A production process and decorative panel technology, applied in the field of plastic processing, can solve problems such as cold material spots, silver streaks, air marks, unstable injection molding process, and unstable product quality, so as to reduce the defective rate and mix raw materials evenly and thoroughly , long service life effect
Inactive Publication Date: 2018-05-01
SUZHOU NIUDONG PRECISION MFG TECH CO LTD
View PDF3 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Among them, the plastic decorative board is the most widely used. When the usual plastic decorative board is processed, some are formed by extrusion, and some are formed by injection molding. Usually, it is easy to appear at the nozzle (glue point) during injection molding. Cold material Spots, silver streaks, air marks, and other appearance defects. The injection molding process cannot be stabilized, the product quality is unstable and the production efficiency is low, and the cost is high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] The production technology of the plastic decorative board of the present embodiment comprises the following steps:
[0020] (1) Ingredients: The mass percentage of each component in the plastic decorative board is: 4.43% epoxy resin, 1.13% styrene, 0.03% magnesium stearate, 0.18% hydroxyl silicone oil, 0.55% polyvinyl chloride resin, 0.45% plasticizer, 0.75% anti-ultraviolet agent, 1.55% hexabromocyclododecane powder, 0.56% titanium dioxide, 0.01% antimony trioxide, 0.36% silazane, 1.51% bone char, and the balance is phenolic resin;
[0021] (2) After mixing the raw materials according to the mass percentage, cleaning and crushing are carried out;
[0022] (3) Carry out drying treatment to raw material, drying temperature is 90 ℃, and drying time is 5 hours;
[0023] (iv) Put the dried raw materials into the injection molding machine, adjust the injection molding machine, use 50-70Mpa pressure, 20m / s medium-low speed injection, injection time is 0.45 seconds, fill the ...
Embodiment 2
[0028] The production technology of the plastic decorative board of the present embodiment comprises the following steps:
[0029] (1) Ingredients: The mass percentage of each component in the plastic decorative board is: 4.87% epoxy resin, 1.23% styrene, 0.14% magnesium stearate, 0.21% hydroxyl silicone oil, 0.62% polyvinyl chloride resin, 0.66% plasticizer, 0.87% anti-ultraviolet agent, 1.76% hexabromocyclododecane powder, 0.77% titanium dioxide, 0.07% antimony trioxide, 0.45% silazane, 2.65% bone char, and the balance is phenolic resin;
[0030] (2) After mixing the raw materials according to the mass percentage, cleaning and crushing are carried out;
[0031] (3) Carry out drying treatment to raw material, drying temperature is 100 ℃, and drying time is 6 hours;
[0032] (iv) Put the dried raw materials into the injection molding machine, adjust the injection molding machine, use 50-70Mpa pressure, 30m / s medium-low speed injection, injection time is 0.7 seconds, fill the ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a production process of a plastic decorative board and belongs to the technical field of plastic processing. The production process of the plastic decorative board comprises the following steps: (1) batching; (2) mixing the raw materials according to the mass percentage, and cleaning and crushing; (3) drying the raw materials at a drying temperature of 80 to 100 DEG C witha drying time of 4 to 6 hours; (4) adding the dried raw materials into an injection molding machine to complete injection molding of a product; (5) cooling: using cooling water to cool a mold, wherein the temperature of the cooling water is 5 to 6 DEG C and flow rate is 0.4 to 0. 5m / s, cooling the mold to room temperature; (6) demolding: detaching an injection-molded plastic decorative plate fromthe mold through the cooled mold; (7) spraying a water-based coating on the surface of the plastic decorative plate. The plastic decorative board has excellent high pressure resistance due to a scientific composition proportion, and is excellent in corrosion resistance and heat resistance, and has a long service life.
Description
technical field [0001] The invention relates to a production process of a plastic decorative board, which belongs to the technical field of plastic processing. Background technique [0002] There are many kinds of decorative materials, including stainless steel decorative materials, plastic decorative materials, and composite board decorative panels, each of which has its own characteristics. Among them, the plastic decorative board is the most widely used. When the usual plastic decorative board is processed, some are formed by extrusion, and some are formed by injection molding. Usually, it is easy to appear at the nozzle (glue point) during injection molding. Cold material Spots, silver streaks, air marks, and other appearance defects. The injection molding process cannot be stabilized, the product quality is unstable, the production efficiency is low, and the cost is high. Contents of the invention [0003] The technical problem to be solved by the present invention i...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more