Continuous polymerization method for preparing rare earth butadiene rubber
A technology of rare earth butadiene and polymerization method, which is applied in the field of rubber preparation to achieve the effects of good fluidity, high catalytic activity and good effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] (1) The catalyst for the preparation of high Mooney rare earth butadiene rubber with narrow molecular weight distribution is neodymium phosphate (wherein the phosphate is bis(2-ethylhexyl), diisobutyl aluminum hydride and monochloro / dichloroethylaluminum, butadiene Diene, molecular weight regulator triisobutylaluminum (triisobutylaluminum / diisobutylaluminum hydride 50:1). The diisobutylaluminum hydride, monochloro / dichloroethylaluminum, butadiene The molar ratio with neodymium phosphate is 5:2:2:1 respectively.
[0030] The continuous polymerization method of the narrow molecular weight distribution high Mooney rare earth butadiene rubber provided by the invention is as follows:
[0031] Before start-up, prepare the device before start-up, introduce public works (water, electricity, gas, etc.), then pressurize the air-tightness test on the equipment and pipelines, and purge with nitrogen to ensure that the device does not leak and is in an oxygen-free state. Collect C6...
Embodiment 2
[0035] (1) The catalyst for preparing high Mooney rare earth butadiene rubber with narrow molecular weight distribution is neodymium phosphate (wherein the phosphate is 2-ethylhexyl phosphate 2-ethylhexyl ester), diisobutyl aluminum hydride and monochloro / dichloro Ethylaluminum, butadiene, molecular weight modifier triisobutylaluminum (triisobutylaluminum / diisobutylaluminum hydride 50:50). The mol ratio of described diisobutyl aluminum hydride and neodymium phosphate is 15:1; :1.
[0036] The continuous polymerization method of the narrow molecular weight distribution high Mooney rare earth butadiene rubber provided by the invention is as follows:
[0037] Before start-up, prepare the device before start-up, introduce public works (water, electricity, gas, etc.), then pressurize the air-tightness test on the equipment and pipelines, and purge with nitrogen to ensure that the device does not leak and is in an oxygen-free state. Collect C6 solvent oil, raw material butadiene a...
Embodiment 3
[0041] (1) The catalysts for preparing high Mooney rare earth butadiene rubber with narrow molecular weight distribution are neodymium phosphate (wherein the phosphoric acid ester is dimethyl heptyl methyl phosphate), diisobutyl aluminum hydride and monochloro / dichloroethyl aluminum, butadiene Diene, molecular weight regulator triisobutylaluminum (triisobutylaluminum / diisobutylaluminum hydride 99:1). The mol ratio of described diisobutyl aluminum hydride and neodymium phosphate is 25:1; :1.
[0042] The continuous polymerization method of the narrow molecular weight distribution high Mooney rare earth butadiene rubber provided by the invention is as follows:
[0043] Before start-up, prepare the device before start-up, introduce public works (water, electricity, gas, etc.), then pressurize the air-tightness test on the equipment and pipelines, and purge with nitrogen to ensure that the device does not leak and is in an oxygen-free state. Collect solvent oil, raw material but...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap