Method for manufacturing high-silicon composite electrical steel narrow-band product
A manufacturing method and technology of electrical steel, applied to other manufacturing equipment/tools, turbines, engine components, etc., can solve problems such as low operating efficiency, high cost, and complicated production process operations, so as to achieve easy control of the process, increase product output, The effect of high production efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] [Example 1]
[0025] The chemical composition of electrical steel strip as the base material: C: 0.003%, Si: 2.5%, Al: 0.25%, Mn: 0.31%, P: 0.012%, S: 0.0025%, N: 0.0025%, the rest is Fe and Inevitable residual elements;
[0026] Substrate thickness: 1.00mm;
[0027] The high-silicon ferro-silicon powder has a particle size of 120 mesh and a silicon content of 6%.
[0028] Using core-spun wire preparation technology and equipment, the base material is wrapped with high-silicon iron powder to prepare high-silicon composite core-spun wire with a wire diameter of 10mm, and then the cold rolling mill rolls to prepare high-silicon composite core-spun flat belt, and the pressing force is controlled to 10T ,.
[0029] The high-silicon composite cored flat belt is heated and sintered in the furnace at a temperature of 1230°C, a protective atmosphere is 100% dry hydrogen, and the holding time is 1.5h.
[0030] The sintered high-silicon composite flat strip is rolled by a four-roll 200-ro...
Example Embodiment
[0032] [Example 2]
[0033] The chemical composition of electrical steel strip as the base material: C: 0.002%, Si: 3.2%, Al: 0.62%, Mn: 0.30%, P: 0.011%, S: 0.002%, N: 0.0021%, the rest is Fe and Inevitable residual elements;
[0034] Substrate thickness: 0.50mm;
[0035] The high silicon iron powder has a particle size of 130 mesh, a silicon content of 6.5%, an aluminum content of 1%, and a calcium content of 0.0054%.
[0036] Using core-spun wire preparation technology and equipment, the base material is wrapped with high-silicon iron powder to prepare high-silicon composite core-spun wire with a wire diameter of 15mm, and then the high-silicon composite core-spun flat belt is prepared by cold rolling mill. Control 15T.
[0037] The high-silicon composite cored ribbon is heated and sintered in a furnace at a temperature of 1310°C, a protective atmosphere of 100% dry hydrogen, and a holding time of 2.0h.
[0038] After sintering, the composite steel plate is rolled on a four-roll 200...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Wire diameter | aaaaa | aaaaa |
Iron loss | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap