Quick-drying adhesive for BOPP adhesive tape and preparation method thereof

A technology of quick-drying adhesives and tapes, applied in the field of quick-drying adhesives, which can solve the problems of slow drying and poor film-forming property of BOPP tapes, and achieve the effects of increased drying speed, improved drying time, and increased quick-drying properties

Inactive Publication Date: 2018-01-19
潘明华
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: the purpose of this invention is to provide a quick-drying adhesive for BOP

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-drying adhesive for BOPP adhesive tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] A quick-drying adhesive for BOPP tape, which is prepared by weight of the following ingredients: 70 parts of butyl acrylate, 15 parts of hydroxyethyl acrylate, 10 parts of vinyl acetate, 70 parts of deionized water, and 0.5 parts of sodium lauryl sulfate Parts, 1.5 parts of alkylphenol polyoxyethylene ether, 0.02 parts of hexadecane, 0.4 parts of ammonium persulfate, 0.1 parts of ammonia water, 0.05 parts of tert-butyl hydroperoxide, 0.05 parts of sodium formaldehyde sulfoxylate, p-tert-butyl phenolic aldehyde 10 parts of resin, 2 parts of allyl modified alkyl phenolic resin, 6 parts of barium sulfate, 3 parts of tung oil.

[0018] The preparation method of the above-mentioned quick-drying adhesive for BOPP tape is: (1) After dissolving sodium lauryl sulfate and hexadecane in 1 / 2 part by weight of deionized water, then dissolving butyl acrylate, hydroxyethyl acrylate, Vinyl acetate was added and mixed and stirred for 20 minutes to obtain a uniformly mixed...

Example Embodiment

[0019] Example 2

[0020] A quick-drying adhesive for BOPP tape, prepared by weight parts of the following ingredients: 110 parts of butyl acrylate, 5 parts of hydroxyethyl acrylate, 15 parts of vinyl acetate, 90 parts of deionized water, 1.5 parts of sodium lauryl sulfate Parts, alkylphenol polyoxyethylene ether 0.7 parts, hexadecane 0.06 parts, ammonium persulfate 1 part, ammonia water 0.5 parts, tert-butyl hydroperoxide 0.3 parts, sodium formaldehyde sulfoxylate 0.3 parts, p-tert-butyl phenolic aldehyde 5 parts of resin, 8 parts of allyl modified alkyl phenolic resin, 2 parts of barium sulfate, 8 parts of tung oil.

[0021] The preparation method of the above-mentioned quick-drying adhesive for BOPP tape is: (1) After dissolving sodium lauryl sulfate and hexadecane in 1 / 2 part by weight of deionized water, then dissolving butyl acrylate, hydroxyethyl acrylate, Vinyl acetate was added and mixed and stirred for 40 minutes to obtain a uniformly mixed pre-emulsion; (2) Dissolve the...

Example Embodiment

[0022] Example 3

[0023] A quick-drying adhesive for BOPP tape, prepared by weight of the following ingredients: 80 parts of butyl acrylate, 12 parts of hydroxyethyl acrylate, 11 parts of vinyl acetate, 75 parts of deionized water, and 1.2 parts of sodium lauryl sulfate Parts, alkylphenol polyoxyethylene ether 1 part, hexadecane 0.03 part, ammonium persulfate 0.5 part, ammonia water 0.2 part, tert-butyl hydroperoxide 0.1 part, sodium formaldehyde sulfoxylate 0.1 part, p-tert-butyl phenolic aldehyde 6 parts of resin, 3 parts of allyl modified alkyl phenolic resin, 5 parts of barium sulfate, 4 parts of tung oil.

[0024] The preparation method of the above-mentioned quick-drying adhesive for BOPP tape is: (1) After dissolving sodium lauryl sulfate and hexadecane in 1 / 2 part by weight of deionized water, then dissolving butyl acrylate, hydroxyethyl acrylate, Vinyl acetate was added and mixed and stirred for 25 minutes to obtain a uniformly mixed pre-emulsion; (2) Dissolve the alkylp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a quick-drying adhesive for a BOPP adhesive tape and a preparation method thereof. The preparation method includes: (1) dissolving sodium dodecyl sulfate and hexadecane with 1/2weight part of deionized water, then adding butyl acrylate, hydroxyethyl acrylate and vinyl acetate, and performing mixing and stirring to obtain a pre-emulsion; (2) dissolving alkylphenol polyoxyethylene and ammonium persulfate with residual water, placing the mixture in a reaction kettle and performing heating, then adding 1/2 weight part of the pre-emulsion dropwise into the reaction kettle for reaction; (3) adding p-tert-butyl phenolic resin, allyl modified alkyl phenolic resin, barium sulfate and tung oil into the remaining pre-emulsion, mixing the substances evenly, and then adding themixture dropwise into the reaction kettle; and (4) at the end of adding in a dropwise manner, performing natural cooling, adding tert-butyl hydroperoxide, then adding sodium formaldehyde sulfoxylate,and finally using ammonia water to adjust the pH to 6-7, thus obtaining the quick-drying adhesive for BOPP. The quick-drying adhesive for a BOPP adhesive tape provided by the invention has the characteristics of good film-forming properties and fast drying speed.

Description

technical field [0001] The invention relates to the field of quick-drying adhesives, in particular to an instant-drying adhesive for BOPP adhesive tape and a preparation method thereof. Background technique [0002] Sealing tape is also called BOPP tape, packaging tape, etc. It is based on BOPP biaxially oriented polypropylene film, and is evenly coated with pressure-sensitive adhesive emulsion after heating to form a glue layer ranging from 8 μm to 28 μm. It is an indispensable product in the life of light industry enterprises, companies and individuals. Pressure-sensitive adhesive is a special type of adhesive, once it is pasted or applied to the surface to be bonded, without solvent or heat, the adherend can be removed by pressing gently with fingers or other tools. Glue it up. In the past, pressure-sensitive adhesives were mainly solvent-based. In recent years, emulsion-type pressure-sensitive adhesives have developed rapidly, accounting for more than 60% of the total,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C09J161/06C09J161/14C09J11/08C09J11/04C09J7/30C08F220/18C08F220/28C08F218/08C08F2/26C08F2/30
Inventor 潘明华
Owner 潘明华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap