Preparation method for polyoxymethylene dimethyl ether
A technology of polyoxymethylene dimethyl ether and paraformaldehyde, applied in the preparation of organic compounds, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problem of low product selectivity, and achieve good yield and good technology effect of effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] 1. Preparation of catalyst
[0032] Sodium sulfonate type polystyrene cation exchange resin 7320 is washed with deionized water until clear water flows out, then soaked four times with 4w% hydrochloric acid, each use is equivalent to 10 times the dry weight of sodium sulfonate type polystyrene cation exchange resin 7320 4w% hydrochloric acid, soaked for 4 hours each time, then washed with deionized water until the eluate was free of chloride ions, and dried at 60°C to obtain a sulfonic acid polystyrene cation exchange resin with a total exchange capacity of 4.10 mmol / g. Get the sulfonic acid type polystyrene cation exchange resin that is equivalent to dry base resin 98 grams and 300ml contain Cu and be 2 grams of Cu(OH) 2 The aqueous suspensions were mixed, 1 drop of glacial acetic acid was added, mixed, left standing at room temperature for 24 hours, and dried in a vacuum drying oven to a constant weight to obtain a catalyst with a Cu content of 2w%.
[0033] 2. Synt...
Embodiment 2
[0036] 1. Preparation of catalyst
[0037] Sodium sulfonate type polystyrene cation exchange resin 7320 is washed with deionized water until clear water flows out, then soaked four times with 4w% hydrochloric acid, each use is equivalent to 10 times the dry weight of sodium sulfonate type polystyrene cation exchange resin 7320 4w% hydrochloric acid, soaked for 4 hours each time, then washed with deionized water until the eluate was free of chloride ions, and dried at 60°C to obtain a sulfonic acid polystyrene cation exchange resin with a total exchange capacity of 4.10 mmol / g. Get the sulfonic acid type polystyrene cation exchange resin equivalent to 98 grams of dry base resin, under nitrogen protection, be 2 grams of Ni(OH) with 300ml containing Ni 2 Mix the aqueous suspensions, add 1 drop of glacial acetic acid, mix, let stand at room temperature for 24 hours, and dry to constant weight in a vacuum oven to prepare a catalyst with a Ni content of 2w%.
[0038] 2. Synthesis ...
Embodiment 3
[0041] 1. Preparation of catalyst
[0042] Sodium sulfonate type polystyrene cation exchange resin 7320 is washed with deionized water until clear water flows out, then soaked four times with 4w% hydrochloric acid, each use is equivalent to 10 times the dry weight of sodium sulfonate type polystyrene cation exchange resin 7320 4w% hydrochloric acid, soaked for 4 hours each time, then washed with deionized water until the eluate was free of chloride ions, and dried at 60°C to obtain a sulfonic acid polystyrene cation exchange resin with a total exchange capacity of 4.10 mmol / g. Get the sulfonic acid type polystyrene cation exchange resin equivalent to 98 grams of dry base resin, under nitrogen protection, with 300ml of Co(OH) containing 2 grams of Co 2 Mix the aqueous suspensions, add 1 drop of glacial acetic acid, mix, let stand at room temperature for 24 hours, and dry to constant weight in a vacuum oven to prepare a catalyst with a Co content of 2w%.
[0043] 2. Synthesis ...