Preparation method of ceramic artwork

A technology of ceramic handicrafts and handicrafts, applied in the direction of ceramic molding machines, manufacturing tools, coatings, etc., can solve the problems of low mechanical strength and complicated preparation methods, and achieve high mechanical strength, scientific and simple preparation methods, and fresh smell Effect

Inactive Publication Date: 2017-12-29
顾玉城
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing preparation methods of ceramic handicrafts are too complicated, and the mechanical properties of the prepared ceramic handicrafts are low. Handicrafts are products made by processing raw materials or semi-finished products by hand or machine, and are a general term for a group of valuable works of art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ceramic artwork

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: as figure 1 Shown, the invention provides a kind of preparation method of ceramic handicraft,

[0028] The weight composition of the handicraft body is as follows: 59 parts of white mud; 50 parts of kaolin; 30 parts of high alumina bauxite; 20 parts of black mud; 20 parts of quicklime; 1 part of zirconium silicate; 1 part of ethanolamine; 1 part of potassium chloride; 1 part of sodium carbonate; 1 part of Chinese herbal medicine powder; 1 part of water reducer;

[0029] The weight composition of this handicraft paint is as follows: 30 parts of water-based resins; 1 part of Chinese herbal medicine powder; 8 parts of additives; 100 parts of water;

[0030] The preparation method of this handicraft is:

[0031] 1) Preparation of Chinese herbal medicine powder: weigh pine needle powder, earthworm, mint, orchid stone, cocklebur, clove, pomegranate peel, loofah vine, mugwort leaf, dogwood, plantain, gall, cinnamon, chrysanthemum, gourd tea, aloe vera , sandal...

Embodiment 2

[0044] Embodiment 2: as figure 1 Shown, the invention provides a kind of preparation method of ceramic handicraft,

[0045] The weight composition of the handicraft body is as follows: 99 parts of white mud; 80 parts of kaolin; 40 parts of high alumina bauxite; 40 parts of black mud; 30 parts of quicklime; 2 parts of zirconium silicate; 2 parts of ethanolamine; 2 parts of potassium chloride; 2 parts of sodium carbonate; 3 parts of Chinese herbal medicine powder; 2 parts of water reducer;

[0046] The weight composition of this handicraft coating is as follows: 35 parts of water-based resins; 2 parts of Chinese herbal medicine powder; 10 parts of additives; 120 parts of water;

[0047] The preparation method of this handicraft is:

[0048] 1) Preparation of Chinese herbal medicine powder: weigh pine needle powder, earthworm, mint, orchid stone, cocklebur, clove, pomegranate peel, loofah vine, mugwort leaf, dogwood, plantain, gall, cinnamon, chrysanthemum, gourd tea, aloe vera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of ceramic artwork. The preparation method comprises the following steps of preparation of Chinese herbal medicinal powder; preparation of pug; preparation of zirconium oxide ceramic powder; mixing and agitation: proportioning raw materials for a green body according to a composition by weight, grinding for 2h by adopting a grinder, then adding the prepared zirconium oxide ceramic powder and the pug, and uniformly agitating, so as to obtain a mixed material; adding the mixed material into a proper amount of water, carrying out wheel rolling, and uniformly agitating; molding: subjecting the mixed material to pugging and aging, and then carrying out compression molding under the pressure of 40Mpa; preparation of the green body: carrying out natural curing, so that the green body, prepared by the preparation method, of Chinese herbal medicinal ceramic artwork can be obtained; spray coating: proportioning raw materials for paint according to a composition by weight, carrying out wet-grinding for 2h by adopting the grinder, and uniformly agitating, so as to obtain slurry for the paint; carrying out the spray coating on the slurry, so as to obtain the ceramic artwork. The preparation method provided by the invention is scientific, simple and convenient and the prepared ceramic artwork has bactericidal, antibacterial and refreshing performance, is fresh in odor, healthy and environment-friendly, and is further higher in mechanical performance and strength.

Description

technical field [0001] The invention relates to the technical field of ceramic processing, in particular to a preparation method of ceramic handicrafts. Background technique [0002] Traditional ceramic handicrafts generally use more traditional colors such as blue, bright red, etc., and handicrafts are usually handicraft products. The existing preparation methods of ceramic handicrafts are too complicated, and the mechanical properties of the prepared ceramic handicrafts are low. Handicrafts are products made by processing raw materials or semi-finished products by hand or machine, and are a general term for a group of valuable artworks. Handicrafts come from life, but they create a value higher than life. It is the crystallization of the wisdom of the people, which fully embodies the creativity and artistry of human beings. It is a priceless treasure of human beings. In addition to functions, we also hope that handicrafts will have more environmentally friendly and value...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B41/63C09D201/00C09D7/12B28B3/00B28B11/24B28C1/04B28C1/16C04B111/20
CPCC04B28/10B28B3/00B28B11/24B28C1/04B28C1/16C04B41/009C04B41/48C04B41/63C04B2111/00956C04B2111/2092C08L2205/035C09D201/00C08L99/00C04B14/106C04B14/303C04B18/146C04B20/0048C04B14/4637C04B24/122C04B22/124C04B22/10C04B22/066C04B18/04C04B14/14C04B24/30C04B14/043C04B24/2611C04B24/045C04B24/32C04B24/008C04B24/124C04B14/366C04B24/2652C04B24/163C04B14/04C04B14/306C04B14/30C04B41/46
Inventor 顾玉城
Owner 顾玉城
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com