Flame-retardant and thermal-insulation coating for server casing

A technology of thermal insulation coating and server, which is applied in the field of coatings to achieve the effects of good thermal insulation and flame retardancy, improved stability and improved temperature tolerance

Inactive Publication Date: 2017-11-24
CHENGDU BAOMIHUA INFORMATION TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the increasingly harsh environment and the heat generated by the server itself, in order to ensure the good and stable operation of the server, higher requirements are put forward for the flame retardant and heat insulation performance of the server shell. Simply relying on the material of the server shell can no longer meet the above requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Embodiment 1, the present invention provides a flame-retardant and heat-insulating coating for server shells, which is made of the following raw materials in proportions by weight: 35 parts of chitosan biguanide hydrochloride, 19 parts of methylphenyl silicone resin , 9 parts of nano-silver powder, 6 parts of phosphate flame retardant, 3 parts of thickener, 5 parts of calcium carbonate, 5 parts of film-forming aid, 4 parts of methylhexanone peroxide, 10 parts of ethylene glycol, and 12 parts of hollow microspheres 5 parts, 5 parts of curing agent, 4 parts of medical stone powder, 0.9 part of methyl p-hydroxybenzoate, 40 parts of deionized water, 0.7 part of glycerol stearate.

[0009] Compared with the shell not coated with the present invention, in the same external environment, the heat insulation time of the server shell coated with the present invention is prolonged by 12%, and the withstand temperature is increased by 18%.

Embodiment 2

[0010] Embodiment 2, the present invention provides a flame-retardant heat-insulating coating for server shells, which is made of the following raw materials in proportions by weight: 28 parts of chitosan biguanide hydrochloride, 15 parts of methylphenyl silicone resin , 8 parts of nano-silver powder, 4 parts of phosphate ester flame retardant, 2 parts of thickener, 3 parts of calcium carbonate, 4 parts of film-forming aid, 2 parts of methylhexanone peroxide, 7 parts of ethylene glycol, and 10 parts of hollow microspheres part, 4 parts of curing agent, 2.9 parts of medical stone powder, 0.8 part of methyl p-hydroxybenzoate, 38 parts of deionized water, and 0.6 part of glycerol stearate.

[0011] Compared with the shell not coated with the present invention, in the same external environment, the heat insulation time of the server shell coated with the present invention is prolonged by 14%, and the withstand temperature is increased by 21%.

Embodiment 3

[0012] Embodiment 3, the present invention provides a flame-retardant and heat-insulating coating for server shells, which is made of the following raw materials in proportions by weight: 20 parts of chitosan biguanide hydrochloride, 12 parts of methylphenyl silicone resin , 5 parts of nano-silver powder, 2 parts of phosphate ester flame retardant, 1 part of thickener, 2 parts of calcium carbonate, 3 parts of film-forming aid, 1 part of methylhexanone peroxide, 5 parts of ethylene glycol, and 6 parts of hollow microspheres 2 parts, 2 parts of curing agent, 2 parts of medical stone powder, 0.7 part of methyl p-hydroxybenzoate, 35 parts of deionized water, 0.5 part of glycerol stearate.

[0013] Compared with the shell not coated with the present invention, in the same external environment, the heat insulation time of the server shell coated with the present invention is prolonged by 11%, and the withstand temperature is increased by 17%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flame-retardant and thermal-insulation coating for a server casing. The flame-retardant and thermal-insulation coating is prepared from raw materials in parts by weight as follows: 20-35 parts of chitosanguanidine chloride, 12-19 parts of methyl phenyl silicone resin, 5-9 parts of nanometer silver powder, 2-6 parts of a phosphate ester flame retardant, 1-3 parts of a thickening agent, 2-5 parts of calcium carbonate, 3-5 parts of a coalescing agent, 1-4 parts of methyl ethyl ketone peroxide, 5-10 parts of ethanediol, 6-12 parts of hollow microspheres, 2-5 parts of a curing agent, 2-4 parts of medical stone powder, 0.7-0.9 parts of methyl 4-hydroxybenzoate, 35-40 parts of deionized water and 0.5-0.7 parts of glyceryl stearate. The flame-retardant and thermal-insulation coating is applied to the casing of a server and has good thermal-insulation and flame-retardant capacity, the tolerable temperature of the server casing is increased, and the stability of the server is improved.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a flame-retardant and heat-insulating coating for server shells. Background technique [0002] A server, also called a server, is a device that provides computing services. The composition of the server includes processors, hard disks, memory, system buses, etc., which are similar to general-purpose computer architectures, but due to the need to provide highly reliable services, processing power, stability, reliability, security, scalability, scalability Management requirements are high. Due to the increasingly harsh environment and the heat generated by the server itself, in order to ensure the good and stable operation of the server, higher requirements are put forward for the flame retardancy and heat insulation performance of the server shell. The material of the server shell alone cannot meet the above requirements. Contents of the invention [0003] The present inventi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D105/08C09D183/04C09D5/18C09D7/12
CPCC09D105/08C08K2003/0806C08K2003/265C08K2201/011C08L2201/02C08L2201/08C09D5/18
Inventor 梁庆欢蒋颖王川林
Owner CHENGDU BAOMIHUA INFORMATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products