Agricultural film material and preparation technology thereof

A technology for agricultural films and film materials, applied in the field of film material preparation, can solve problems such as increased residual film and its fragments, ecological environment hazards, crop yield reduction, etc., to improve degradability, improve tensile performance, reduce residual film and Fragmentation effect

Inactive Publication Date: 2018-02-16
MAANSHAN SONGHAK INFORMATION TECH CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the increase in the use of agricultural film and its refractory property will increase the residual film and its fragments in the soil, causing soil compaction and poor permeability, resulting in a reduction in crop production, and its difficulty in recycling leads to it being discarded in nature. environmental hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The film material components include 20 parts by weight of high-density polyethylene, 10 parts of cellulose, 8 parts of toughening agent, 4 parts of ethylene-vinyl acetate copolymer, 5 parts of acetyl citrate, and 3 parts of epoxy soybean oil , 4 parts of epoxy dioctyl tetrahydrophthalate, 6 parts of corn starch, and 1 part of graphene oxide.

[0015] The preparation process of the present embodiment comprises the following steps:

[0016] A. Mix ethylene-vinyl acetate copolymer, acetyl citrate, epoxy soybean oil, epoxy tetrahydrophthalate dioctyl, and corn starch and add them to the mixer for mixing. The mixing temperature is 130 °C, the time is 15min, to obtain the mixture A;

[0017] B. After mixing high-density polyethylene, cellulose, and toughening agent, add them to the stirring tank and stir at a speed of 300 rpm for 20 minutes to obtain mixture B;

[0018] C. Add mixture B to mixture A, and then add graphene oxide. After fully mixing, add it to a twin-screw e...

Embodiment 2

[0020] The film material components include 40 parts by weight of high-density polyethylene, 20 parts of cellulose, 20 parts of toughening agent, 12 parts of ethylene-vinyl acetate copolymer, 15 parts of acetyl citrate, and 9 parts of epoxy soybean oil , 12 parts of epoxy dioctyl tetrahydrophthalate, 20 parts of corn starch, and 4 parts of graphene oxide.

[0021] The preparation process of the present embodiment comprises the following steps:

[0022] A. Mix ethylene-vinyl acetate copolymer, acetyl citrate, epoxy soybean oil, epoxy tetrahydrophthalate dioctyl, and corn starch and add them to the mixer for mixing. The mixing temperature is 130 °C, the time is 15min, to obtain the mixture A;

[0023] B. After mixing high-density polyethylene, cellulose, and toughening agent, add them to the stirring tank and stir at a speed of 300 rpm for 20 minutes to obtain mixture B;

[0024] C. Add mixture B to mixture A, and then add graphene oxide. After fully mixing, add it to a twin-s...

Embodiment 3

[0026] The film material components include 25 parts by weight of high-density polyethylene, 16 parts of cellulose, 10 parts of toughening agent, 7 parts of ethylene-vinyl acetate copolymer, 9 parts of acetyl citrate, and 4 parts of epoxy soybean oil , 6 parts of epoxy dioctyl tetrahydrophthalate, 12 parts of corn starch, and 2 parts of graphene oxide.

[0027] The preparation process of the present embodiment comprises the following steps:

[0028] A. Mix ethylene-vinyl acetate copolymer, acetyl citrate, epoxy soybean oil, epoxy tetrahydrophthalate dioctyl, and corn starch and add them to the mixer for mixing. The mixing temperature is 130 °C, the time is 15min, to obtain the mixture A;

[0029] B. After mixing high-density polyethylene, cellulose, and toughening agent, add them to the stirring tank and stir at a speed of 300 rpm for 20 minutes to obtain mixture B;

[0030] C. Add mixture B to mixture A, and then add graphene oxide. After fully mixing, add it to a twin-scre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile propertiesaaaaaaaaaa
Login to View More

Abstract

The invention discloses an agricultural film material and a preparation technology thereof. The agricultural film material comprises the following components in parts by weight: 20-40 parts of high density polyethylene, 10-20 parts of cellulose, 8-20 parts of flexibilizer, 4-12 parts of ethylene-vinyl acetate copolymer, 5-15 parts of acetyl citrate, 3-9 parts of epoxidized soybean oil, 4-12 partsof di(2-ethylhexyl)-4,5-epoxytetrahydrophthalate, 6-20 parts of corn starch and 1-4 parts of graphene oxide. According to the invention, the preparation technology is simple, the prepared film material is capable of promoting the degrading property of the film and the residual film and fragments in the soil are reduced.

Description

technical field [0001] The invention relates to the technical field of film material preparation, in particular to an agricultural film material and a preparation process thereof. Background technique [0002] The main component of agricultural mulch film is polyethylene or polypropylene, which is currently the most produced plastic product in the world. The use of agricultural film is beneficial to the growth and development of crops and increases crop yield. However, the increase in the use of agricultural film and its refractory property will increase the residual film and its fragments in the soil, causing soil compaction and poor permeability, resulting in a reduction in crop production, and its difficulty in recycling leads to it being discarded in nature. The environmental hazards are great. Contents of the invention [0003] The object of the present invention is to provide an agricultural film material and its preparation process, so as to solve the problems rai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L1/02C08L23/08C08L3/02C08K3/04C08K5/11
CPCC08J5/18C08J2323/06C08J2401/02C08J2403/02C08L23/06C08L2203/16C08L2205/035C08L2207/062C08L1/02C08L23/0853C08L3/02C08K3/04C08K5/11
Inventor 施享
Owner MAANSHAN SONGHAK INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com