section is 110-125 DEG C and the operating temperature of the extrusion head is 150-195 DEG C. The high-strength antibacterial garbage bag has excellent mechanical properties, such as high tensile strength and good tensile property, and also has excellent antibacterial property.

Description

technical field [0001] The invention relates to the field of garbage bags, in particular to a high-strength antibacterial garbage bag and a preparation method thereof. Background technique [0002] Garbage bags, as the name suggests, are bags for garbage. A small bag brings great convenience to thousands of households, and it also provides an important guarantee for environmental protection, and is even conducive to garbage recycling and classification. According to the classification of materials, garbage bags can be divided into plastic garbage bags, paper garbage bags and paper-plastic composite bags. Although paper garbage bags and paper-plastic composite bags are environmentally friendly due to their materials, they are far inferior to plastic garbage bags in terms of mechanical strength and durability. However, the airtightness of the material that plastic waste is easy to cause will easily lead to the growth of bacteria. Contents of the invention [0003] The purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L61/06C08L5/08C08K13/02C08K5/098C08K3/34C08K5/12C08K5/5425C08K5/5435
CPCC08L69/00C08L2205/035C08L2205/16C08L61/06C08L5/08C08K13/02C08K5/098C08K3/34C08K3/346C08K5/12C08K5/5425C08K5/5435
Inventor 钱万水
Owner WUHU BLUE SKY ENG PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap