Low carbon aluminum containing cold heading steel continuous casting billet net-shaped crack control method

A network crack and control method technology, which is applied in the field of continuous casting, can solve problems such as network cracks, and achieve the effects of reducing the depth, reducing the static pressure of molten steel, and reducing the sensitivity of cracks

Active Publication Date: 2018-03-13
ANGANG STEEL CO LTD
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to control the [Mn] / [S] ratio in the steel, the moisture content in the mold flux, the total amount of [N]+[O]+[H] in molten steel and reduce the specific water in the secondary cooling zone, thereby Solving the problem of reticular cracks in low-carbon aluminum-containing cold heading steel continuous casting billets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: The steel type is SWRCH22A.

[0016] 1. The smelting process is: hot metal desulfurization pretreatment - converter smelting - LF furnace refining - continuous casting. The converter smelting process uses ladles and alloys for baking to ensure that raw and auxiliary materials such as lime do not absorb moisture.

[0017] 2. LF refining process: foam slag is built during the refining process to realize submerged arc heating to prevent the molten steel surface from being exposed in the arc area; the seal between the ladle and the fume hood is strengthened to ensure the reducing atmosphere in the furnace; micro positive pressure operation is adopted, Reduce the contact between molten steel and air; control the intensity of argon blowing, control the intensity of argon blowing at 0.28 ~ 0.41Mpa, reduce the exposure of molten steel, the exposed area of ​​molten steel is less than 2%, control the nitrogen increase, and increase nitrogen by 0.0040% during the LF ...

Embodiment 2

[0022] Example 2: SWRCH18AB.

[0023] 1. The smelting process is: hot metal desulfurization pretreatment - converter smelting - LF furnace refining - continuous casting. The converter smelting process uses ladles and alloys for baking to ensure that raw and auxiliary materials such as lime do not absorb moisture.

[0024] 2. LF refining process: foam slag is built during the refining process to realize submerged arc heating to prevent the molten steel surface from being exposed in the arc area; the seal between the ladle and the fume hood is strengthened to ensure the reducing atmosphere in the furnace; micro positive pressure operation is adopted, Reduce the contact between molten steel and air; control the intensity of argon blowing, reduce the exposure of molten steel, control the nitrogen increase, 0.0035% nitrogen increase in the LF refining process; desulfurization treatment, control the mass fraction after refining: N 0.0040%, S 0.0065%, Mn 0.61%.

[0025] 3. Continuo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a low carbon aluminum containing cold heading steel continuous casting billet net-shaped crack control method. According to a smelting process, molten iron desulphurization pretreatment, converter smelting, LF furnace refining and continuous casting are sequentially carried out, and steel ladle and alloy baking is carried out; in the LF refining process, foaming slag is prepared, submerged arc heating is carried out, micro-positive pressure operation is carried out, the increase nitrogen is smaller than 0.0005%, and the [Mn] / [S] ratio is controlled to range from 80 to 100; continuous casting protective slag and a tundish covering agent H2O are smaller than or equal to 0.4%, tundish cover argon blowing is carried out before pouring starting, argon blowing protection is carried out on sliding plates of a long nozzle and a submersed nozzle in the pouring process, the argon flow is 4 L / min to 6 L / min, and the T[O] is controlled to be smaller than 0.0015%; [N] in tundish molten steel is smaller than 60 ppm, the precipitation amount and the precipitation size of AlN in a casting billet are reduced, and [H] is smaller than 0.0004%; and straightening is carried out with the casting blank surface temperature higher than the steel ball brittleness zone temperature, the specific water flow is controlled to range from 0.8 L / kg to 0.9 L / kg. By means of the low carbonaluminum containing cold heading steel continuous casting billet net-shaped crack control method, the surface quality of the low carbon aluminum containing cold heading steel continuous casting billetcan be improved, the occurrence rate of a net-shaped crack is effectively controlled, the depth of the net-shaped crack is reduced, and the polishing cost of the casting billet is reduced.

Description

technical field [0001] The invention belongs to the technical field of continuous casting, and in particular relates to a method for controlling reticular cracks of a continuous casting billet of low-carbon aluminum-containing cold heading steel. Background technique [0002] Low-carbon aluminum-containing cold heading steel is mainly used to manufacture bolts, screws, rivets and pins. It not only has excellent cold drawing performance, but also has good cold forging and cold extrusion performance. At present, most domestic enterprises refer to the Japanese Industrial Standards. For example, the grades are SWRCH18A and SWRCH22A, and the aluminum content is generally required to be 0.03-0.06%. The typical production process of low-carbon aluminum-containing cold heading steel is: molten iron—converter—refining—continuous casting—slab inspection—slab opening, continuous rolling—slab grinding—high-end hot-rolled wire rod—finished product inspection—into library. The productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22D11/111C21C7/064C21C7/072B22D11/18
CPCB22D11/111B22D11/18C21C7/064C21C7/072
Inventor 常桂华黄玉平吴世龙唐雪峰孙振宇李广帮杨辉张维维尚德礼
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products