A nano-structure and organic technology, applied in the field of organic polymer and nano-material science, can solve the problems that there are no relevant reports on the stabilization of organic nano-structures, and achieve long-term non-destructive preservation, simple operation process and wide application range

Active Publication Date: 2020-07-28
PEKING UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned results show that the nanostructure control methods based on block copolymer materials emerge in an endless stream, but so far, except for the chemical cross-linking method (Yu Haifeng, Wang Tianjie, Wang Wenzhong. Preparation of stable nanopatterns based on cross-linkable polymer materials and Control method, application number: 201610076750.6) can stabilize organic nanostructures, and there is no relevant report on the theory and method of stabilizing organic nanostructures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of stabilization method of organic nanostructure
  • A kind of stabilization method of organic nanostructure
  • A kind of stabilization method of organic nanostructure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]

[0030] 1. Preparation of phase separation structure:

[0031] Dissolve the block copolymer A-b-C represented by formula I a) in a good organic solvent such as toluene or tetrahydrofuran to obtain a clear homogeneous solution. After the copolymer is fully dissolved, filter the solution, and use spin coating, rod coating or dipping The filtrate is evenly coated on the clean substrate by pulling and other methods to form a copolymer film. After the thin film is annealed at different temperatures, regular and ordered nano phase separation structures with different morphologies can be obtained. The nanopillars formed by the dispersed phase generally have a diameter of 5-50nm, a length of 20nm-20μm, and a period of 10-100nm, or form an in-plane arrangement parallel to the substrate, which is displayed as a striped morphology in the AFM phase diagram; Or form an out-of-plane arrangement perpendicular to the substrate, which is displayed as a dot-like morphology in the AF...

Embodiment 2

[0041]

[0042] 1, the preparation of phase separation structure: adopt the block copolymer PEO-b-PM in formula II a) 11 AzPy prepares the copolymer film, and the preparation method is the same as that of Example 1.

[0043] 2. Stabilization of nanopatterns by surface coating: except that polyvinylpyrrolidone (PVP) in formula II b) is used instead of the water-soluble polymer used for the surface coating, the others are the same as in Example 1.

[0044] 3. Long-term non-destructive storage of samples: the same as in Example 1.

[0045] 4. Preparation of complex nano-patterns: the same as in Example 1.

Embodiment 3

[0047]

[0048] 1. Preparation of phase-separated structure: the copolymer film was prepared by using the block copolymer PS-b-PNIPAAm in formula III a), and the preparation method was the same as that in Example 1.

[0049] 2. Stabilization of nanopatterns by the surface coating: except that the water-soluble polymer used in the surface coating is replaced by polyethylene oxide (PEO) in formula III b), the others are the same as in Example 1.

[0050] 3. Long-term non-destructive storage of samples: the same as in Example 1.

[0051] 4. Preparation of complex nano-patterns: the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for stabilizing an organic nanometer structure based on a water-soluble polymer coating. The method is characterized in that a film amphiphilic block copolymer is self-assembled to form the organic nanometer structure; under the selective anchoring function of water-soluble macromolecular surface coating, the nanometer patterns of the organic nanometer structure can be thermally stabilized at normal temperature and even high temperature; by adding the surface coating, a fully new path is opened for the long-time nondestructive storage of the nanometer patters and the design and preparation of multiple complicated nanometer patterns. The method has the advantages that the cost of the material is low, the operation process is simple, the stabilizing degree ishigh, the application range is broad, and the like; the application of the organic nanometer structure in the fields of optics, microelectronics, physics, chemicals, materials and the like is greatlybroadened.

Description

technical field [0001] The invention relates to an organic nanostructure regulation technology, in particular to a method for stabilizing an organic nanometer pattern based on a water-soluble polymer coating, and belongs to the field of organic macromolecule and nanomaterial science. Background technique [0002] A block copolymer refers to a polymer formed by covalently bonding two or more polymer blocks at one or more nodes. When there is a large difference in the properties of different blocks, the block copolymer will form a phase separation structure in the block state or film state, and the separation structure between the blocks, the size of the dispersed phase is between 10 ~100nm, so it is called microphase separation structure. The block copolymer in the film state will form spherical phase, columnar phase, lamellar phase, bicontinuous equal microphase separation structure with the change of the volume fraction of each component in the system, and then form rich r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/056C08J7/048C08L33/14C08L33/26C08L33/02
CPCC08J7/0427C08J7/08C08J2333/02C08J2333/14C08J2333/26C08J2425/18C08J2433/02C08J2439/06C08J2471/02
Inventor 于海峰陈雨萱王添洁
Owner PEKING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap