Polyethylene film with tensile strength, and preparation method thereof

A polyethylene film and anti-stretching technology, which is applied in the field of polyethylene materials, can solve the problems such as the resilience and tensile strength need to be improved, and the moisture permeability is small, and achieve the effects of high production efficiency, convenient operation and easy industrialization.

Inactive Publication Date: 2018-04-13
ANHUI YOURFRIEND PULP MOLDING TECH
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyethylene film has the characteristics of moisture resistance and low moisture permeability, but the existing polyethylene film for packaging needs to be improved in resilience and tensile strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A stretch-resistant polyethylene film, prepared from the following raw materials in parts by weight: 20 parts of low-density polyethylene, 60 parts of linear low-density polyethylene, 10 parts of metallocene polyethylene, and 10 parts of polyethylene terephthalate , 5 parts of trimethylolpropane trimethacrylate, 8 parts of zinc stearate, 15 parts of oxidized polyethylene wax, 14 parts of ammonium polyphosphate, 4 parts of nano silicon dioxide, 3 parts of silane coupling agent, glass 4 parts of fiber, 1687 parts of antioxidant and 3280.2 parts of ultraviolet absorber. The silane coupling agent is γ-aminopropyltriethoxysilane.

[0021] The preparation method of the stretch-resistant polyethylene film described in the present embodiment comprises the following steps:

[0022] (1) glass fibers are chopped to obtain glass fibers with a length below 0.5 mm;

[0023] (2) Weigh low-density polyethylene, linear low-density polyethylene, metallocene polyethylene and polyethylene...

Embodiment 2

[0027] A stretch-resistant polyethylene film, prepared from the following raw materials in parts by weight: 15 parts of low-density polyethylene, 70 parts of linear low-density polyethylene, 5 parts of metallocene polyethylene, and 15 parts of polyethylene terephthalate Parts, 7 parts of trimethylolpropane trimethacrylate, 5 parts of zinc stearate, 18 parts of oxidized polyethylene wax, 12 parts of ammonium polyphosphate, 6 parts of nano silicon dioxide, 4 parts of silane coupling agent, glass 3 parts of fiber, 16810 parts of antioxidant and 3280.2 parts of ultraviolet absorber. The silane coupling agent is γ-(2,3-glycidoxy)propyltrimethoxysilane.

[0028] The preparation method of the stretch-resistant polyethylene film described in the present embodiment comprises the following steps:

[0029] (1) glass fibers are chopped to obtain glass fibers with a length below 0.5mm;

[0030] (2) Weigh low-density polyethylene, linear low-density polyethylene, metallocene polyethylene a...

Embodiment 3

[0034] A stretch-resistant polyethylene film, prepared from the following raw materials in parts by weight: 25 parts of low-density polyethylene, 50 parts of linear low-density polyethylene, 15 parts of metallocene polyethylene, and 10 parts of polyethylene terephthalate , 3 parts of trimethylolpropane trimethacrylate, 12 parts of zinc stearate, 14 parts of oxidized polyethylene wax, 16 parts of ammonium polyphosphate, 3 parts of nano silicon dioxide, 1 part of silane coupling agent, glass 8 parts of fiber, 1686 parts of antioxidant and 3280.4 parts of ultraviolet absorber. The silane coupling agent is γ-aminopropyltriethoxysilane.

[0035] The preparation method of the stretch-resistant polyethylene film described in the present embodiment comprises the following steps:

[0036] (1) glass fibers are chopped to obtain glass fibers with a length below 0.5 mm;

[0037] (2) Weigh low-density polyethylene, linear low-density polyethylene, metallocene polyethylene and polyethylene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
resilienceaaaaaaaaaa
Login to view more

Abstract

The invention provides a polyethylene film with tensile strength. The polyethylene film is prepared from the following raw materials by weight: 15-25 parts of low-density polyethylene, 50-70 parts oflinear low-density polyethylene, 5-15 parts of metallocene polyethylene, 10-15 parts of polyethylene terephthalate, 3-7 parts of trimethylolpropane trimethacrylate, 5-12 parts of zinc stearate, 14-18parts of oxidized polyethylene wax, 12-16 parts of ammonium polyphosphate, 3-6 parts of nanometer silica, 1-4 parts of a silane coupling agent, 3-8 parts of glass fibers, 6-10 parts of an antioxidant168 and 0.2-0.4 part of an ultraviolet absorber 328. The polyethylene film with tensile strength has excellent strength, toughness and tensile resistance. The invention also provides a preparation method for the polyethylene film with tensile strength.

Description

technical field [0001] The invention belongs to the technical field of polyethylene materials, in particular to a stretch-resistant polyethylene film and a preparation method thereof. Background technique [0002] Plastic films, used for packaging and as laminations. Plastic packaging and plastic packaging products are taking an increasing share in the market, especially composite plastic flexible packaging, which has been widely used in food, medicine, chemical and other fields. [0003] Polyethylene film is a colorless, tasteless, odorless, translucent, non-toxic insulating material. It is widely used in packaging bags, food bags, and various containers. Polyethylene film has the characteristics of moisture resistance and low moisture permeability, but the existing polyethylene film for packaging needs to be improved in resilience and tensile strength. [0004] Metallocene polyethylene is a new type of thermoplastic. Metallocene polyolefin has better performance than the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/06C08L67/02C08L23/30C08K13/04C08K7/14C08K5/098C08K3/36C08K3/32C08J5/18
CPCC08J5/18C08J2323/08C08J2423/06C08J2467/02C08K3/36C08K5/098C08K7/14C08K2003/323
Inventor 汪锋王龙珑
Owner ANHUI YOURFRIEND PULP MOLDING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap